- W2918102671 abstract "The focus of this work is on comparison the compression strength of the cementitious - limestone composite samples made according to different recipes. The study includes the results of own experimental research of the high performance cementitious - limestone composites as well as an analytical calculations of the mixture proportioning and designed compressive strength. Mixture proportioning based on the formulas of Funk and Dinger was determined. In the following step compressive strength based on the modified formulas Larrard was designed. Three test samples with dimensions of 100 x 100 x 100 mm were made for each recipe B1, B2, and B3. Information on the curing of research samples, cement, microsilica, limestone powder and limestone sand was presented. On the basis of experimental results after 7 days curing with using the proper amount of superplasticizer, the following section of the paper presents results after 28 days. Then a reference sample for the comparative analysis of the mixture proportioning was made and marked as B4. Based on the reference sample, the next samples with removed fractions (B5 < 0,063mm; B6 < 0,063mm and 0,063-0,125mm) were made. The last sample marked B7 with a different amount of cement in relation to samples B6 was also made. Results of compressive strength for samples B1-B7 were compared. Direct measurements allowed us to observe that B1 - B3 samples with different amounts of superplasticizer have compressive strengths differing by up to 3% both after 7 and 28 days. Samples marked B5 and B6 shown increased compressive strength by 6% and 12%, respectively in relation to the sample B4. The sample B7. The results demonstrated that sample B7 indicate the reduced compressive strength in comparison to sample B6." @default.
- W2918102671 created "2019-03-02" @default.
- W2918102671 creator A5009725947 @default.
- W2918102671 creator A5021150156 @default.
- W2918102671 creator A5073383906 @default.
- W2918102671 date "2019-02-23" @default.
- W2918102671 modified "2023-09-25" @default.
- W2918102671 title "Effect of Mixture Proportioning of the High Performance Cementitious – Limestone Composites on the Compressive Strength" @default.
- W2918102671 cites W1968656497 @default.
- W2918102671 cites W2014188371 @default.
- W2918102671 cites W2045843887 @default.
- W2918102671 cites W2063029034 @default.
- W2918102671 cites W2070240161 @default.
- W2918102671 cites W2089261572 @default.
- W2918102671 cites W2120445725 @default.
- W2918102671 cites W2125527927 @default.
- W2918102671 cites W2130329221 @default.
- W2918102671 cites W2486308706 @default.
- W2918102671 cites W2541606225 @default.
- W2918102671 cites W2592213108 @default.
- W2918102671 cites W2753746924 @default.
- W2918102671 cites W4256236742 @default.
- W2918102671 doi "https://doi.org/10.1088/1757-899x/471/3/032050" @default.
- W2918102671 hasPublicationYear "2019" @default.
- W2918102671 type Work @default.
- W2918102671 sameAs 2918102671 @default.
- W2918102671 citedByCount "1" @default.
- W2918102671 countsByYear W29181026712020 @default.
- W2918102671 crossrefType "journal-article" @default.
- W2918102671 hasAuthorship W2918102671A5009725947 @default.
- W2918102671 hasAuthorship W2918102671A5021150156 @default.
- W2918102671 hasAuthorship W2918102671A5073383906 @default.
- W2918102671 hasBestOaLocation W29181026711 @default.
- W2918102671 hasConcept C11839303 @default.
- W2918102671 hasConcept C132976073 @default.
- W2918102671 hasConcept C159985019 @default.
- W2918102671 hasConcept C192562407 @default.
- W2918102671 hasConcept C192757587 @default.
- W2918102671 hasConcept C2779666059 @default.
- W2918102671 hasConcept C30407753 @default.
- W2918102671 hasConcept C523993062 @default.
- W2918102671 hasConceptScore W2918102671C11839303 @default.
- W2918102671 hasConceptScore W2918102671C132976073 @default.
- W2918102671 hasConceptScore W2918102671C159985019 @default.
- W2918102671 hasConceptScore W2918102671C192562407 @default.
- W2918102671 hasConceptScore W2918102671C192757587 @default.
- W2918102671 hasConceptScore W2918102671C2779666059 @default.
- W2918102671 hasConceptScore W2918102671C30407753 @default.
- W2918102671 hasConceptScore W2918102671C523993062 @default.
- W2918102671 hasLocation W29181026711 @default.
- W2918102671 hasOpenAccess W2918102671 @default.
- W2918102671 hasPrimaryLocation W29181026711 @default.
- W2918102671 hasRelatedWork W1643163489 @default.
- W2918102671 hasRelatedWork W1986862433 @default.
- W2918102671 hasRelatedWork W2020261311 @default.
- W2918102671 hasRelatedWork W2076485674 @default.
- W2918102671 hasRelatedWork W2389242885 @default.
- W2918102671 hasRelatedWork W2725268246 @default.
- W2918102671 hasRelatedWork W3198897256 @default.
- W2918102671 hasRelatedWork W4365813097 @default.
- W2918102671 hasRelatedWork W844712698 @default.
- W2918102671 hasRelatedWork W3126380050 @default.
- W2918102671 hasVolume "471" @default.
- W2918102671 isParatext "false" @default.
- W2918102671 isRetracted "false" @default.
- W2918102671 magId "2918102671" @default.
- W2918102671 workType "article" @default.