- W2936502079 abstract "The hybrid bonded magnet NdFeB - BaFe12O19 has been made. The composition of BaFe12O19 was varied as 0, 3, 5, 8, and 10 wt%. The preparation process was started by mixing BaFe12O19 powder with NdFeB (MQP-B+), then mixed with exopy resin binder of 8 wt% and subsequently compacted with a pressure of 60 MPa to form a pellet. The pellet samples were heated in 10 mmbar of vacuum dryer at 90°C for 1 hour. Some parameters were measured such as mechanical properties (compressive strength), magnetic properties (magnetic flux density and hysteresis curve) and corrosion resistance. The results show that the hybrid bonded magnet NdFeB with 10 wt% BaFe12O19 exhibits the highest compressive strength of about 268,15 kgf/cm2. While the optimum corrosion resistance of bonded magnet NdFeB - BaFe12O19 is obtained by 5 wt% BaFe12O19 addition. It has a flux magnetic density of 1340 Gauss, remanence Br of 3,827 kG and coercivity Hcj of 8,924 kOe. According to the corrosion test result, it is found that the sample with higher content of Ba-ferrite has a better corrosion resistance compare to the sample with small content of Ba-ferrite." @default.
- W2936502079 created "2019-04-25" @default.
- W2936502079 creator A5040133279 @default.
- W2936502079 creator A5043663463 @default.
- W2936502079 creator A5060199907 @default.
- W2936502079 creator A5077098432 @default.
- W2936502079 creator A5081418046 @default.
- W2936502079 date "2019-03-01" @default.
- W2936502079 modified "2023-10-14" @default.
- W2936502079 title "Mechanical, magnetic properties and corrosion resistance of hybrid bonded magnet NdFeB - BaFe<sub>12</sub>O<sub>19</sub>" @default.
- W2936502079 cites W1972152257 @default.
- W2936502079 cites W2028056269 @default.
- W2936502079 cites W2029984339 @default.
- W2936502079 cites W2048895669 @default.
- W2936502079 cites W2086390173 @default.
- W2936502079 cites W2125678830 @default.
- W2936502079 cites W2593811565 @default.
- W2936502079 cites W2782641131 @default.
- W2936502079 doi "https://doi.org/10.1088/1742-6596/1191/1/012048" @default.
- W2936502079 hasPublicationYear "2019" @default.
- W2936502079 type Work @default.
- W2936502079 sameAs 2936502079 @default.
- W2936502079 citedByCount "2" @default.
- W2936502079 countsByYear W29365020792021 @default.
- W2936502079 countsByYear W29365020792022 @default.
- W2936502079 crossrefType "journal-article" @default.
- W2936502079 hasAuthorship W2936502079A5040133279 @default.
- W2936502079 hasAuthorship W2936502079A5043663463 @default.
- W2936502079 hasAuthorship W2936502079A5060199907 @default.
- W2936502079 hasAuthorship W2936502079A5077098432 @default.
- W2936502079 hasAuthorship W2936502079A5081418046 @default.
- W2936502079 hasBestOaLocation W29365020791 @default.
- W2936502079 hasConcept C110135171 @default.
- W2936502079 hasConcept C115260700 @default.
- W2936502079 hasConcept C121332964 @default.
- W2936502079 hasConcept C126530901 @default.
- W2936502079 hasConcept C155058782 @default.
- W2936502079 hasConcept C159985019 @default.
- W2936502079 hasConcept C16389437 @default.
- W2936502079 hasConcept C191897082 @default.
- W2936502079 hasConcept C192562407 @default.
- W2936502079 hasConcept C20625102 @default.
- W2936502079 hasConcept C26873012 @default.
- W2936502079 hasConcept C32546565 @default.
- W2936502079 hasConcept C37210646 @default.
- W2936502079 hasConcept C62520636 @default.
- W2936502079 hasConceptScore W2936502079C110135171 @default.
- W2936502079 hasConceptScore W2936502079C115260700 @default.
- W2936502079 hasConceptScore W2936502079C121332964 @default.
- W2936502079 hasConceptScore W2936502079C126530901 @default.
- W2936502079 hasConceptScore W2936502079C155058782 @default.
- W2936502079 hasConceptScore W2936502079C159985019 @default.
- W2936502079 hasConceptScore W2936502079C16389437 @default.
- W2936502079 hasConceptScore W2936502079C191897082 @default.
- W2936502079 hasConceptScore W2936502079C192562407 @default.
- W2936502079 hasConceptScore W2936502079C20625102 @default.
- W2936502079 hasConceptScore W2936502079C26873012 @default.
- W2936502079 hasConceptScore W2936502079C32546565 @default.
- W2936502079 hasConceptScore W2936502079C37210646 @default.
- W2936502079 hasConceptScore W2936502079C62520636 @default.
- W2936502079 hasLocation W29365020791 @default.
- W2936502079 hasOpenAccess W2936502079 @default.
- W2936502079 hasPrimaryLocation W29365020791 @default.
- W2936502079 hasRelatedWork W2091154086 @default.
- W2936502079 hasRelatedWork W2093607618 @default.
- W2936502079 hasRelatedWork W2107706768 @default.
- W2936502079 hasRelatedWork W2154382674 @default.
- W2936502079 hasRelatedWork W2155120406 @default.
- W2936502079 hasRelatedWork W2369332722 @default.
- W2936502079 hasRelatedWork W2375390555 @default.
- W2936502079 hasRelatedWork W3106412289 @default.
- W2936502079 hasRelatedWork W4249989416 @default.
- W2936502079 hasRelatedWork W4386574080 @default.
- W2936502079 hasVolume "1191" @default.
- W2936502079 isParatext "false" @default.
- W2936502079 isRetracted "false" @default.
- W2936502079 magId "2936502079" @default.
- W2936502079 workType "article" @default.