- W2914763020 abstract "Abstract The magnetic properties of nanostructured Fe-49 wt.% Co-2 wt.% V alloy powder, synthesized by mechanically milling pre-alloyed gas-atomized powder, were investigated from cryogenic to high temperatures (60–900 K). At cryogenic temperatures, the as-milled nanostructured alloy powder exhibited stable magnetic properties. The decrease in MS was by a minuscule ∼2 %—from ∼212 ± 1 Am2/kg (at 300 K) to ∼217 ± 2 Am2/kg (at 60 K), and the increase in HCI was by a modest (∼8%)—from ∼6.1 kA/m (at 300 K) to ∼6.6 kA/m (at 60 K). At high temperatures (>300 K), both MS and HCI decreased. Annealing improved the soft-magnetic properties of the as-milled alloy powder. The annealed alloy powders retained their nanostructure—grain size ∼15–30 nm. The as-milled alloy annealed at 900 K showed the highest MS and the lowest HCI among all the other annealing temperatures—MS increased by ∼7%–∼225 ± 1 Am2/kg and the HCI decreased to ∼1.0 kA/m. The annealed nanostructured Fe-49 wt% Co-2 wt.% V alloy powder exhibited magnetic properties comparable to a few annealed nanostructured Fe- Co-based alloys. The annealed nanostructured alloy powder displayed fairly stable magnetic properties over a wide range of cryogenic temperatures. The annealed Fe-49 wt.% Co-2 wt.% V alloy powder is better suited for soft-magnetic applications than the as-milled powder, from ambient to cryogenic temperatures." @default.
- W2914763020 created "2019-02-21" @default.
- W2914763020 creator A5008768885 @default.
- W2914763020 creator A5070289637 @default.
- W2914763020 creator A5075761758 @default.
- W2914763020 creator A5080281879 @default.
- W2914763020 date "2019-04-01" @default.
- W2914763020 modified "2023-09-27" @default.
- W2914763020 title "Influence of temperature on the magnetic properties of nanostructured Fe-49 wt.% Co-2 wt.% V alloy powder synthesized by mechanically milling pre-alloyed gas-atomized powder" @default.
- W2914763020 cites W1524406403 @default.
- W2914763020 cites W175780446 @default.
- W2914763020 cites W1970992254 @default.
- W2914763020 cites W1973649830 @default.
- W2914763020 cites W1984734551 @default.
- W2914763020 cites W1995063595 @default.
- W2914763020 cites W2000181466 @default.
- W2914763020 cites W2000467880 @default.
- W2914763020 cites W2012380774 @default.
- W2914763020 cites W2021835188 @default.
- W2914763020 cites W2029501454 @default.
- W2914763020 cites W2032725918 @default.
- W2914763020 cites W2034517316 @default.
- W2914763020 cites W2035911989 @default.
- W2914763020 cites W2038211881 @default.
- W2914763020 cites W2040432202 @default.
- W2914763020 cites W2052603348 @default.
- W2914763020 cites W2062194661 @default.
- W2914763020 cites W2065403288 @default.
- W2914763020 cites W2069159580 @default.
- W2914763020 cites W2075258272 @default.
- W2914763020 cites W2094054659 @default.
- W2914763020 cites W2099567425 @default.
- W2914763020 cites W2108421067 @default.
- W2914763020 cites W2116578727 @default.
- W2914763020 cites W2155138330 @default.
- W2914763020 cites W2765274437 @default.
- W2914763020 cites W2792627017 @default.
- W2914763020 cites W4210978293 @default.
- W2914763020 doi "https://doi.org/10.1016/j.matchemphys.2019.01.044" @default.
- W2914763020 hasPublicationYear "2019" @default.
- W2914763020 type Work @default.
- W2914763020 sameAs 2914763020 @default.
- W2914763020 citedByCount "6" @default.
- W2914763020 countsByYear W29147630202019 @default.
- W2914763020 countsByYear W29147630202020 @default.
- W2914763020 countsByYear W29147630202021 @default.
- W2914763020 countsByYear W29147630202023 @default.
- W2914763020 crossrefType "journal-article" @default.
- W2914763020 hasAuthorship W2914763020A5008768885 @default.
- W2914763020 hasAuthorship W2914763020A5070289637 @default.
- W2914763020 hasAuthorship W2914763020A5075761758 @default.
- W2914763020 hasAuthorship W2914763020A5080281879 @default.
- W2914763020 hasConcept C127413603 @default.
- W2914763020 hasConcept C191897082 @default.
- W2914763020 hasConcept C192562407 @default.
- W2914763020 hasConcept C2780026712 @default.
- W2914763020 hasConcept C42360764 @default.
- W2914763020 hasConceptScore W2914763020C127413603 @default.
- W2914763020 hasConceptScore W2914763020C191897082 @default.
- W2914763020 hasConceptScore W2914763020C192562407 @default.
- W2914763020 hasConceptScore W2914763020C2780026712 @default.
- W2914763020 hasConceptScore W2914763020C42360764 @default.
- W2914763020 hasFunder F4320309652 @default.
- W2914763020 hasLocation W29147630201 @default.
- W2914763020 hasOpenAccess W2914763020 @default.
- W2914763020 hasPrimaryLocation W29147630201 @default.
- W2914763020 hasRelatedWork W1507116910 @default.
- W2914763020 hasRelatedWork W1969887887 @default.
- W2914763020 hasRelatedWork W1991986159 @default.
- W2914763020 hasRelatedWork W1999962534 @default.
- W2914763020 hasRelatedWork W2089251307 @default.
- W2914763020 hasRelatedWork W2322045178 @default.
- W2914763020 hasRelatedWork W2783283445 @default.
- W2914763020 hasRelatedWork W2996358649 @default.
- W2914763020 hasRelatedWork W4206568719 @default.
- W2914763020 hasRelatedWork W4303926928 @default.
- W2914763020 hasVolume "227" @default.
- W2914763020 isParatext "false" @default.
- W2914763020 isRetracted "false" @default.
- W2914763020 magId "2914763020" @default.
- W2914763020 workType "article" @default.