- W2922278316 abstract "This paper aims to study the mechanical properties of mixed isotropic carbon fiber 3D printed composites and further investigates the influence of hot press on the [0°/45°/90°]2 fiber angles composite with varying temperature, pressure and time. Tensile tests, autoclave treatment and microstructural observation were utilized to characterize the composites. Results revealed that the [0°/45°/90°]2 performed the highest tensile strength of 79 MPa and modulus of 3.51 GPa, compared to [30°/45°/60°]2 and [15°/45°/75°]2. This is due to the fibers along the tensile axis angle that bears maximum load in longitudinal direction. At 200 °C temperature, the hot pressed composites presented the highest tensile strength of 98 MPa and modulus of 3.93 GPa than non-hot pressed. Increased temperature caused better interface wettability between fibers and matrix. At 200 kPa pressure, the hot pressed composites showed the highest tensile strength of 100 MPa and modulus of 4.06 GPa than non-hot pressed. Further increased pressure resulted in lower tensile strength and modulus, as the material became stiffer pushing more matrix material to side leaving numerous fibers unbounded by the matrix. For 30 min withholding time, the hot pressed composites indicated the highest tensile strength of 106 MPa and modulus of 4.27 GPa than non-hot pressed. Increased time caused strongest interface bonding by removing the air gaps induced during printing between fibers and matrix. Results revealed that hot press significantly improved the mechanical properties of carbon fiber 3D printed composites." @default.
- W2922278316 created "2019-03-22" @default.
- W2922278316 creator A5007179001 @default.
- W2922278316 creator A5019094519 @default.
- W2922278316 creator A5033988887 @default.
- W2922278316 creator A5044906378 @default.
- W2922278316 creator A5082450254 @default.
- W2922278316 date "2019-05-01" @default.
- W2922278316 modified "2023-10-14" @default.
- W2922278316 title "Influence of mixed isotropic fiber angles and hot press on the mechanical properties of 3D printed composites" @default.
- W2922278316 cites W1782215331 @default.
- W2922278316 cites W1966049388 @default.
- W2922278316 cites W1988671598 @default.
- W2922278316 cites W1995105354 @default.
- W2922278316 cites W2001493762 @default.
- W2922278316 cites W2002869883 @default.
- W2922278316 cites W2016034459 @default.
- W2922278316 cites W2036828531 @default.
- W2922278316 cites W2058467218 @default.
- W2922278316 cites W2093500299 @default.
- W2922278316 cites W2118678798 @default.
- W2922278316 cites W2231801657 @default.
- W2922278316 cites W2323685424 @default.
- W2922278316 cites W2415066110 @default.
- W2922278316 cites W2436552658 @default.
- W2922278316 cites W2506707078 @default.
- W2922278316 cites W2553221934 @default.
- W2922278316 cites W2563122849 @default.
- W2922278316 cites W2587827816 @default.
- W2922278316 cites W2601051689 @default.
- W2922278316 cites W2613577497 @default.
- W2922278316 cites W2625149712 @default.
- W2922278316 cites W2753859052 @default.
- W2922278316 cites W2760827413 @default.
- W2922278316 cites W2765491978 @default.
- W2922278316 cites W2768196135 @default.
- W2922278316 cites W2791815149 @default.
- W2922278316 cites W2792630086 @default.
- W2922278316 cites W2794373177 @default.
- W2922278316 cites W2809894170 @default.
- W2922278316 cites W566602208 @default.
- W2922278316 doi "https://doi.org/10.1016/j.addma.2019.03.008" @default.
- W2922278316 hasPublicationYear "2019" @default.
- W2922278316 type Work @default.
- W2922278316 sameAs 2922278316 @default.
- W2922278316 citedByCount "21" @default.
- W2922278316 countsByYear W29222783162019 @default.
- W2922278316 countsByYear W29222783162020 @default.
- W2922278316 countsByYear W29222783162021 @default.
- W2922278316 countsByYear W29222783162022 @default.
- W2922278316 countsByYear W29222783162023 @default.
- W2922278316 crossrefType "journal-article" @default.
- W2922278316 hasAuthorship W2922278316A5007179001 @default.
- W2922278316 hasAuthorship W2922278316A5019094519 @default.
- W2922278316 hasAuthorship W2922278316A5033988887 @default.
- W2922278316 hasAuthorship W2922278316A5044906378 @default.
- W2922278316 hasAuthorship W2922278316A5082450254 @default.
- W2922278316 hasConcept C104779481 @default.
- W2922278316 hasConcept C112950240 @default.
- W2922278316 hasConcept C159985019 @default.
- W2922278316 hasConcept C192562407 @default.
- W2922278316 hasConcept C193867417 @default.
- W2922278316 hasConcept C196029304 @default.
- W2922278316 hasConcept C2994609957 @default.
- W2922278316 hasConcept C519885992 @default.
- W2922278316 hasConceptScore W2922278316C104779481 @default.
- W2922278316 hasConceptScore W2922278316C112950240 @default.
- W2922278316 hasConceptScore W2922278316C159985019 @default.
- W2922278316 hasConceptScore W2922278316C192562407 @default.
- W2922278316 hasConceptScore W2922278316C193867417 @default.
- W2922278316 hasConceptScore W2922278316C196029304 @default.
- W2922278316 hasConceptScore W2922278316C2994609957 @default.
- W2922278316 hasConceptScore W2922278316C519885992 @default.
- W2922278316 hasFunder F4320334924 @default.
- W2922278316 hasLocation W29222783161 @default.
- W2922278316 hasOpenAccess W2922278316 @default.
- W2922278316 hasPrimaryLocation W29222783161 @default.
- W2922278316 hasRelatedWork W2005496670 @default.
- W2922278316 hasRelatedWork W2006232431 @default.
- W2922278316 hasRelatedWork W2089085266 @default.
- W2922278316 hasRelatedWork W2729932191 @default.
- W2922278316 hasRelatedWork W2794237881 @default.
- W2922278316 hasRelatedWork W2795554382 @default.
- W2922278316 hasRelatedWork W2922278316 @default.
- W2922278316 hasRelatedWork W3000513371 @default.
- W2922278316 hasRelatedWork W3095073354 @default.
- W2922278316 hasRelatedWork W4248473238 @default.
- W2922278316 hasVolume "27" @default.
- W2922278316 isParatext "false" @default.
- W2922278316 isRetracted "false" @default.
- W2922278316 magId "2922278316" @default.
- W2922278316 workType "article" @default.