• W2936983876 endingPage "239" @default.
• W2936983876 startingPage "233" @default.
• W2936983876 abstract "Four kinds of well-crystallized tritium permeation barrier coatings, including γ-Al2O3, α-Al2O3, γ-Al2O3/Cr2O3 and α-Al2O3/Cr2O3, were prepared by the metal organic decomposition (MOD) method using a dipping technique. In this study, we concentrated on the preparation and properties of α-Al2O3 and α-Al2O3/Cr2O3 double-layer coatings. The results showed that the α-Al2O3 coating exhibited a pure phase structure, which was entirely and directly transformed from the γ-Al2O3 at an annealing temperature of 1000 °C, and no obvious substrate oxides were formed. An unannealed Cr2O3 MOD layer with a thickness of 0.8 μm featured higher crystallization and was taken as a buffer layer. However, the template effect of Cr2O3 was not obvious because the formation temperature of the α-Al2O3 did not decrease. The corrosion resistance (1.068 × 10−7 A/cm2) and nanohardness (18.49 GPa) of the α-Al2O3/Cr2O3 double-layer coating improved compared to those of γ-Al2O3, α-Al2O3, and γ-Al2O3/Cr2O3 coatings. In contrast, the deuterium permeation test showed that the α-Al2O3 MOD coating had the lowest deuterium ion current at temperatures of 400 ˜ 600 °C of the films considered in this study, demonstrating better resistance to deuterium permeation. Relevant mechanisms and explanations are discussed in detail." @default.
• W2936983876 created "2019-04-25" @default.
• W2936983876 creator A5002569640 @default.
• W2936983876 creator A5021559836 @default.
• W2936983876 creator A5021871203 @default.
• W2936983876 creator A5024792434 @default.
• W2936983876 creator A5037004694 @default.
• W2936983876 creator A5038895885 @default.
• W2936983876 creator A5039441081 @default.
• W2936983876 creator A5039965047 @default.
• W2936983876 creator A5053252415 @default.
• W2936983876 creator A5084589573 @default.
• W2936983876 date "2019-06-01" @default.
• W2936983876 modified "2023-10-05" @default.
• W2936983876 title "Preparation and properties of improved Al2O3 based MOD coatings as tritium permeation barrier" @default.
• W2936983876 cites W122342963 @default.
• W2936983876 cites W1495406873 @default.
• W2936983876 cites W1584205316 @default.
• W2936983876 cites W1765594 @default.
• W2936983876 cites W1967906550 @default.
• W2936983876 cites W196811843 @default.
• W2936983876 cites W1986983573 @default.
• W2936983876 cites W1991332762 @default.
• W2936983876 cites W1995174553 @default.
• W2936983876 cites W2006397183 @default.
• W2936983876 cites W2012536999 @default.
• W2936983876 cites W2020432211 @default.
• W2936983876 cites W2038855252 @default.
• W2936983876 cites W2057181819 @default.
• W2936983876 cites W2059731494 @default.
• W2936983876 cites W2061115161 @default.
• W2936983876 cites W2069020039 @default.
• W2936983876 cites W2077248656 @default.
• W2936983876 cites W2077727161 @default.
• W2936983876 cites W2080318934 @default.
• W2936983876 cites W2092983031 @default.
• W2936983876 cites W2109424358 @default.
• W2936983876 cites W213805719 @default.
• W2936983876 cites W2156766566 @default.
• W2936983876 cites W2217750243 @default.
• W2936983876 cites W2586727228 @default.
• W2936983876 cites W2604857282 @default.
• W2936983876 cites W2607555820 @default.
• W2936983876 cites W2791160414 @default.
• W2936983876 cites W2793944320 @default.
• W2936983876 cites W4231394324 @default.
• W2936983876 doi "https://doi.org/10.1016/j.fusengdes.2019.04.012" @default.
• W2936983876 hasPublicationYear "2019" @default.
• W2936983876 type Work @default.
• W2936983876 sameAs 2936983876 @default.
• W2936983876 citedByCount "20" @default.
• W2936983876 countsByYear W29369838762019 @default.
• W2936983876 countsByYear W29369838762020 @default.
• W2936983876 countsByYear W29369838762021 @default.
• W2936983876 countsByYear W29369838762022 @default.
• W2936983876 countsByYear W29369838762023 @default.
• W2936983876 crossrefType "journal-article" @default.
• W2936983876 hasAuthorship W2936983876A5002569640 @default.
• W2936983876 hasAuthorship W2936983876A5021559836 @default.
• W2936983876 hasAuthorship W2936983876A5021871203 @default.
• W2936983876 hasAuthorship W2936983876A5024792434 @default.
• W2936983876 hasAuthorship W2936983876A5037004694 @default.
• W2936983876 hasAuthorship W2936983876A5038895885 @default.
• W2936983876 hasAuthorship W2936983876A5039441081 @default.
• W2936983876 hasAuthorship W2936983876A5039965047 @default.
• W2936983876 hasAuthorship W2936983876A5053252415 @default.
• W2936983876 hasAuthorship W2936983876A5084589573 @default.
• W2936983876 hasConcept C121332964 @default.
• W2936983876 hasConcept C127413603 @default.
• W2936983876 hasConcept C154945302 @default.
• W2936983876 hasConcept C159985019 @default.
• W2936983876 hasConcept C185544564 @default.
• W2936983876 hasConcept C185592680 @default.
• W2936983876 hasConcept C192562407 @default.
• W2936983876 hasConcept C203036418 @default.
• W2936983876 hasConcept C20625102 @default.
• W2936983876 hasConcept C2777855556 @default.
• W2936983876 hasConcept C2779227376 @default.
• W2936983876 hasConcept C2781448156 @default.
• W2936983876 hasConcept C29231244 @default.
• W2936983876 hasConcept C41008148 @default.
• W2936983876 hasConcept C41625074 @default.
• W2936983876 hasConcept C42360764 @default.
• W2936983876 hasConcept C50670333 @default.
• W2936983876 hasConcept C55493867 @default.
• W2936983876 hasConcept C58364064 @default.
• W2936983876 hasConcept C62520636 @default.
• W2936983876 hasConcept C62538594 @default.
• W2936983876 hasConceptScore W2936983876C121332964 @default.
• W2936983876 hasConceptScore W2936983876C127413603 @default.
• W2936983876 hasConceptScore W2936983876C154945302 @default.
• W2936983876 hasConceptScore W2936983876C159985019 @default.
• W2936983876 hasConceptScore W2936983876C185544564 @default.
• W2936983876 hasConceptScore W2936983876C185592680 @default.
• W2936983876 hasConceptScore W2936983876C192562407 @default.
• W2936983876 hasConceptScore W2936983876C203036418 @default.
• W2936983876 hasConceptScore W2936983876C20625102 @default.
• W2936983876 hasConceptScore W2936983876C2777855556 @default.

• next