- W2912634465 abstract "Thermal barrier coatings (TBCs) were deposited on DD6 specimens with [001] orientation, and the TBCs coated DD6 specimens were exposed at 1150 °C for one hour. Then, both the TBCs coated and bared specimens were subjected to high-cycle fatigue (HCF) testing at 900 °C in ambient atmosphere. The results revealed that the HCF life decreased with increasing stress amplitude and the fatigue strength of the TBCs coated substrate was higher than that of the bared alloy. There are two main reasons for this phenomenon, one is because the coating can bear part of the load and make the specimens stronger and the other is the existence of residual compressive stresses. SEM and TEM were used to observe the microstructure near the fracture. For the TBCs coated alloy, many pores and cracks appeared at the bond coat after HCF test, and the fatigue cracks may be resulted from some of them. In the process of testing, the crack expanded to the substrate and propagated along {111} octahedral slip planes." @default.
- W2912634465 created "2019-02-21" @default.
- W2912634465 creator A5002461917 @default.
- W2912634465 creator A5027531484 @default.
- W2912634465 creator A5080595106 @default.
- W2912634465 creator A5089822136 @default.
- W2912634465 date "2019-01-01" @default.
- W2912634465 modified "2023-09-24" @default.
- W2912634465 title "Fatigue Behavior of Thermal Barrier Coated DD6 Single Crystal Superalloy at 900 °C" @default.
- W2912634465 cites W164223319 @default.
- W2912634465 cites W1966734955 @default.
- W2912634465 cites W1972841378 @default.
- W2912634465 cites W1984777063 @default.
- W2912634465 cites W1986669150 @default.
- W2912634465 cites W2026123407 @default.
- W2912634465 cites W2030132377 @default.
- W2912634465 cites W2037577235 @default.
- W2912634465 cites W2045712399 @default.
- W2912634465 cites W2058551465 @default.
- W2912634465 cites W2059696069 @default.
- W2912634465 cites W2075659255 @default.
- W2912634465 cites W2077231500 @default.
- W2912634465 cites W2090841993 @default.
- W2912634465 cites W2138792587 @default.
- W2912634465 cites W2139287370 @default.
- W2912634465 cites W2168681186 @default.
- W2912634465 cites W2523548914 @default.
- W2912634465 doi "https://doi.org/10.1007/978-981-13-5944-6_34" @default.
- W2912634465 hasPublicationYear "2019" @default.
- W2912634465 type Work @default.
- W2912634465 sameAs 2912634465 @default.
- W2912634465 citedByCount "2" @default.
- W2912634465 countsByYear W29126344652022 @default.
- W2912634465 countsByYear W29126344652023 @default.
- W2912634465 crossrefType "book-chapter" @default.
- W2912634465 hasAuthorship W2912634465A5002461917 @default.
- W2912634465 hasAuthorship W2912634465A5027531484 @default.
- W2912634465 hasAuthorship W2912634465A5080595106 @default.
- W2912634465 hasAuthorship W2912634465A5089822136 @default.
- W2912634465 hasConcept C111368507 @default.
- W2912634465 hasConcept C127313418 @default.
- W2912634465 hasConcept C127413603 @default.
- W2912634465 hasConcept C146978453 @default.
- W2912634465 hasConcept C159985019 @default.
- W2912634465 hasConcept C176711861 @default.
- W2912634465 hasConcept C191897082 @default.
- W2912634465 hasConcept C192562407 @default.
- W2912634465 hasConcept C195268267 @default.
- W2912634465 hasConcept C207055975 @default.
- W2912634465 hasConcept C2777289219 @default.
- W2912634465 hasConcept C2780026712 @default.
- W2912634465 hasConcept C2781448156 @default.
- W2912634465 hasConcept C87976508 @default.
- W2912634465 hasConceptScore W2912634465C111368507 @default.
- W2912634465 hasConceptScore W2912634465C127313418 @default.
- W2912634465 hasConceptScore W2912634465C127413603 @default.
- W2912634465 hasConceptScore W2912634465C146978453 @default.
- W2912634465 hasConceptScore W2912634465C159985019 @default.
- W2912634465 hasConceptScore W2912634465C176711861 @default.
- W2912634465 hasConceptScore W2912634465C191897082 @default.
- W2912634465 hasConceptScore W2912634465C192562407 @default.
- W2912634465 hasConceptScore W2912634465C195268267 @default.
- W2912634465 hasConceptScore W2912634465C207055975 @default.
- W2912634465 hasConceptScore W2912634465C2777289219 @default.
- W2912634465 hasConceptScore W2912634465C2780026712 @default.
- W2912634465 hasConceptScore W2912634465C2781448156 @default.
- W2912634465 hasConceptScore W2912634465C87976508 @default.
- W2912634465 hasLocation W29126344651 @default.
- W2912634465 hasOpenAccess W2912634465 @default.
- W2912634465 hasPrimaryLocation W29126344651 @default.
- W2912634465 hasRelatedWork W1996687174 @default.
- W2912634465 hasRelatedWork W2010733322 @default.
- W2912634465 hasRelatedWork W2020660716 @default.
- W2912634465 hasRelatedWork W2058736572 @default.
- W2912634465 hasRelatedWork W2058945371 @default.
- W2912634465 hasRelatedWork W2089251307 @default.
- W2912634465 hasRelatedWork W2353788746 @default.
- W2912634465 hasRelatedWork W2379855728 @default.
- W2912634465 hasRelatedWork W4221060116 @default.
- W2912634465 hasRelatedWork W4303926928 @default.
- W2912634465 isParatext "false" @default.
- W2912634465 isRetracted "false" @default.
- W2912634465 magId "2912634465" @default.
- W2912634465 workType "book-chapter" @default.