• W2939779102 abstract "Previous 3D printers developed for the fabrication of ceramic cores have been limited to implement mechanical properties and provide shapes that meet the requirements, since the type and size of powder, and the type of binder are standardized according to the printer. Therefore, in this study, the composition and manufacturing process of ceramic powder and binder were studied to fabricate ceramic cores with high mechanical properties without depending on the type of 3D printer. Fine mullite powder (average particle size: 16 μm) and zircon flour (average particle size: 43 μm) with conventional mullite bead. In addition, two types of polyvinyl alcohol (PVA) were used to enhance the coating ratio of an inorganic binder. Green bodies were formed by a three-dimensional (3D) printer employing three kinds of starting powders and PVAs mixed at the proper ratio. The green bodies were then heat-treated at 250 °C to evaporate the PVA with a lower boiling point. Then, the heat-treated core samples were dipped into the inorganic precursor, dried, and heat-treated at 1000 °C for the organic–inorganic conversion process. Through using a combination of different starting powders, the compact density of the sample was increased and the pore size was reduced, resulting in an increase in the coating efficiency of the inorganic binder. This study demonstrates the feasibility of the fabrication of a ceramic core with excellent strength through the 3D-printing process." @default.
• W2939779102 created "2019-04-25" @default.
• W2939779102 creator A5017947172 @default.
• W2939779102 creator A5019037415 @default.
• W2939779102 creator A5032813280 @default.
• W2939779102 creator A5065883237 @default.
• W2939779102 creator A5066312250 @default.
• W2939779102 date "2019-06-01" @default.
• W2939779102 modified "2023-09-26" @default.
• W2939779102 title "Process development of fabricating ceramic core using 3D printing technique" @default.
• W2939779102 cites W1982008918 @default.
• W2939779102 cites W1996555126 @default.
• W2939779102 cites W2010752427 @default.
• W2939779102 cites W2045834052 @default.
• W2939779102 cites W2059713872 @default.
• W2939779102 cites W2062489307 @default.
• W2939779102 cites W2065376024 @default.
• W2939779102 cites W2075550508 @default.
• W2939779102 cites W2087635529 @default.
• W2939779102 cites W2094168531 @default.
• W2939779102 cites W2133390202 @default.
• W2939779102 cites W2192136807 @default.
• W2939779102 cites W2574009636 @default.
• W2939779102 cites W2736719679 @default.
• W2939779102 cites W2769522696 @default.
• W2939779102 cites W2803731308 @default.
• W2939779102 cites W2884581299 @default.
• W2939779102 cites W2904147459 @default.
• W2939779102 cites W2908925506 @default.
• W2939779102 cites W4248180894 @default.
• W2939779102 doi "https://doi.org/10.1016/j.matchemphys.2019.04.039" @default.
• W2939779102 hasPublicationYear "2019" @default.
• W2939779102 type Work @default.
• W2939779102 sameAs 2939779102 @default.
• W2939779102 citedByCount "16" @default.
• W2939779102 countsByYear W29397791022020 @default.
• W2939779102 countsByYear W29397791022021 @default.
• W2939779102 countsByYear W29397791022022 @default.
• W2939779102 countsByYear W29397791022023 @default.
• W2939779102 crossrefType "journal-article" @default.
• W2939779102 hasAuthorship W2939779102A5017947172 @default.
• W2939779102 hasAuthorship W2939779102A5019037415 @default.
• W2939779102 hasAuthorship W2939779102A5032813280 @default.
• W2939779102 hasAuthorship W2939779102A5065883237 @default.
• W2939779102 hasAuthorship W2939779102A5066312250 @default.
• W2939779102 hasConcept C111368507 @default.
• W2939779102 hasConcept C127313418 @default.
• W2939779102 hasConcept C127413603 @default.
• W2939779102 hasConcept C134132462 @default.
• W2939779102 hasConcept C136525101 @default.
• W2939779102 hasConcept C142724271 @default.
• W2939779102 hasConcept C159985019 @default.
• W2939779102 hasConcept C178790620 @default.
• W2939779102 hasConcept C185592680 @default.
• W2939779102 hasConcept C187530423 @default.
• W2939779102 hasConcept C192562407 @default.
• W2939779102 hasConcept C204787440 @default.
• W2939779102 hasConcept C206139338 @default.
• W2939779102 hasConcept C2164484 @default.
• W2939779102 hasConcept C2778517922 @default.
• W2939779102 hasConcept C2778551929 @default.
• W2939779102 hasConcept C2781007617 @default.
• W2939779102 hasConcept C2781436864 @default.
• W2939779102 hasConcept C2781448156 @default.
• W2939779102 hasConcept C42360764 @default.
• W2939779102 hasConcept C524769229 @default.
• W2939779102 hasConcept C71924100 @default.
• W2939779102 hasConceptScore W2939779102C111368507 @default.
• W2939779102 hasConceptScore W2939779102C127313418 @default.
• W2939779102 hasConceptScore W2939779102C127413603 @default.
• W2939779102 hasConceptScore W2939779102C134132462 @default.
• W2939779102 hasConceptScore W2939779102C136525101 @default.
• W2939779102 hasConceptScore W2939779102C142724271 @default.
• W2939779102 hasConceptScore W2939779102C159985019 @default.
• W2939779102 hasConceptScore W2939779102C178790620 @default.
• W2939779102 hasConceptScore W2939779102C185592680 @default.
• W2939779102 hasConceptScore W2939779102C187530423 @default.
• W2939779102 hasConceptScore W2939779102C192562407 @default.
• W2939779102 hasConceptScore W2939779102C204787440 @default.
• W2939779102 hasConceptScore W2939779102C206139338 @default.
• W2939779102 hasConceptScore W2939779102C2164484 @default.
• W2939779102 hasConceptScore W2939779102C2778517922 @default.
• W2939779102 hasConceptScore W2939779102C2778551929 @default.
• W2939779102 hasConceptScore W2939779102C2781007617 @default.
• W2939779102 hasConceptScore W2939779102C2781436864 @default.
• W2939779102 hasConceptScore W2939779102C2781448156 @default.
• W2939779102 hasConceptScore W2939779102C42360764 @default.
• W2939779102 hasConceptScore W2939779102C524769229 @default.
• W2939779102 hasConceptScore W2939779102C71924100 @default.
• W2939779102 hasFunder F4320322120 @default.
• W2939779102 hasFunder F4320335199 @default.
• W2939779102 hasLocation W29397791021 @default.
• W2939779102 hasOpenAccess W2939779102 @default.
• W2939779102 hasPrimaryLocation W29397791021 @default.
• W2939779102 hasRelatedWork W1976855640 @default.
• W2939779102 hasRelatedWork W1992399540 @default.
• W2939779102 hasRelatedWork W2000721444 @default.
• W2939779102 hasRelatedWork W2001255670 @default.

• next