- W2939044091 abstract "The nature of an anodic oxide film formed on Mg alloys is porous and cleaved. Sealing of the pores is necessary to enhance the corrosion resistance of the alloys. This work reports the effect of beeswax-colophony sealant on the corrosion resistance of anodic oxide layer formed on AZ31 magnesium (Mg) alloy. Anodization was conducted in 0.5 M Na3PO4 solution at 30°C at a constant voltage 5 V with variation time 10, 20, and 30 min. The resulting anodic film exhibited thicknesses of 6.3, 14.8, and 16.7 µm for 10, 20, and 30 min anodization time, respectively. The film was presumably composed of Mg(OH)2 and Mg3(PO4)2 as predicted by EDX analysis. Sealing was done by dipping the specimen in a mixture of beeswax-colophony with ratio 7:1. The corrosion test was performed by weight loss method in 0.9% NaCl solution at 37°C for 14 days. The unsealed and sealed specimens exhibited a similar increase in weight loss with increasing exposure time. However, the sealed specimens showed remarkably lower material loss below 3.8 mg/cm2 relative to the unsealed specimens with weight loss up to 11.5 mg/cm2. The corrosion rate of the sealed specimens was five times lower than the unsealed ones." @default.
- W2939044091 created "2019-04-25" @default.
- W2939044091 creator A5035184348 @default.
- W2939044091 creator A5055616276 @default.
- W2939044091 date "2019-03-01" @default.
- W2939044091 modified "2023-09-27" @default.
- W2939044091 title "Remarkable improvement in corrosion resistance of anodized AZ31 alloy by sealing with beeswax-colophony resin" @default.
- W2939044091 cites W1975649027 @default.
- W2939044091 cites W1988791764 @default.
- W2939044091 cites W2020240221 @default.
- W2939044091 cites W2040235837 @default.
- W2939044091 cites W2065213455 @default.
- W2939044091 cites W2083429353 @default.
- W2939044091 cites W2501791992 @default.
- W2939044091 cites W2565839987 @default.
- W2939044091 cites W4241920571 @default.
- W2939044091 cites W1936857424 @default.
- W2939044091 doi "https://doi.org/10.1088/1742-6596/1191/1/012032" @default.
- W2939044091 hasPublicationYear "2019" @default.
- W2939044091 type Work @default.
- W2939044091 sameAs 2939044091 @default.
- W2939044091 citedByCount "3" @default.
- W2939044091 countsByYear W29390440912020 @default.
- W2939044091 countsByYear W29390440912021 @default.
- W2939044091 countsByYear W29390440912022 @default.
- W2939044091 crossrefType "journal-article" @default.
- W2939044091 hasAuthorship W2939044091A5035184348 @default.
- W2939044091 hasAuthorship W2939044091A5055616276 @default.
- W2939044091 hasBestOaLocation W29390440911 @default.
- W2939044091 hasConcept C147789679 @default.
- W2939044091 hasConcept C153033020 @default.
- W2939044091 hasConcept C159985019 @default.
- W2939044091 hasConcept C17525397 @default.
- W2939044091 hasConcept C185592680 @default.
- W2939044091 hasConcept C191897082 @default.
- W2939044091 hasConcept C192562407 @default.
- W2939044091 hasConcept C20625102 @default.
- W2939044091 hasConcept C22016385 @default.
- W2939044091 hasConcept C2776793449 @default.
- W2939044091 hasConcept C2779851234 @default.
- W2939044091 hasConcept C2780026712 @default.
- W2939044091 hasConcept C513153333 @default.
- W2939044091 hasConcept C543218039 @default.
- W2939044091 hasConcept C89395315 @default.
- W2939044091 hasConceptScore W2939044091C147789679 @default.
- W2939044091 hasConceptScore W2939044091C153033020 @default.
- W2939044091 hasConceptScore W2939044091C159985019 @default.
- W2939044091 hasConceptScore W2939044091C17525397 @default.
- W2939044091 hasConceptScore W2939044091C185592680 @default.
- W2939044091 hasConceptScore W2939044091C191897082 @default.
- W2939044091 hasConceptScore W2939044091C192562407 @default.
- W2939044091 hasConceptScore W2939044091C20625102 @default.
- W2939044091 hasConceptScore W2939044091C22016385 @default.
- W2939044091 hasConceptScore W2939044091C2776793449 @default.
- W2939044091 hasConceptScore W2939044091C2779851234 @default.
- W2939044091 hasConceptScore W2939044091C2780026712 @default.
- W2939044091 hasConceptScore W2939044091C513153333 @default.
- W2939044091 hasConceptScore W2939044091C543218039 @default.
- W2939044091 hasConceptScore W2939044091C89395315 @default.
- W2939044091 hasLocation W29390440911 @default.
- W2939044091 hasOpenAccess W2939044091 @default.
- W2939044091 hasPrimaryLocation W29390440911 @default.
- W2939044091 hasRelatedWork W13377028 @default.
- W2939044091 hasRelatedWork W19793484 @default.
- W2939044091 hasRelatedWork W24815076 @default.
- W2939044091 hasRelatedWork W27973393 @default.
- W2939044091 hasRelatedWork W36583241 @default.
- W2939044091 hasRelatedWork W38976464 @default.
- W2939044091 hasRelatedWork W39811153 @default.
- W2939044091 hasRelatedWork W49655644 @default.
- W2939044091 hasRelatedWork W5073005 @default.
- W2939044091 hasRelatedWork W21433334 @default.
- W2939044091 isParatext "false" @default.
- W2939044091 isRetracted "false" @default.
- W2939044091 magId "2939044091" @default.
- W2939044091 workType "article" @default.