- W2900519128 abstract "In this research, the formation of carbide layer coating on SUJ2 steel by pack Thermal Reactive Deposition method was studied. Mixture of 35/65 weight percent of ferrochromium/ferrovanadium (FeCr/FeV) powder was applied as coating elements. The process was carried out at temperatures of 900, 950, and 1000 °C for 6 hours for each temperature. The effects of temperature on layer thickness, microstructures, homogeneity, hardness, and wear resistance were analyzed. The result showed that the higher the temperature, the thicker the layer formed on substrate surface. The higher percentage of vanadium in the coating layer compared to chromium found by EDS Linescan results indicate that vanadium has higher affinity to carbon than chromium. This result also means the possibility of vanadium carbide formation will be higher than chromium carbides, due to the lower Gibbs energy for vanadium carbide formation. XRD results showed that the layer formed in this process consists of vanadium carbide (V8C7 and V6C5), chromium carbide (Cr23C6 and Cr7C3), and complex carbides. The average micro hardness and wear rate of all coatings with three different temperature variations were 2100 HV, and 3 × 10−4 mm3/m respectively. This hardness was close to FeV hardness as single carbide former at approximately 2400 HV." @default.
- W2900519128 created "2018-11-29" @default.
- W2900519128 creator A5039462882 @default.
- W2900519128 creator A5046326746 @default.
- W2900519128 date "2018-11-19" @default.
- W2900519128 modified "2023-09-26" @default.
- W2900519128 title "Study of temperature effect on carbide layer formation behaviour of dual elements thermal reactive deposition on SUJ2 steel substrate" @default.
- W2900519128 cites W1967197447 @default.
- W2900519128 cites W1992928412 @default.
- W2900519128 cites W2000767300 @default.
- W2900519128 cites W2001348351 @default.
- W2900519128 cites W2022042595 @default.
- W2900519128 cites W2025323678 @default.
- W2900519128 cites W2039841152 @default.
- W2900519128 cites W2046452287 @default.
- W2900519128 cites W2067098578 @default.
- W2900519128 cites W2067451561 @default.
- W2900519128 cites W2069205430 @default.
- W2900519128 cites W2075332192 @default.
- W2900519128 cites W2168030902 @default.
- W2900519128 cites W2218144482 @default.
- W2900519128 cites W2289437795 @default.
- W2900519128 doi "https://doi.org/10.1088/1757-899x/432/1/012019" @default.
- W2900519128 hasPublicationYear "2018" @default.
- W2900519128 type Work @default.
- W2900519128 sameAs 2900519128 @default.
- W2900519128 citedByCount "2" @default.
- W2900519128 countsByYear W29005191282022 @default.
- W2900519128 countsByYear W29005191282023 @default.
- W2900519128 crossrefType "journal-article" @default.
- W2900519128 hasAuthorship W2900519128A5039462882 @default.
- W2900519128 hasAuthorship W2900519128A5046326746 @default.
- W2900519128 hasBestOaLocation W29005191281 @default.
- W2900519128 hasConcept C159985019 @default.
- W2900519128 hasConcept C191897082 @default.
- W2900519128 hasConcept C192562407 @default.
- W2900519128 hasConcept C2776776789 @default.
- W2900519128 hasConcept C2777195266 @default.
- W2900519128 hasConcept C2779227376 @default.
- W2900519128 hasConcept C2781448156 @default.
- W2900519128 hasConcept C504678139 @default.
- W2900519128 hasConcept C511782168 @default.
- W2900519128 hasConcept C5335593 @default.
- W2900519128 hasConcept C87976508 @default.
- W2900519128 hasConceptScore W2900519128C159985019 @default.
- W2900519128 hasConceptScore W2900519128C191897082 @default.
- W2900519128 hasConceptScore W2900519128C192562407 @default.
- W2900519128 hasConceptScore W2900519128C2776776789 @default.
- W2900519128 hasConceptScore W2900519128C2777195266 @default.
- W2900519128 hasConceptScore W2900519128C2779227376 @default.
- W2900519128 hasConceptScore W2900519128C2781448156 @default.
- W2900519128 hasConceptScore W2900519128C504678139 @default.
- W2900519128 hasConceptScore W2900519128C511782168 @default.
- W2900519128 hasConceptScore W2900519128C5335593 @default.
- W2900519128 hasConceptScore W2900519128C87976508 @default.
- W2900519128 hasLocation W29005191281 @default.
- W2900519128 hasOpenAccess W2900519128 @default.
- W2900519128 hasPrimaryLocation W29005191281 @default.
- W2900519128 hasRelatedWork W2004730573 @default.
- W2900519128 hasRelatedWork W2065418788 @default.
- W2900519128 hasRelatedWork W2101662854 @default.
- W2900519128 hasRelatedWork W2317614673 @default.
- W2900519128 hasRelatedWork W2349270042 @default.
- W2900519128 hasRelatedWork W3107442106 @default.
- W2900519128 hasRelatedWork W4292103758 @default.
- W2900519128 hasRelatedWork W2028334806 @default.
- W2900519128 hasRelatedWork W2336478573 @default.
- W2900519128 hasRelatedWork W2517529095 @default.
- W2900519128 hasVolume "432" @default.
- W2900519128 isParatext "false" @default.
- W2900519128 isRetracted "false" @default.
- W2900519128 magId "2900519128" @default.
- W2900519128 workType "article" @default.