- W2907970912 abstract "Titanium alloys are often used in fatigue-limited structural applications within the aerospace industry. Because of the primary processing control and reactivity of titanium, the fatigue life of the material is predominantly dependent upon the α-phase microstructure, rather than internal defects such as voids or inclusions. For titanium alloy Ti – 6 wt % aluminum - 4 wt % vanadium (Ti-6Al-4V), the influence of cooling rate from above the s-transus is known to affect the resulting microstructure and influence high cycle fatigue life. The transfer time from the furnace to the water-quenching bath significantly influences the cooling rate, and thus controls the microstructural development and fatigue properties. A hydraulic actuator produced from a Ti-6Al-4V forging failed prematurely during fatigue testing, and provided the industrial motivation for this work. A quench dilatometer was used, along with subsequent scanning electron microscopy, to explore the microstructural variations produced as a function of thermal history. Rotating bending fatigue testing in the high cycle fatigue regime highlighted a two orders of magnitude reduction in fatigue life due to an increased quenching transfer time. The increased quench transfer time was shown to create packets of co-oriented α laths that facilitated crack initiation. Fatigue crack growth rate measurements were also used to quantify post-initiation crack growth rates in microstructures produced by different quench delay times. Long crack growth rates were found to be similar for short and long quench delay times. Post-mortem fractographic analysis and electron back scattered diffraction aided in determining the microstructural influence on fatigue crack initiation and propagation, indicating that long, planar basal slip lengths contribute to crack nucleation. Based upon these findings, it is found that even minor variations in quench transfer time can significantly influence the high cycle fatigue life of titanium alloys." @default.
- W2907970912 created "2019-01-11" @default.
- W2907970912 creator A5089547465 @default.
- W2907970912 date "2016-12-31" @default.
- W2907970912 modified "2023-09-28" @default.
- W2907970912 title "Effects of thermal processing variations on microstructure and high cycle fatigue of beta-STOA Ti-6Al-4V" @default.
- W2907970912 hasPublicationYear "2016" @default.
- W2907970912 type Work @default.
- W2907970912 sameAs 2907970912 @default.
- W2907970912 citedByCount "0" @default.
- W2907970912 crossrefType "dissertation" @default.
- W2907970912 hasAuthorship W2907970912A5089547465 @default.
- W2907970912 hasConcept C121332964 @default.
- W2907970912 hasConcept C121745418 @default.
- W2907970912 hasConcept C159985019 @default.
- W2907970912 hasConcept C191897082 @default.
- W2907970912 hasConcept C192562407 @default.
- W2907970912 hasConcept C2780026712 @default.
- W2907970912 hasConcept C59085676 @default.
- W2907970912 hasConcept C62520636 @default.
- W2907970912 hasConcept C69809600 @default.
- W2907970912 hasConcept C75512024 @default.
- W2907970912 hasConcept C87976508 @default.
- W2907970912 hasConcept C8953137 @default.
- W2907970912 hasConcept C91881484 @default.
- W2907970912 hasConcept C96494537 @default.
- W2907970912 hasConceptScore W2907970912C121332964 @default.
- W2907970912 hasConceptScore W2907970912C121745418 @default.
- W2907970912 hasConceptScore W2907970912C159985019 @default.
- W2907970912 hasConceptScore W2907970912C191897082 @default.
- W2907970912 hasConceptScore W2907970912C192562407 @default.
- W2907970912 hasConceptScore W2907970912C2780026712 @default.
- W2907970912 hasConceptScore W2907970912C59085676 @default.
- W2907970912 hasConceptScore W2907970912C62520636 @default.
- W2907970912 hasConceptScore W2907970912C69809600 @default.
- W2907970912 hasConceptScore W2907970912C75512024 @default.
- W2907970912 hasConceptScore W2907970912C87976508 @default.
- W2907970912 hasConceptScore W2907970912C8953137 @default.
- W2907970912 hasConceptScore W2907970912C91881484 @default.
- W2907970912 hasConceptScore W2907970912C96494537 @default.
- W2907970912 hasLocation W29079709121 @default.
- W2907970912 hasOpenAccess W2907970912 @default.
- W2907970912 hasPrimaryLocation W29079709121 @default.
- W2907970912 hasRelatedWork W1978937628 @default.
- W2907970912 hasRelatedWork W1979964348 @default.
- W2907970912 hasRelatedWork W2019712706 @default.
- W2907970912 hasRelatedWork W2026723013 @default.
- W2907970912 hasRelatedWork W2036198440 @default.
- W2907970912 hasRelatedWork W2059319421 @default.
- W2907970912 hasRelatedWork W2089459511 @default.
- W2907970912 hasRelatedWork W2130896741 @default.
- W2907970912 hasRelatedWork W2331619266 @default.
- W2907970912 hasRelatedWork W2344888091 @default.
- W2907970912 hasRelatedWork W2390176615 @default.
- W2907970912 hasRelatedWork W2619637804 @default.
- W2907970912 hasRelatedWork W2742324943 @default.
- W2907970912 hasRelatedWork W2807278317 @default.
- W2907970912 hasRelatedWork W2917140214 @default.
- W2907970912 hasRelatedWork W3001508798 @default.
- W2907970912 hasRelatedWork W3035949233 @default.
- W2907970912 hasRelatedWork W3084122704 @default.
- W2907970912 hasRelatedWork W3150638769 @default.
- W2907970912 hasRelatedWork W142674735 @default.
- W2907970912 isParatext "false" @default.
- W2907970912 isRetracted "false" @default.
- W2907970912 magId "2907970912" @default.
- W2907970912 workType "dissertation" @default.