• W2918600538 abstract "This work attempts to a better understanding of the fatigue damage in ferrite-pearlite steels in the Very High Cycle Fatigue (VHCF) domain. The influences of two parameters, pearlite phase percentage and free interstitial atoms percentage in solid solution, are investigated to understand dissipative mechanisms under 20 kHz high frequency fatigue loading. In-situ infrared thermography is carried out to record the temperature changes, while fractography studies and microscope observations are conducted to investigate the dissipative mechanism on the surface of specimens.For body centered cubic (BCC) materials, under high stress amplitudes, a sudden increase of the temperature occurs without a crack initiation and fracture. The inevitable temperature increase up to hundreds of degrees at high stress amplitudes, is caused mainly by the screw dislocations mobility, which is the key to explaining the observed fatigue behavior and thermal response of BCC structure under high frequency loading. Therefore, PSBs on surface and micro-voids in matrix emerge massively, accompanying with this abrupt temperature increase. These phenomena are considered as transition of deformation mechanism from thermal regime to athermal regime. At low amplitudes, few PSBs or surface roughness are still observed on the specimen surface. Through the cycles of PSB appearance on armco-iron, it’s found that PSBs are inclined to appear before 1x10(7)cycles, and PSB threshold lies below the conventional fatigue limit. The increase of pearlite phase content weakens the temperature elevation, and strengthens the fatigue properties. The presence of free interstitial atoms in steels results in appearence of a secondary temperature increase in the stabilized temperature part (100-200 degree). This behavior seems to be related to the interaction of edge dislocations with free interstitial atoms. Moreover, the remarkable hardening-softening-hardening phenomenon after the sudden temperature elevation to above 300 degree is thought as the interaction of multiplicated screw dislocations and free interstitial atoms." @default.
• W2918600538 created "2019-03-11" @default.
• W2918600538 creator A5032626813 @default.
• W2918600538 date "2019-01-30" @default.
• W2918600538 modified "2023-09-23" @default.
• W2918600538 title "Thermomechanical study of the gigacycle fatigue behavior of pure iron and carbon-manganese steels : influence of chemical composition and microstructure on damage and crack initiation mechanism" @default.
• W2918600538 hasPublicationYear "2019" @default.
• W2918600538 type Work @default.
• W2918600538 sameAs 2918600538 @default.
• W2918600538 citedByCount "0" @default.
• W2918600538 crossrefType "dissertation" @default.
• W2918600538 hasAuthorship W2918600538A5032626813 @default.
• W2918600538 hasConcept C131850400 @default.
• W2918600538 hasConcept C159985019 @default.
• W2918600538 hasConcept C191897082 @default.
• W2918600538 hasConcept C192562407 @default.
• W2918600538 hasConcept C37210646 @default.
• W2918600538 hasConcept C45780264 @default.
• W2918600538 hasConcept C5701217 @default.
• W2918600538 hasConcept C61039299 @default.
• W2918600538 hasConcept C87976508 @default.
• W2918600538 hasConcept C96288455 @default.
• W2918600538 hasConceptScore W2918600538C131850400 @default.
• W2918600538 hasConceptScore W2918600538C159985019 @default.
• W2918600538 hasConceptScore W2918600538C191897082 @default.
• W2918600538 hasConceptScore W2918600538C192562407 @default.
• W2918600538 hasConceptScore W2918600538C37210646 @default.
• W2918600538 hasConceptScore W2918600538C45780264 @default.
• W2918600538 hasConceptScore W2918600538C5701217 @default.
• W2918600538 hasConceptScore W2918600538C61039299 @default.
• W2918600538 hasConceptScore W2918600538C87976508 @default.
• W2918600538 hasConceptScore W2918600538C96288455 @default.
• W2918600538 hasLocation W29186005381 @default.
• W2918600538 hasOpenAccess W2918600538 @default.
• W2918600538 hasPrimaryLocation W29186005381 @default.
• W2918600538 hasRelatedWork W1970535616 @default.
• W2918600538 hasRelatedWork W1970943898 @default.
• W2918600538 hasRelatedWork W1971613235 @default.
• W2918600538 hasRelatedWork W2005930959 @default.
• W2918600538 hasRelatedWork W2013042091 @default.
• W2918600538 hasRelatedWork W2013223595 @default.
• W2918600538 hasRelatedWork W2027350521 @default.
• W2918600538 hasRelatedWork W2031477130 @default.
• W2918600538 hasRelatedWork W2061452570 @default.
• W2918600538 hasRelatedWork W2074510010 @default.
• W2918600538 hasRelatedWork W2161409989 @default.
• W2918600538 hasRelatedWork W2265085802 @default.
• W2918600538 hasRelatedWork W2302099116 @default.
• W2918600538 hasRelatedWork W2381013668 @default.
• W2918600538 hasRelatedWork W2901062159 @default.
• W2918600538 hasRelatedWork W2901455992 @default.
• W2918600538 hasRelatedWork W2907970912 @default.
• W2918600538 hasRelatedWork W2912215519 @default.
• W2918600538 hasRelatedWork W2922337270 @default.
• W2918600538 hasRelatedWork W3001508798 @default.
• W2918600538 isParatext "false" @default.
• W2918600538 isRetracted "false" @default.
• W2918600538 magId "2918600538" @default.
• W2918600538 workType "dissertation" @default.