• W2922832947 abstract "HBO2-II ceramics were prepared by cold sintering with 10wt% dehydrated ethanol as the transient liquid phase. When the processing temperature is 30°C, the relative density of the mechanically robust HBO2-II ceramics increases from 77.5% to 84.5% with increasing the uniaxial pressure from 200 to 500 MPa. It changes less than 0.2% for higher pressure up to 700 MPa. Under a constant uniaxial pressure of 500 MPa, the relative density further increases to 94.7% for the processing temperature of 120°C. HBO2-I is observed as the secondary phase when the processing temperature is 150°C. In comparison, the compacts prepared in the absence of ethanol are fragile, and the relative densities are 78.5%-84.5% for the processing temperatures of 30-120°C and uniaxial pressure of 500 MPa. It is indicated that ethanol promotes the densification significantly through the dissolution-precipitation mechanism. The permittivity increases with increasing the processing temperature, while the Qf value decreases. The optimal properties with the relative density of 94.7%, εr = 4.21, Qf = 47 500 GHz, and τf = −70.0 ppm/°C were obtained in the single-phase HBO2-II ceramics cold sintered at 120°C under 500 MPa for 10 minutes. The relative density and Qf value are significantly higher than those of the HBO2-II ceramic prepared by sintering the H3BO3 compact at 180°C for 2 hours (70.3% and 32 700 GHz, respectively). The results indicate that the nonaqueous solvent can also be used as the transient liquid phase for cold sintering, so that more materials that are unstable or insoluble in water can be densified by this method." @default.
• W2922832947 created "2019-04-01" @default.
• W2922832947 creator A5037739635 @default.
• W2922832947 creator A5044592466 @default.
• W2922832947 creator A5047398603 @default.
• W2922832947 creator A5077910059 @default.
• W2922832947 date "2019-04-09" @default.
• W2922832947 modified "2023-09-26" @default.
• W2922832947 title "Cold sintering and microwave dielectric properties of dense <scp>HBO</scp> ₂ ‐ <scp>II</scp> ceramics" @default.
• W2922832947 cites W1966578089 @default.
• W2922832947 cites W1982081303 @default.
• W2922832947 cites W1996634868 @default.
• W2922832947 cites W1997903922 @default.
• W2922832947 cites W2068432882 @default.
• W2922832947 cites W2082862052 @default.
• W2922832947 cites W2087041232 @default.
• W2922832947 cites W2087129056 @default.
• W2922832947 cites W2092334517 @default.
• W2922832947 cites W2112001192 @default.
• W2922832947 cites W2132189255 @default.
• W2922832947 cites W2160849410 @default.
• W2922832947 cites W2526551757 @default.
• W2922832947 cites W2530181669 @default.
• W2922832947 cites W2592993316 @default.
• W2922832947 cites W2600707125 @default.
• W2922832947 cites W2604852925 @default.
• W2922832947 cites W2737249608 @default.
• W2922832947 cites W2795276857 @default.
• W2922832947 cites W2803319515 @default.
• W2922832947 cites W2807365698 @default.
• W2922832947 cites W2877681099 @default.
• W2922832947 cites W2885389354 @default.
• W2922832947 cites W2886589403 @default.
• W2922832947 cites W2887427416 @default.
• W2922832947 cites W2889313595 @default.
• W2922832947 cites W2908383839 @default.
• W2922832947 cites W2910985133 @default.
• W2922832947 cites W2914157180 @default.
• W2922832947 doi "https://doi.org/10.1111/jace.16450" @default.
• W2922832947 hasPublicationYear "2019" @default.
• W2922832947 type Work @default.
• W2922832947 sameAs 2922832947 @default.
• W2922832947 citedByCount "21" @default.
• W2922832947 countsByYear W29228329472019 @default.
• W2922832947 countsByYear W29228329472020 @default.
• W2922832947 countsByYear W29228329472021 @default.
• W2922832947 countsByYear W29228329472022 @default.
• W2922832947 countsByYear W29228329472023 @default.
• W2922832947 crossrefType "journal-article" @default.
• W2922832947 hasAuthorship W2922832947A5037739635 @default.
• W2922832947 hasAuthorship W2922832947A5044592466 @default.
• W2922832947 hasAuthorship W2922832947A5047398603 @default.
• W2922832947 hasAuthorship W2922832947A5077910059 @default.
• W2922832947 hasConcept C107054158 @default.
• W2922832947 hasConcept C113196181 @default.
• W2922832947 hasConcept C121332964 @default.
• W2922832947 hasConcept C133386390 @default.
• W2922832947 hasConcept C134132462 @default.
• W2922832947 hasConcept C13760523 @default.
• W2922832947 hasConcept C147789679 @default.
• W2922832947 hasConcept C153294291 @default.
• W2922832947 hasConcept C159985019 @default.
• W2922832947 hasConcept C168651791 @default.
• W2922832947 hasConcept C178790620 @default.
• W2922832947 hasConcept C185592680 @default.
• W2922832947 hasConcept C192562407 @default.
• W2922832947 hasConcept C199289684 @default.
• W2922832947 hasConcept C2777581544 @default.
• W2922832947 hasConcept C43617362 @default.
• W2922832947 hasConcept C44280652 @default.
• W2922832947 hasConcept C49040817 @default.
• W2922832947 hasConcept C82455628 @default.
• W2922832947 hasConcept C88380143 @default.
• W2922832947 hasConceptScore W2922832947C107054158 @default.
• W2922832947 hasConceptScore W2922832947C113196181 @default.
• W2922832947 hasConceptScore W2922832947C121332964 @default.
• W2922832947 hasConceptScore W2922832947C133386390 @default.
• W2922832947 hasConceptScore W2922832947C134132462 @default.
• W2922832947 hasConceptScore W2922832947C13760523 @default.
• W2922832947 hasConceptScore W2922832947C147789679 @default.
• W2922832947 hasConceptScore W2922832947C153294291 @default.
• W2922832947 hasConceptScore W2922832947C159985019 @default.
• W2922832947 hasConceptScore W2922832947C168651791 @default.
• W2922832947 hasConceptScore W2922832947C178790620 @default.
• W2922832947 hasConceptScore W2922832947C185592680 @default.
• W2922832947 hasConceptScore W2922832947C192562407 @default.
• W2922832947 hasConceptScore W2922832947C199289684 @default.
• W2922832947 hasConceptScore W2922832947C2777581544 @default.
• W2922832947 hasConceptScore W2922832947C43617362 @default.
• W2922832947 hasConceptScore W2922832947C44280652 @default.
• W2922832947 hasConceptScore W2922832947C49040817 @default.
• W2922832947 hasConceptScore W2922832947C82455628 @default.
• W2922832947 hasConceptScore W2922832947C88380143 @default.
• W2922832947 hasFunder F4320338464 @default.
• W2922832947 hasIssue "10" @default.
• W2922832947 hasLocation W29228329471 @default.
• W2922832947 hasOpenAccess W2922832947 @default.
• W2922832947 hasPrimaryLocation W29228329471 @default.

• next