- W2902535814 abstract "The work described in this thesis explored the manufacturing of fully resorbable high strength glass fibres as the reinforcement of poly-e-caprolactone (PCL) composites and attempted chitosan and 3,4-Dihydroxy-L-phenylalanine (L-DOPA) as coupling agents to improve the interface of PGF/PCL composites. Phosphate based glasses (PBGs) in the system of P2O5-B2O3-Na2O-CaO-MgO-Fe2O3 were studied on their structural, thermal and degradation properties. The results of the experiments conducted revealed that the glass transition temperature, density and chemical durability were increased with increasing iron oxides in PBGs at the expense of CaO/MgO. The analysis of glass stability indicated that higher CaO/MgO ratios would have a positive effect on the fibre drawing from the glasses investigated. Fibres were produced from the glasses investigated using a melt drawn system and the effect of composition on the mechanical and degradation properties of the fibres were evaluated. Addition of Fe2O3 showed a significant improvement on the mechanical properties (tensile strength and modulus) and chemical durability of the fibres. Annealing treatment also enhanced the Young’s modulus and chemical durability of the fibres, while a reduction in tensile strength of the fibres was observed after annealing. Chitosan (CS) dissolved in dilute acetic acid solution was observed to significantly improve the interface of PGF/PCL composites. Coating of CS also showed a significant effect on glass surface protection, resulting in a maintaining of mechanical strength of the fibres in dilute acid solution. TG, SEM, FTIR, Raman and XPS were used to characterize the fibre surface. The results of XPS revealed a threshold value for CS concentration to improve the interface of the composites. L-DOPA dissolved in Tris buffer solution could also improve the interfacial properties of PGF/PCL composites. Meanwhile, a sufficiently high L-DOPA concentration within 0.02-0.04 g/mL could significantly enhance the tensile strength of the fibres. TG, SEM, FTIR and XPS were used to characterize the fibre surface. The results of these analyses suggested the zwitterionic form for L-DOPA powders and the melanin-like polymer layer on the fibres after coating." @default.
- W2902535814 created "2018-12-11" @default.
- W2902535814 creator A5040258033 @default.
- W2902535814 date "2018-07-01" @default.
- W2902535814 modified "2023-09-23" @default.
- W2902535814 title "Preparation and investigation of phosphate glass fibres and organic coupling agents for fully resorbable PGF/PCL composites" @default.
- W2902535814 hasPublicationYear "2018" @default.
- W2902535814 type Work @default.
- W2902535814 sameAs 2902535814 @default.
- W2902535814 citedByCount "0" @default.
- W2902535814 crossrefType "dissertation" @default.
- W2902535814 hasAuthorship W2902535814A5040258033 @default.
- W2902535814 hasConcept C104304963 @default.
- W2902535814 hasConcept C112950240 @default.
- W2902535814 hasConcept C122865956 @default.
- W2902535814 hasConcept C127413603 @default.
- W2902535814 hasConcept C159985019 @default.
- W2902535814 hasConcept C160892712 @default.
- W2902535814 hasConcept C177229083 @default.
- W2902535814 hasConcept C186399102 @default.
- W2902535814 hasConcept C192562407 @default.
- W2902535814 hasConcept C2777855556 @default.
- W2902535814 hasConcept C2781094431 @default.
- W2902535814 hasConcept C42360764 @default.
- W2902535814 hasConcept C49040817 @default.
- W2902535814 hasConcept C521977710 @default.
- W2902535814 hasConcept C57863236 @default.
- W2902535814 hasConcept C59061564 @default.
- W2902535814 hasConcept C7055690 @default.
- W2902535814 hasConceptScore W2902535814C104304963 @default.
- W2902535814 hasConceptScore W2902535814C112950240 @default.
- W2902535814 hasConceptScore W2902535814C122865956 @default.
- W2902535814 hasConceptScore W2902535814C127413603 @default.
- W2902535814 hasConceptScore W2902535814C159985019 @default.
- W2902535814 hasConceptScore W2902535814C160892712 @default.
- W2902535814 hasConceptScore W2902535814C177229083 @default.
- W2902535814 hasConceptScore W2902535814C186399102 @default.
- W2902535814 hasConceptScore W2902535814C192562407 @default.
- W2902535814 hasConceptScore W2902535814C2777855556 @default.
- W2902535814 hasConceptScore W2902535814C2781094431 @default.
- W2902535814 hasConceptScore W2902535814C42360764 @default.
- W2902535814 hasConceptScore W2902535814C49040817 @default.
- W2902535814 hasConceptScore W2902535814C521977710 @default.
- W2902535814 hasConceptScore W2902535814C57863236 @default.
- W2902535814 hasConceptScore W2902535814C59061564 @default.
- W2902535814 hasConceptScore W2902535814C7055690 @default.
- W2902535814 hasLocation W29025358141 @default.
- W2902535814 hasOpenAccess W2902535814 @default.
- W2902535814 hasPrimaryLocation W29025358141 @default.
- W2902535814 hasRelatedWork W1456271339 @default.
- W2902535814 hasRelatedWork W1774970807 @default.
- W2902535814 hasRelatedWork W1979918880 @default.
- W2902535814 hasRelatedWork W1998850867 @default.
- W2902535814 hasRelatedWork W2000964974 @default.
- W2902535814 hasRelatedWork W2006145931 @default.
- W2902535814 hasRelatedWork W2019805404 @default.
- W2902535814 hasRelatedWork W2032977557 @default.
- W2902535814 hasRelatedWork W2049467772 @default.
- W2902535814 hasRelatedWork W2059970115 @default.
- W2902535814 hasRelatedWork W2122903757 @default.
- W2902535814 hasRelatedWork W2161208760 @default.
- W2902535814 hasRelatedWork W2209640004 @default.
- W2902535814 hasRelatedWork W2329330817 @default.
- W2902535814 hasRelatedWork W2359995396 @default.
- W2902535814 hasRelatedWork W2784155248 @default.
- W2902535814 hasRelatedWork W2885363982 @default.
- W2902535814 hasRelatedWork W3112320575 @default.
- W2902535814 hasRelatedWork W3177124271 @default.
- W2902535814 hasRelatedWork W2273744359 @default.
- W2902535814 isParatext "false" @default.
- W2902535814 isRetracted "false" @default.
- W2902535814 magId "2902535814" @default.
- W2902535814 workType "dissertation" @default.