- W2901402359 abstract "Cu-Ti alloy, processed by multiaxial forging (MAF) at cryogenic temperature with a cumulative strain up to 1.64, was investigated for microstructure and mechanical properties. The deformed microstructures were analyzed using optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The average grain size of 2 μm was achieved in the deformed sample after 3 cycles of MAF. TEM studies indicated that the shear bands width of the deformed sample after 3 cycles reduced to 1 μm. Tests for mechanical properties indicated an increase in tensile strength and hardness and it was found to be correlated with an increase in dislocation density and grain boundary strengthening mechanism. Ultimate tensile strength (UTS) of 390 MPa, 480 MPa, and 590 MPa was observed in MAF processed samples after 1, 2, and 3 cycles, respectively. Hardness increased from 65 Hv (as-received) to 240 Hv after 3 cycles of MAF. Fractography analysis showed that, with an increase in number of MAF cycles, dimple size reduced up to 1 cycle and percentage elongation increased after 2 cycles of MAF." @default.
- W2901402359 created "2018-11-29" @default.
- W2901402359 creator A5041268403 @default.
- W2901402359 creator A5056406984 @default.
- W2901402359 creator A5064074430 @default.
- W2901402359 creator A5076339263 @default.
- W2901402359 date "2018-11-23" @default.
- W2901402359 modified "2023-09-25" @default.
- W2901402359 title "Effect of multiaxial cryoforging on microstructure and mechanical properties of a Cu-Ti Alloy" @default.
- W2901402359 cites W1674176118 @default.
- W2901402359 cites W169662839 @default.
- W2901402359 cites W1965517063 @default.
- W2901402359 cites W1967604748 @default.
- W2901402359 cites W1976672190 @default.
- W2901402359 cites W1980487591 @default.
- W2901402359 cites W1987491080 @default.
- W2901402359 cites W1987502584 @default.
- W2901402359 cites W1992623678 @default.
- W2901402359 cites W1995747896 @default.
- W2901402359 cites W1999067071 @default.
- W2901402359 cites W2004449160 @default.
- W2901402359 cites W2007336018 @default.
- W2901402359 cites W2009062101 @default.
- W2901402359 cites W2009256118 @default.
- W2901402359 cites W2031511199 @default.
- W2901402359 cites W2035138502 @default.
- W2901402359 cites W2035601211 @default.
- W2901402359 cites W2038210910 @default.
- W2901402359 cites W2044610603 @default.
- W2901402359 cites W2066583286 @default.
- W2901402359 cites W2078756896 @default.
- W2901402359 cites W2088571858 @default.
- W2901402359 cites W2137022507 @default.
- W2901402359 cites W2203078126 @default.
- W2901402359 cites W2331000781 @default.
- W2901402359 cites W2333902069 @default.
- W2901402359 cites W2471612562 @default.
- W2901402359 cites W2493622911 @default.
- W2901402359 cites W2507808715 @default.
- W2901402359 cites W2589377300 @default.
- W2901402359 cites W2591976922 @default.
- W2901402359 cites W2615876922 @default.
- W2901402359 cites W2617412614 @default.
- W2901402359 cites W2623873506 @default.
- W2901402359 cites W2678173742 @default.
- W2901402359 cites W2724106052 @default.
- W2901402359 cites W2767069386 @default.
- W2901402359 doi "https://doi.org/10.1088/2053-1591/aaf085" @default.
- W2901402359 hasPublicationYear "2018" @default.
- W2901402359 type Work @default.
- W2901402359 sameAs 2901402359 @default.
- W2901402359 citedByCount "5" @default.
- W2901402359 countsByYear W29014023592019 @default.
- W2901402359 countsByYear W29014023592020 @default.
- W2901402359 countsByYear W29014023592022 @default.
- W2901402359 crossrefType "journal-article" @default.
- W2901402359 hasAuthorship W2901402359A5041268403 @default.
- W2901402359 hasAuthorship W2901402359A5056406984 @default.
- W2901402359 hasAuthorship W2901402359A5064074430 @default.
- W2901402359 hasAuthorship W2901402359A5076339263 @default.
- W2901402359 hasConcept C191897082 @default.
- W2901402359 hasConcept C192562407 @default.
- W2901402359 hasConcept C2780026712 @default.
- W2901402359 hasConcept C87976508 @default.
- W2901402359 hasConcept C8953137 @default.
- W2901402359 hasConceptScore W2901402359C191897082 @default.
- W2901402359 hasConceptScore W2901402359C192562407 @default.
- W2901402359 hasConceptScore W2901402359C2780026712 @default.
- W2901402359 hasConceptScore W2901402359C87976508 @default.
- W2901402359 hasConceptScore W2901402359C8953137 @default.
- W2901402359 hasIssue "2" @default.
- W2901402359 hasLocation W29014023591 @default.
- W2901402359 hasOpenAccess W2901402359 @default.
- W2901402359 hasPrimaryLocation W29014023591 @default.
- W2901402359 hasRelatedWork W1979687356 @default.
- W2901402359 hasRelatedWork W2010733322 @default.
- W2901402359 hasRelatedWork W2067827792 @default.
- W2901402359 hasRelatedWork W2089251307 @default.
- W2901402359 hasRelatedWork W2123155170 @default.
- W2901402359 hasRelatedWork W2359655419 @default.
- W2901402359 hasRelatedWork W2379855728 @default.
- W2901402359 hasRelatedWork W4205648827 @default.
- W2901402359 hasRelatedWork W4220863741 @default.
- W2901402359 hasRelatedWork W4303926928 @default.
- W2901402359 hasVolume "6" @default.
- W2901402359 isParatext "false" @default.
- W2901402359 isRetracted "false" @default.
- W2901402359 magId "2901402359" @default.
- W2901402359 workType "article" @default.