- W2901955765 abstract "The abrasive wear performance of glass–polyamide fibers/epoxy composites was experimentally studied using a pin-on-disc wear tester at different applied normal loads. Specimens were fabricated in inter-ply configuration using the hand layup technique. Specimens were subjected to distilled water and sea water immersion at room temperature for 200 days. The effects of the reinforcement hybridization, stacking sequence, and relative fiber amounts on the wear behavior of dry and wet specimens were discussed. Temperature rise at the specimen pin–disc interface has been measured. The morphologies of the worn surfaces were investigated with scanning electron microscopy (SEM). Results showed that distilled water and sea water uptake of glass/epoxy composite is 2.5 and 2 times those of polyamide/epoxy counterparts. Correction factor decreases the diffusion coefficient by about 24% and 26% for, respectively, polyamide/epoxy and glass/epoxy composites. Hybridizing glass fiber composite with polyamide fiber could reduce the specimen’s weight loss during wear test for dry and wet specimens. Water uptake induces a significant decrease in wear resistance of the studied composites. Stacking sequence has a slight effect on wear resistance, while relative fiber amounts have a noticeable effect. The maximum temperature at the specimen pin–disc interface (21.5°C) was noticed for glass/epoxy composite under applied load of 10 N. As the applied load and the sliding time increase, the wear resistance of the composites decreases but the temperature at the specimen pin–disc interface increases. SEM observations show debonding, cracks, fiber fracture, and debris formation." @default.
- W2901955765 created "2018-11-29" @default.
- W2901955765 creator A5052227087 @default.
- W2901955765 creator A5067865211 @default.
- W2901955765 creator A5069035862 @default.
- W2901955765 date "2018-11-11" @default.
- W2901955765 modified "2023-09-26" @default.
- W2901955765 title "Wear behavior of glass–polyamide reinforced epoxy hybrid composites" @default.
- W2901955765 cites W1523469794 @default.
- W2901955765 cites W1978502385 @default.
- W2901955765 cites W1979798179 @default.
- W2901955765 cites W1982018794 @default.
- W2901955765 cites W1983025412 @default.
- W2901955765 cites W1984272103 @default.
- W2901955765 cites W1984590699 @default.
- W2901955765 cites W1985576578 @default.
- W2901955765 cites W1994664811 @default.
- W2901955765 cites W2000602464 @default.
- W2901955765 cites W2002336799 @default.
- W2901955765 cites W2002955865 @default.
- W2901955765 cites W2004263827 @default.
- W2901955765 cites W2006131212 @default.
- W2901955765 cites W2012322513 @default.
- W2901955765 cites W2016824348 @default.
- W2901955765 cites W2018941772 @default.
- W2901955765 cites W2018949907 @default.
- W2901955765 cites W2034746362 @default.
- W2901955765 cites W2055356795 @default.
- W2901955765 cites W2058283115 @default.
- W2901955765 cites W2070649166 @default.
- W2901955765 cites W2094581445 @default.
- W2901955765 cites W2099545593 @default.
- W2901955765 cites W2118956339 @default.
- W2901955765 cites W2141391611 @default.
- W2901955765 cites W2149910752 @default.
- W2901955765 cites W2331600506 @default.
- W2901955765 cites W2341810061 @default.
- W2901955765 cites W2371857781 @default.
- W2901955765 cites W2502400023 @default.
- W2901955765 cites W2510612970 @default.
- W2901955765 cites W2555378595 @default.
- W2901955765 cites W2608825857 @default.
- W2901955765 cites W2754381043 @default.
- W2901955765 cites W2757099979 @default.
- W2901955765 cites W2778261911 @default.
- W2901955765 cites W2791906877 @default.
- W2901955765 cites W2793844462 @default.
- W2901955765 cites W2793848561 @default.
- W2901955765 cites W2802266496 @default.
- W2901955765 cites W2804736512 @default.
- W2901955765 cites W2899124703 @default.
- W2901955765 doi "https://doi.org/10.1177/0892705718805127" @default.
- W2901955765 hasPublicationYear "2018" @default.
- W2901955765 type Work @default.
- W2901955765 sameAs 2901955765 @default.
- W2901955765 citedByCount "22" @default.
- W2901955765 countsByYear W29019557652019 @default.
- W2901955765 countsByYear W29019557652020 @default.
- W2901955765 countsByYear W29019557652021 @default.
- W2901955765 countsByYear W29019557652022 @default.
- W2901955765 countsByYear W29019557652023 @default.
- W2901955765 crossrefType "journal-article" @default.
- W2901955765 hasAuthorship W2901955765A5052227087 @default.
- W2901955765 hasAuthorship W2901955765A5067865211 @default.
- W2901955765 hasAuthorship W2901955765A5069035862 @default.
- W2901955765 hasConcept C104779481 @default.
- W2901955765 hasConcept C159985019 @default.
- W2901955765 hasConcept C166595027 @default.
- W2901955765 hasConcept C177229083 @default.
- W2901955765 hasConcept C185592680 @default.
- W2901955765 hasConcept C190399342 @default.
- W2901955765 hasConcept C192562407 @default.
- W2901955765 hasConcept C26771246 @default.
- W2901955765 hasConcept C2779429693 @default.
- W2901955765 hasConcept C2780957350 @default.
- W2901955765 hasConcept C43617362 @default.
- W2901955765 hasConceptScore W2901955765C104779481 @default.
- W2901955765 hasConceptScore W2901955765C159985019 @default.
- W2901955765 hasConceptScore W2901955765C166595027 @default.
- W2901955765 hasConceptScore W2901955765C177229083 @default.
- W2901955765 hasConceptScore W2901955765C185592680 @default.
- W2901955765 hasConceptScore W2901955765C190399342 @default.
- W2901955765 hasConceptScore W2901955765C192562407 @default.
- W2901955765 hasConceptScore W2901955765C26771246 @default.
- W2901955765 hasConceptScore W2901955765C2779429693 @default.
- W2901955765 hasConceptScore W2901955765C2780957350 @default.
- W2901955765 hasConceptScore W2901955765C43617362 @default.
- W2901955765 hasIssue "2" @default.
- W2901955765 hasLocation W29019557651 @default.
- W2901955765 hasOpenAccess W2901955765 @default.
- W2901955765 hasPrimaryLocation W29019557651 @default.
- W2901955765 hasRelatedWork W1964086589 @default.
- W2901955765 hasRelatedWork W2072775309 @default.
- W2901955765 hasRelatedWork W2078664330 @default.
- W2901955765 hasRelatedWork W2185106550 @default.
- W2901955765 hasRelatedWork W2371285531 @default.
- W2901955765 hasRelatedWork W2790593562 @default.
- W2901955765 hasRelatedWork W2883244620 @default.