• W2900182016 abstract "C/C-ZrC-SiC composites were produced by the joint processes of chemical liquid-vapor deposition (CLVD) and precursor infiltration and pyrolysis (PIP), and the effects of deposition period in CLVD process on the preparation, microstructure and anti-ablation property were studied. The results displayed the non-woven layers of the composites was preferred to be densified in CLVD method, but the subsequent PIP process could fill the pores of the fiber webs. Thus the joint technologies reduced the porosity of the composites and improved the content of ceramics. Meanwhile, the insufficient deposition in CLVD process led to large amounts of defects, which were not densified fully in the following PIP. However, the excessive deposition of CLVD filled the pores remarkably, so the channels for precursor infiltration in the subsequent PIP were reduced. When the deposition period was 8 h, the sample C8P9 had a low porosity, high ceramics content and uniform distribution, which was responsible for its outstanding ablation resistance. After ablation for 60 s, sample C8P9 was damaged slightly, and its mass and linear ablation rate was 1.22 × 10−3 g/s and 1.07 × 10−3 mm/s. The ablation surface was divided into four regions, and the different oxide coatings were generated on these regions. These coatings could provide effective protection for the composites, which made a significant contribution to improve the ablation resistance." @default.
• W2900182016 created "2018-11-16" @default.
• W2900182016 creator A5040051893 @default.
• W2900182016 creator A5040796228 @default.
• W2900182016 creator A5041444542 @default.
• W2900182016 creator A5050965845 @default.
• W2900182016 creator A5061764745 @default.
• W2900182016 date "2019-02-01" @default.
• W2900182016 modified "2023-10-10" @default.
• W2900182016 title "Microstructure and ablation property of C/C-ZrC-SiC composites fabricated by chemical liquid-vapor deposition combined with precursor infiltration and pyrolysis" @default.
• W2900182016 cites W1812033235 @default.
• W2900182016 cites W1977931554 @default.
• W2900182016 cites W1984250251 @default.
• W2900182016 cites W2003897172 @default.
• W2900182016 cites W2021785435 @default.
• W2900182016 cites W2024406724 @default.
• W2900182016 cites W2048147170 @default.
• W2900182016 cites W2050280494 @default.
• W2900182016 cites W2052384925 @default.
• W2900182016 cites W2071480986 @default.
• W2900182016 cites W2072916711 @default.
• W2900182016 cites W2078030752 @default.
• W2900182016 cites W2078974572 @default.
• W2900182016 cites W2088169856 @default.
• W2900182016 cites W2089442420 @default.
• W2900182016 cites W2119772919 @default.
• W2900182016 cites W2178099846 @default.
• W2900182016 cites W2191693843 @default.
• W2900182016 cites W2340112330 @default.
• W2900182016 cites W2376936548 @default.
• W2900182016 cites W2378662760 @default.
• W2900182016 cites W2460772316 @default.
• W2900182016 cites W2485679134 @default.
• W2900182016 cites W2515492581 @default.
• W2900182016 cites W2517379236 @default.
• W2900182016 cites W2538584447 @default.
• W2900182016 cites W2547776721 @default.
• W2900182016 cites W2585497660 @default.
• W2900182016 cites W2594721213 @default.
• W2900182016 cites W2605131160 @default.
• W2900182016 cites W2608670715 @default.
• W2900182016 cites W2620019186 @default.
• W2900182016 cites W2737326314 @default.
• W2900182016 cites W2737510781 @default.
• W2900182016 cites W2747485851 @default.
• W2900182016 cites W2791224046 @default.
• W2900182016 cites W2792613428 @default.
• W2900182016 cites W2799860263 @default.
• W2900182016 cites W2803101751 @default.
• W2900182016 cites W2803928789 @default.
• W2900182016 cites W2810541322 @default.
• W2900182016 cites W2883695009 @default.
• W2900182016 cites W2884348159 @default.
• W2900182016 cites W2889651069 @default.
• W2900182016 cites W2892617777 @default.
• W2900182016 cites W580751959 @default.
• W2900182016 doi "https://doi.org/10.1016/j.ceramint.2018.11.045" @default.
• W2900182016 hasPublicationYear "2019" @default.
• W2900182016 type Work @default.
• W2900182016 sameAs 2900182016 @default.
• W2900182016 citedByCount "18" @default.
• W2900182016 countsByYear W29001820162019 @default.
• W2900182016 countsByYear W29001820162020 @default.
• W2900182016 countsByYear W29001820162021 @default.
• W2900182016 countsByYear W29001820162022 @default.
• W2900182016 countsByYear W29001820162023 @default.
• W2900182016 crossrefType "journal-article" @default.
• W2900182016 hasAuthorship W2900182016A5040051893 @default.
• W2900182016 hasAuthorship W2900182016A5040796228 @default.
• W2900182016 hasAuthorship W2900182016A5041444542 @default.
• W2900182016 hasAuthorship W2900182016A5050965845 @default.
• W2900182016 hasAuthorship W2900182016A5061764745 @default.
• W2900182016 hasConcept C120024216 @default.
• W2900182016 hasConcept C127413603 @default.
• W2900182016 hasConcept C134132462 @default.
• W2900182016 hasConcept C146978453 @default.
• W2900182016 hasConcept C151730666 @default.
• W2900182016 hasConcept C153400128 @default.
• W2900182016 hasConcept C159985019 @default.
• W2900182016 hasConcept C171250308 @default.
• W2900182016 hasConcept C191897082 @default.
• W2900182016 hasConcept C192562407 @default.
• W2900182016 hasConcept C2778902805 @default.
• W2900182016 hasConcept C2779851234 @default.
• W2900182016 hasConcept C2816523 @default.
• W2900182016 hasConcept C36759035 @default.
• W2900182016 hasConcept C42360764 @default.
• W2900182016 hasConcept C57410435 @default.
• W2900182016 hasConcept C64297162 @default.
• W2900182016 hasConcept C6648577 @default.
• W2900182016 hasConcept C86803240 @default.
• W2900182016 hasConcept C87976508 @default.
• W2900182016 hasConceptScore W2900182016C120024216 @default.
• W2900182016 hasConceptScore W2900182016C127413603 @default.
• W2900182016 hasConceptScore W2900182016C134132462 @default.
• W2900182016 hasConceptScore W2900182016C146978453 @default.
• W2900182016 hasConceptScore W2900182016C151730666 @default.
• W2900182016 hasConceptScore W2900182016C153400128 @default.

• next