- W2945393987 abstract "In this work, we investigated the oxide reliability of 4H-SiC (0001) MOS capacitors, the oxide was fabricated about 60 nm by thermal oxidation temperature at 1350°C, the oxides than annealed at different temperatures and times in diluted NO (10% in N 2 ). The 4H-SiC MOS structure was analyzed by C-V and I-V measurement. Compared the J-E curves and Weibull distribution curves of charge-to-breakdown for fives samples under different annealing temperature and time, it shows that the high annealing temperature improves the electrical properties as the lifetime enhanced. The mode value of field-to-breakdown (E BD ) for thermal oxides by post-oxide-annealing in NO for 30 min at 1350°C was 10.09 MV/cm, the charge-to-breakdown (Q BD ) of this sample was the highest in all samples, and the Q BD value at 63.2% cumulative failure rate was 0.15 C/cm 2 . The Q BD of the sample annealing at 1200°C for 120 min was 0.06 C/ cm 2 . The effects of NO annealing in high temperature enhance the lifetime of electrical properties and field-to-breakdown obviously. It can be demonstrated that the annealing temperature as high as 1300°C for 30 min can be used to accelerate TDDB of SiC MOS gate oxide." @default.
- W2945393987 created "2019-05-29" @default.
- W2945393987 creator A5021653526 @default.
- W2945393987 creator A5049965337 @default.
- W2945393987 creator A5078670644 @default.
- W2945393987 date "2019-05-01" @default.
- W2945393987 modified "2023-10-17" @default.
- W2945393987 title "Reliability of 4H-SiC (0001) MOS Gate Oxide by NO Post-Oxide-Annealing" @default.
- W2945393987 cites W1537270999 @default.
- W2945393987 cites W1559027090 @default.
- W2945393987 cites W1969544474 @default.
- W2945393987 cites W2000877898 @default.
- W2945393987 cites W2004451215 @default.
- W2945393987 cites W2021772071 @default.
- W2945393987 cites W2092874501 @default.
- W2945393987 cites W2149697246 @default.
- W2945393987 doi "https://doi.org/10.4028/www.scientific.net/msf.954.109" @default.
- W2945393987 hasPublicationYear "2019" @default.
- W2945393987 type Work @default.
- W2945393987 sameAs 2945393987 @default.
- W2945393987 citedByCount "4" @default.
- W2945393987 countsByYear W29453939872021 @default.
- W2945393987 countsByYear W29453939872023 @default.
- W2945393987 crossrefType "journal-article" @default.
- W2945393987 hasAuthorship W2945393987A5021653526 @default.
- W2945393987 hasAuthorship W2945393987A5049965337 @default.
- W2945393987 hasAuthorship W2945393987A5078670644 @default.
- W2945393987 hasConcept C105795698 @default.
- W2945393987 hasConcept C113196181 @default.
- W2945393987 hasConcept C119599485 @default.
- W2945393987 hasConcept C127413603 @default.
- W2945393987 hasConcept C152909973 @default.
- W2945393987 hasConcept C159985019 @default.
- W2945393987 hasConcept C165801399 @default.
- W2945393987 hasConcept C172385210 @default.
- W2945393987 hasConcept C173291955 @default.
- W2945393987 hasConcept C185592680 @default.
- W2945393987 hasConcept C191897082 @default.
- W2945393987 hasConcept C192562407 @default.
- W2945393987 hasConcept C2361726 @default.
- W2945393987 hasConcept C2777855556 @default.
- W2945393987 hasConcept C2779851234 @default.
- W2945393987 hasConcept C33923547 @default.
- W2945393987 hasConcept C43617362 @default.
- W2945393987 hasConceptScore W2945393987C105795698 @default.
- W2945393987 hasConceptScore W2945393987C113196181 @default.
- W2945393987 hasConceptScore W2945393987C119599485 @default.
- W2945393987 hasConceptScore W2945393987C127413603 @default.
- W2945393987 hasConceptScore W2945393987C152909973 @default.
- W2945393987 hasConceptScore W2945393987C159985019 @default.
- W2945393987 hasConceptScore W2945393987C165801399 @default.
- W2945393987 hasConceptScore W2945393987C172385210 @default.
- W2945393987 hasConceptScore W2945393987C173291955 @default.
- W2945393987 hasConceptScore W2945393987C185592680 @default.
- W2945393987 hasConceptScore W2945393987C191897082 @default.
- W2945393987 hasConceptScore W2945393987C192562407 @default.
- W2945393987 hasConceptScore W2945393987C2361726 @default.
- W2945393987 hasConceptScore W2945393987C2777855556 @default.
- W2945393987 hasConceptScore W2945393987C2779851234 @default.
- W2945393987 hasConceptScore W2945393987C33923547 @default.
- W2945393987 hasConceptScore W2945393987C43617362 @default.
- W2945393987 hasLocation W29453939871 @default.
- W2945393987 hasOpenAccess W2945393987 @default.
- W2945393987 hasPrimaryLocation W29453939871 @default.
- W2945393987 hasRelatedWork W2077805257 @default.
- W2945393987 hasRelatedWork W2099624314 @default.
- W2945393987 hasRelatedWork W2106473374 @default.
- W2945393987 hasRelatedWork W2539595190 @default.
- W2945393987 hasRelatedWork W2761090787 @default.
- W2945393987 hasRelatedWork W3038423925 @default.
- W2945393987 hasRelatedWork W3160961382 @default.
- W2945393987 hasRelatedWork W4220813443 @default.
- W2945393987 hasRelatedWork W4229016249 @default.
- W2945393987 hasRelatedWork W2150292786 @default.
- W2945393987 hasVolume "954" @default.
- W2945393987 isParatext "false" @default.
- W2945393987 isRetracted "false" @default.
- W2945393987 magId "2945393987" @default.
- W2945393987 workType "article" @default.