- W2912221709 abstract "Powder metallurgy techniques have been used to study the dispersion strengthening in iron-based alloys containing alumina, zirconia, or titania. The degree of densification obtained from sintering experiments decreased with increasing oxide content in the carbonyl-iron: the presence of zirconia virtually prevent densification even at 1500 C. These particles, including zirconia, produce less inhibition in densification in stainless steel matrix. The final particle morphology, studied by optical and electron microscopy, was found to be closely related to the sinterability of the oxide phase, post-sintered particle size, and the fabrication technique used. In the case of alloys which had been sintered at 1350 C, and then forged and cold-rolled, the room-temperature strengthening effect of alumina was found to be significantly higher than that of zirconia; whereas, for alloys sintered at the same temperature but tested in the extruded condition there was no such difference in strengthening effect. Furthermore, sintering at 1200 C followed by forging and cold-rolling produced a similar degree of strengthening for each of the two dispersoids. These effects are interpreted in terms of the variation of particle morphology with production history. The analysis of yielding, yield-point phenomena, and work hardening characteristics of alloys containing various amounts of alumina or zirconia indicate a basic difference in the group and dynamic behaviour of dislocationsbetween iron-alumina and iron- zirconia alloys. The strain-rate-change experiments have been used to determine the activation volume and dislocation velocity exponent, and these have been correlated with the dispersion parameters. The activation volume decreased and the dislocation velocity exponent increased with decreasing free-spacing between the particles. Tensile properties were also determined at temperatures in the range 20-600 C for the extruded alloys. The dispersion strengthening effect decreased with increasing temperature in a manner which is consistent with the experimentally determined recrystallization temperature of these alloys." @default.
- W2912221709 created "2019-02-21" @default.
- W2912221709 creator A5039966199 @default.
- W2912221709 date "1969-01-01" @default.
- W2912221709 modified "2023-09-27" @default.
- W2912221709 title "Sintering and dispersion hardening of iron-based alloys." @default.
- W2912221709 hasPublicationYear "1969" @default.
- W2912221709 type Work @default.
- W2912221709 sameAs 2912221709 @default.
- W2912221709 citedByCount "0" @default.
- W2912221709 crossrefType "dissertation" @default.
- W2912221709 hasAuthorship W2912221709A5039966199 @default.
- W2912221709 hasConcept C120665830 @default.
- W2912221709 hasConcept C121332964 @default.
- W2912221709 hasConcept C123609680 @default.
- W2912221709 hasConcept C127413603 @default.
- W2912221709 hasConcept C134132462 @default.
- W2912221709 hasConcept C159985019 @default.
- W2912221709 hasConcept C177562468 @default.
- W2912221709 hasConcept C187530423 @default.
- W2912221709 hasConcept C191897082 @default.
- W2912221709 hasConcept C192562407 @default.
- W2912221709 hasConcept C2777581544 @default.
- W2912221709 hasConcept C2779851234 @default.
- W2912221709 hasConcept C42360764 @default.
- W2912221709 hasConcept C65590680 @default.
- W2912221709 hasConcept C7794659 @default.
- W2912221709 hasConceptScore W2912221709C120665830 @default.
- W2912221709 hasConceptScore W2912221709C121332964 @default.
- W2912221709 hasConceptScore W2912221709C123609680 @default.
- W2912221709 hasConceptScore W2912221709C127413603 @default.
- W2912221709 hasConceptScore W2912221709C134132462 @default.
- W2912221709 hasConceptScore W2912221709C159985019 @default.
- W2912221709 hasConceptScore W2912221709C177562468 @default.
- W2912221709 hasConceptScore W2912221709C187530423 @default.
- W2912221709 hasConceptScore W2912221709C191897082 @default.
- W2912221709 hasConceptScore W2912221709C192562407 @default.
- W2912221709 hasConceptScore W2912221709C2777581544 @default.
- W2912221709 hasConceptScore W2912221709C2779851234 @default.
- W2912221709 hasConceptScore W2912221709C42360764 @default.
- W2912221709 hasConceptScore W2912221709C65590680 @default.
- W2912221709 hasConceptScore W2912221709C7794659 @default.
- W2912221709 hasLocation W29122217091 @default.
- W2912221709 hasOpenAccess W2912221709 @default.
- W2912221709 hasPrimaryLocation W29122217091 @default.
- W2912221709 hasRelatedWork W1966102369 @default.
- W2912221709 hasRelatedWork W2010673011 @default.
- W2912221709 hasRelatedWork W2016779629 @default.
- W2912221709 hasRelatedWork W2034338064 @default.
- W2912221709 hasRelatedWork W2036280715 @default.
- W2912221709 hasRelatedWork W2063628488 @default.
- W2912221709 hasRelatedWork W2084542403 @default.
- W2912221709 hasRelatedWork W2088561893 @default.
- W2912221709 hasRelatedWork W2321337278 @default.
- W2912221709 hasRelatedWork W2358998531 @default.
- W2912221709 hasRelatedWork W2794231634 @default.
- W2912221709 hasRelatedWork W2807192368 @default.
- W2912221709 hasRelatedWork W2887131619 @default.
- W2912221709 hasRelatedWork W2888783167 @default.
- W2912221709 hasRelatedWork W2943705376 @default.
- W2912221709 hasRelatedWork W2986030275 @default.
- W2912221709 hasRelatedWork W3022444664 @default.
- W2912221709 hasRelatedWork W3048405162 @default.
- W2912221709 hasRelatedWork W198991345 @default.
- W2912221709 hasRelatedWork W2188799841 @default.
- W2912221709 isParatext "false" @default.
- W2912221709 isRetracted "false" @default.
- W2912221709 magId "2912221709" @default.
- W2912221709 workType "dissertation" @default.