- W2902237545 abstract "2.5-Dimensional SiO2 fiber-reinforced Al2O3-SiO2 (SiO2f/Al2O3-SiO2) composites were prepared by the sol-gel method, using diphasic SiO2 sol as the precursor into which Al2O3 powders were added. Their antioxidative behaviors and flexural strengths at high temperature were tested and compared. In an oxidation atmosphere, the composites showed high oxidation resistance, with a flexural strength retention ratio of over 90.00% at 1200 °C. After oxidation at 1500 °C, the mass retention ratio and flexural strength were 97.49% and 65.0 MPa respectively. The oxidation resistance of SiO2f/Al2O3-SiO2 composites was higher than that of SiO2f/SiO2 composites. After high-temperature test, the flexural strength retention ratios of SiO2f/SiO2 and SiO2f/Al2O3-SiO2 composites were 86.18% and 94.80% respectively, and the latter had a flexural strength of 134.9 MPa. SiO2 f/Al2O3-SiO2 composites worked better than SiO2f/SiO2 composites did in the flexural strength test at 1200 °C. The mechanical performance degradation and mass variations of the composites during tests were closely associated with their microstructural evolutions." @default.
- W2902237545 created "2018-12-11" @default.
- W2902237545 creator A5024445733 @default.
- W2902237545 creator A5035414792 @default.
- W2902237545 creator A5083340338 @default.
- W2902237545 creator A5085245939 @default.
- W2902237545 creator A5089057417 @default.
- W2902237545 date "2019-04-01" @default.
- W2902237545 modified "2023-09-26" @default.
- W2902237545 title "Degradation behavior of SiO2f/Al2O3-SiO2 composites: Anti-oxidation behavior and high-temperature flexural strength" @default.
- W2902237545 cites W1964010776 @default.
- W2902237545 cites W1964125561 @default.
- W2902237545 cites W1968340359 @default.
- W2902237545 cites W1971763744 @default.
- W2902237545 cites W1991922203 @default.
- W2902237545 cites W1993358418 @default.
- W2902237545 cites W2001221728 @default.
- W2902237545 cites W2015859893 @default.
- W2902237545 cites W2022550507 @default.
- W2902237545 cites W2028313903 @default.
- W2902237545 cites W2031486186 @default.
- W2902237545 cites W2036537829 @default.
- W2902237545 cites W2039492067 @default.
- W2902237545 cites W2043185853 @default.
- W2902237545 cites W2056503020 @default.
- W2902237545 cites W2065302019 @default.
- W2902237545 cites W2066216043 @default.
- W2902237545 cites W2068303323 @default.
- W2902237545 cites W2068841410 @default.
- W2902237545 cites W2072412811 @default.
- W2902237545 cites W2077814007 @default.
- W2902237545 cites W2083211400 @default.
- W2902237545 cites W2093310389 @default.
- W2902237545 cites W2096612041 @default.
- W2902237545 cites W2127950686 @default.
- W2902237545 cites W2132048340 @default.
- W2902237545 cites W2345962196 @default.
- W2902237545 cites W247988002 @default.
- W2902237545 cites W2522398270 @default.
- W2902237545 cites W2528727528 @default.
- W2902237545 cites W2732613182 @default.
- W2902237545 cites W2748318534 @default.
- W2902237545 cites W2771163941 @default.
- W2902237545 cites W34458865 @default.
- W2902237545 cites W2616624756 @default.
- W2902237545 doi "https://doi.org/10.1016/j.ceramint.2018.11.214" @default.
- W2902237545 hasPublicationYear "2019" @default.
- W2902237545 type Work @default.
- W2902237545 sameAs 2902237545 @default.
- W2902237545 citedByCount "2" @default.
- W2902237545 countsByYear W29022375452021 @default.
- W2902237545 countsByYear W29022375452023 @default.
- W2902237545 crossrefType "journal-article" @default.
- W2902237545 hasAuthorship W2902237545A5024445733 @default.
- W2902237545 hasAuthorship W2902237545A5035414792 @default.
- W2902237545 hasAuthorship W2902237545A5083340338 @default.
- W2902237545 hasAuthorship W2902237545A5085245939 @default.
- W2902237545 hasAuthorship W2902237545A5089057417 @default.
- W2902237545 hasConcept C159985019 @default.
- W2902237545 hasConcept C178405089 @default.
- W2902237545 hasConcept C192562407 @default.
- W2902237545 hasConcept C2779679103 @default.
- W2902237545 hasConcept C41008148 @default.
- W2902237545 hasConcept C76155785 @default.
- W2902237545 hasConceptScore W2902237545C159985019 @default.
- W2902237545 hasConceptScore W2902237545C178405089 @default.
- W2902237545 hasConceptScore W2902237545C192562407 @default.
- W2902237545 hasConceptScore W2902237545C2779679103 @default.
- W2902237545 hasConceptScore W2902237545C41008148 @default.
- W2902237545 hasConceptScore W2902237545C76155785 @default.
- W2902237545 hasFunder F4320321001 @default.
- W2902237545 hasIssue "5" @default.
- W2902237545 hasLocation W29022375451 @default.
- W2902237545 hasOpenAccess W2902237545 @default.
- W2902237545 hasPrimaryLocation W29022375451 @default.
- W2902237545 hasRelatedWork W2025687592 @default.
- W2902237545 hasRelatedWork W2082293200 @default.
- W2902237545 hasRelatedWork W2137307547 @default.
- W2902237545 hasRelatedWork W2374325751 @default.
- W2902237545 hasRelatedWork W2380293314 @default.
- W2902237545 hasRelatedWork W2789571739 @default.
- W2902237545 hasRelatedWork W2943188944 @default.
- W2902237545 hasRelatedWork W2944045227 @default.
- W2902237545 hasRelatedWork W3082440218 @default.
- W2902237545 hasRelatedWork W4285802202 @default.
- W2902237545 hasVolume "45" @default.
- W2902237545 isParatext "false" @default.
- W2902237545 isRetracted "false" @default.
- W2902237545 magId "2902237545" @default.
- W2902237545 workType "article" @default.