- W2917495086 endingPage "473" @default.
- W2917495086 startingPage "473" @default.
- W2917495086 abstract "Supported iron oxides have been established as an important class of catalyst for high temperature sulfuric acid decomposition. With an objective to elucidate the role of support in modifying the overall catalytic properties of dispersed iron oxide catalysts, a series of supported iron oxide based catalysts, Fe2O3 (15 wt%)/MO2 (M = Zr, Ce, Ti and Si), synthesized by adsorption-equilibrium method, is investigated for sulfuric acid decomposition reaction. The structure of dispersed iron oxide phases largely depended on the nature of the support oxide as revealed by the XRD and Mössbauer studies. α-Fe2O3 is found to be present as a major phase on ZrO2 and CeO2 support while ε-Fe2O3 was the major phase on silica supported iron oxide. On the other hand, presence of mixed oxide Fe2TiO5 was revealed over TiO2 support. Strong dispersed metal oxide-support interactions inhibited the total reduction of the dispersed phase on SiO2 and TiO2 as compared to complete reduction of dispersed iron oxide on CeO2 and ZrO2 supports during temperature programmed reduction upto 1000 °C. The order of catalytic activity at a temperature of ∼750 °C is observed as Fe2O3/SiO2 > Fe2TiO5/TiO2 > Fe2O3/ZrO2 > Fe2O3/CeO2, while at higher temperatures of ∼900 °C the SO2 yield is found to be comparable for all catalysts. A relationship between the rate of sulfate decomposition and catalytic activity is established through detailed TG-DTA investigations of sulfated catalyst and support. Considerable influence of the support oxide on the composition, structure, redox properties, morphology and catalytic activities of the active iron oxide dispersed phase has been observed. Thus, the support oxides operate as a critical component in the complex supported metal oxide catalysts and these findings might influence the design and development of future high temperature sulfuric acid decomposition catalysts." @default.
- W2917495086 created "2019-03-02" @default.
- W2917495086 creator A5024816713 @default.
- W2917495086 creator A5087627752 @default.
- W2917495086 date "2018-01-01" @default.
- W2917495086 modified "2023-10-18" @default.
- W2917495086 title "TMREES Conference Series: A preface to the special issue section on “The International Conference on Technologies and Materials for Renewable Energy, Environment and Sustainability (TMREES17), 21–24 April 2017, Beirut, Lebanon”" @default.
- W2917495086 doi "https://doi.org/10.1016/j.ijhydene.2017.11.108" @default.
- W2917495086 hasPublicationYear "2018" @default.
- W2917495086 type Work @default.
- W2917495086 sameAs 2917495086 @default.
- W2917495086 citedByCount "0" @default.
- W2917495086 crossrefType "journal-article" @default.
- W2917495086 hasAuthorship W2917495086A5024816713 @default.
- W2917495086 hasAuthorship W2917495086A5087627752 @default.
- W2917495086 hasConcept C124681953 @default.
- W2917495086 hasConcept C127413603 @default.
- W2917495086 hasConcept C161790260 @default.
- W2917495086 hasConcept C178790620 @default.
- W2917495086 hasConcept C179104552 @default.
- W2917495086 hasConcept C185592680 @default.
- W2917495086 hasConcept C191897082 @default.
- W2917495086 hasConcept C192562407 @default.
- W2917495086 hasConcept C2777697756 @default.
- W2917495086 hasConcept C2778199549 @default.
- W2917495086 hasConcept C2779131772 @default.
- W2917495086 hasConcept C2779851234 @default.
- W2917495086 hasConcept C42360764 @default.
- W2917495086 hasConceptScore W2917495086C124681953 @default.
- W2917495086 hasConceptScore W2917495086C127413603 @default.
- W2917495086 hasConceptScore W2917495086C161790260 @default.
- W2917495086 hasConceptScore W2917495086C178790620 @default.
- W2917495086 hasConceptScore W2917495086C179104552 @default.
- W2917495086 hasConceptScore W2917495086C185592680 @default.
- W2917495086 hasConceptScore W2917495086C191897082 @default.
- W2917495086 hasConceptScore W2917495086C192562407 @default.
- W2917495086 hasConceptScore W2917495086C2777697756 @default.
- W2917495086 hasConceptScore W2917495086C2778199549 @default.
- W2917495086 hasConceptScore W2917495086C2779131772 @default.
- W2917495086 hasConceptScore W2917495086C2779851234 @default.
- W2917495086 hasConceptScore W2917495086C42360764 @default.
- W2917495086 hasIssue "1" @default.
- W2917495086 hasLocation W29174950861 @default.
- W2917495086 hasOpenAccess W2917495086 @default.
- W2917495086 hasPrimaryLocation W29174950861 @default.
- W2917495086 hasRelatedWork W1990717809 @default.
- W2917495086 hasRelatedWork W1992158717 @default.
- W2917495086 hasRelatedWork W2044382906 @default.
- W2917495086 hasRelatedWork W2071704543 @default.
- W2917495086 hasRelatedWork W2085323481 @default.
- W2917495086 hasRelatedWork W2113303509 @default.
- W2917495086 hasRelatedWork W2793508912 @default.
- W2917495086 hasRelatedWork W2884689957 @default.
- W2917495086 hasRelatedWork W297328956 @default.
- W2917495086 hasRelatedWork W2060215328 @default.
- W2917495086 hasVolume "43" @default.
- W2917495086 isParatext "false" @default.
- W2917495086 isRetracted "false" @default.
- W2917495086 magId "2917495086" @default.
- W2917495086 workType "article" @default.