- W2918084719 endingPage "36" @default.
- W2918084719 startingPage "28" @default.
- W2918084719 abstract "Pure cobalt (II) boride nanoparticles/nanocylinders were synthesized in aqueous media under Argon blanket using cobalt chloride (CoCl 2 ) and sodium borohydride (NaBH 4 ) as reactants. CoCl 2 (0.325 g) was dissolved in cold distilled water (DDI) and the solution was introduced into a sealed glass reactor. Then, NaBH 4 was then dissolved in DDI (90 mL) and the solution was added drop-wise into the reactor and stirred magnetically at 300 rpm. By the addition of NaBH 4 (10 mL, 0.225 g) solution, amorphous b lack cobalt boride particles were synthesized immediately. The presence of crystalline Co 2 B phase with high purity in the nanocylinders which is obtained by calcination at 500 o C was shown by X-ray diffraction spectroscopy. An amorphous Co 2 B structure was observed with the sample dried under vacuum. In the synthesis runs, Co 2 B nanoparticles with different morphological characteristics were achieved by changing the initial CoCl 2 concentration and the reaction period. A microscopic structure in the form of nanocylinders was observed for the calcined products. The nanocylinder diameter increased from ca. 30 nm to 100 nm by increasing the reaction time from 3 to 120 min. CoCl 2 initial concentration was also found another factor increasing the nanocylinder diameter. The nanocylinders with diameters between 80-500 nm were obtained by increasing CoCl 2 concentration from 12.6 to 100.1 mM. The lowest and highest saturation magnetization values were obtained 19 and 69 emu/g for crystalline sample calcined under air (Co-Co 2 B mixture) and amorphous Co 2 B sample obtained by vacuum-drying, respectively. Amorphous and crystalline Co 2 B samples were used as catalyst for Hydrogen generation by the hydrolysis of NaBH 4 in aqueous media. Amorphous Co 2 B gave significantly higher H 2 generation rate with respect to the catalysts prepared by calcination of amorphous Co 2 B under air or Argon at 500 o C. The maximum H 2 generation rate was obtained as 1.1 L/g catalyst.min by using amorphous Co 2 B with 1 % w/w of initial NaBH 4 concentration." @default.
- W2918084719 created "2019-03-02" @default.
- W2918084719 creator A5050854338 @default.
- W2918084719 creator A5070041882 @default.
- W2918084719 date "2017-03-16" @default.
- W2918084719 modified "2023-09-24" @default.
- W2918084719 title "Synthesis of Co2B nanostructures and their catalytic properties for hydrogen generation" @default.
- W2918084719 hasPublicationYear "2017" @default.
- W2918084719 type Work @default.
- W2918084719 sameAs 2918084719 @default.
- W2918084719 citedByCount "0" @default.
- W2918084719 crossrefType "journal-article" @default.
- W2918084719 hasAuthorship W2918084719A5050854338 @default.
- W2918084719 hasAuthorship W2918084719A5070041882 @default.
- W2918084719 hasConcept C127413603 @default.
- W2918084719 hasConcept C13965031 @default.
- W2918084719 hasConcept C155672457 @default.
- W2918084719 hasConcept C161790260 @default.
- W2918084719 hasConcept C171250308 @default.
- W2918084719 hasConcept C175708663 @default.
- W2918084719 hasConcept C178790620 @default.
- W2918084719 hasConcept C179104552 @default.
- W2918084719 hasConcept C184651966 @default.
- W2918084719 hasConcept C185592680 @default.
- W2918084719 hasConcept C192562407 @default.
- W2918084719 hasConcept C2779429693 @default.
- W2918084719 hasConcept C2780048404 @default.
- W2918084719 hasConcept C42360764 @default.
- W2918084719 hasConcept C43617362 @default.
- W2918084719 hasConcept C515602321 @default.
- W2918084719 hasConcept C56052488 @default.
- W2918084719 hasConcept C7082614 @default.
- W2918084719 hasConcept C8010536 @default.
- W2918084719 hasConceptScore W2918084719C127413603 @default.
- W2918084719 hasConceptScore W2918084719C13965031 @default.
- W2918084719 hasConceptScore W2918084719C155672457 @default.
- W2918084719 hasConceptScore W2918084719C161790260 @default.
- W2918084719 hasConceptScore W2918084719C171250308 @default.
- W2918084719 hasConceptScore W2918084719C175708663 @default.
- W2918084719 hasConceptScore W2918084719C178790620 @default.
- W2918084719 hasConceptScore W2918084719C179104552 @default.
- W2918084719 hasConceptScore W2918084719C184651966 @default.
- W2918084719 hasConceptScore W2918084719C185592680 @default.
- W2918084719 hasConceptScore W2918084719C192562407 @default.
- W2918084719 hasConceptScore W2918084719C2779429693 @default.
- W2918084719 hasConceptScore W2918084719C2780048404 @default.
- W2918084719 hasConceptScore W2918084719C42360764 @default.
- W2918084719 hasConceptScore W2918084719C43617362 @default.
- W2918084719 hasConceptScore W2918084719C515602321 @default.
- W2918084719 hasConceptScore W2918084719C56052488 @default.
- W2918084719 hasConceptScore W2918084719C7082614 @default.
- W2918084719 hasConceptScore W2918084719C8010536 @default.
- W2918084719 hasIssue "1" @default.
- W2918084719 hasLocation W29180847191 @default.
- W2918084719 hasOpenAccess W2918084719 @default.
- W2918084719 hasPrimaryLocation W29180847191 @default.
- W2918084719 hasRelatedWork W109271763 @default.
- W2918084719 hasRelatedWork W1971965316 @default.
- W2918084719 hasRelatedWork W2028948323 @default.
- W2918084719 hasRelatedWork W2045500269 @default.
- W2918084719 hasRelatedWork W2045862168 @default.
- W2918084719 hasRelatedWork W2062429149 @default.
- W2918084719 hasRelatedWork W2210586088 @default.
- W2918084719 hasRelatedWork W2343108191 @default.
- W2918084719 hasRelatedWork W2357615345 @default.
- W2918084719 hasRelatedWork W2408716569 @default.
- W2918084719 hasRelatedWork W2469577475 @default.
- W2918084719 hasRelatedWork W2558992551 @default.
- W2918084719 hasRelatedWork W2727652406 @default.
- W2918084719 hasRelatedWork W2790541323 @default.
- W2918084719 hasRelatedWork W2807606377 @default.
- W2918084719 hasRelatedWork W2899227694 @default.
- W2918084719 hasRelatedWork W2965575745 @default.
- W2918084719 hasRelatedWork W3017019369 @default.
- W2918084719 hasRelatedWork W869960273 @default.
- W2918084719 hasRelatedWork W2557135413 @default.
- W2918084719 hasVolume "2" @default.
- W2918084719 isParatext "false" @default.
- W2918084719 isRetracted "false" @default.
- W2918084719 magId "2918084719" @default.
- W2918084719 workType "article" @default.