• W2945646225 abstract "R.F. sputtering was used to deposit thin films of YBCO onto a variety of substrates. The films were found to be superconducting with critical temperatures in excess of 77 Kelvin. Using x-ray diffraction the orientation of the YBCO thin films on MgO(lOO) was found to be c-axis. The films deposited on SrTiO3(100) were found to be a and c axis orientated, where as on SrTiO3(110) the thin films were (110/013) orientated. Using scanning electron microscopy the films were found to be granular in nature. The films deposited on MgO(lOO) had circular grains. The films deposited on SrTiO3(110) had elongated sausage like grains. The shape of the grains is due to spiral and ridge type growth respectively. Electrical measurements were taken using a 4 probe contact technique. The rf experiments were used to calculate the paraconductivity. The coherence length and superconducting sheet thickness where calculated for c-axis YBCO thin films using the Lawrence-Doniach theory. The coherence length was found to be 4 A, the sheet thickness was 11 A for T=0 Kelvin. Examination of the transition region revealed a flux flow region in films deposited on MgO(lOO). The temperature dependence of the flux flow region was found to be in agreement with that predicted by Kosterlitz-Thouless and independently by Berezinskii. This implies that the films were 2 dimensional in nature. Some films deposited on SrTiO3(110) do not appear to have a flux flow region. Films deposited on SrTiO3(110) may be 3 dimensional. Examination of the magnetic properties were in agreement with existing theory, namely that the resistance was directly proportional to the applied magnetic field. In order to perform critical current measurements the films were wet etched into strips. The temperature dependence of the critical current of the granular thin films was found to be in agreement with Ambegaokar-Baratoff theory for a 2 dimensional film of Josephson junctions. An ac electrical technique was used to investigate the reactive properties of YBCO thin films. Results show that the normal inductance was very anisotropic. The inductance for temperature below Tc was used to calculate the penetration depth. The penetration depth, for T=0K, was found to be between 2.24-10.58[xm. Penetration depths of this magnitude are predicted by Ambegaokar-Baratoff for certain cases. The temperature dependence of the penetration depth was investigated in terms of the London theory and good agreement was found. Anomalous behaviour was found to occur in certain thin films. The anomaly was present as a change in the temperature dependence of the kinetic inductance. The anomaly may be due to 2D-3D crossover, known to occur in YBCO thin films. An anomalous resonance effect was observed in very thin film at 48 Kelvin. The behaviour of the anomaly is very similar to a dielectric but may be due to substrate effect." @default.
• W2945646225 created "2019-05-29" @default.
• W2945646225 creator A5078978548 @default.
• W2945646225 date "1994-01-01" @default.
• W2945646225 modified "2023-09-24" @default.
• W2945646225 title "Low frequency impedance and structural properties of high temperature superconducting YBa2Cu3Ox thin films" @default.
• W2945646225 hasPublicationYear "1994" @default.
• W2945646225 type Work @default.
• W2945646225 sameAs 2945646225 @default.
• W2945646225 citedByCount "0" @default.
• W2945646225 crossrefType "dissertation" @default.
• W2945646225 hasAuthorship W2945646225A5078978548 @default.
• W2945646225 hasConcept C113196181 @default.
• W2945646225 hasConcept C115961682 @default.
• W2945646225 hasConcept C121332964 @default.
• W2945646225 hasConcept C154945302 @default.
• W2945646225 hasConcept C159985019 @default.
• W2945646225 hasConcept C168553754 @default.
• W2945646225 hasConcept C171250308 @default.
• W2945646225 hasConcept C185592680 @default.
• W2945646225 hasConcept C19067145 @default.
• W2945646225 hasConcept C192562407 @default.
• W2945646225 hasConcept C26771246 @default.
• W2945646225 hasConcept C26873012 @default.
• W2945646225 hasConcept C2781195486 @default.
• W2945646225 hasConcept C41008148 @default.
• W2945646225 hasConcept C43617362 @default.
• W2945646225 hasConcept C54101563 @default.
• W2945646225 hasConceptScore W2945646225C113196181 @default.
• W2945646225 hasConceptScore W2945646225C115961682 @default.
• W2945646225 hasConceptScore W2945646225C121332964 @default.
• W2945646225 hasConceptScore W2945646225C154945302 @default.
• W2945646225 hasConceptScore W2945646225C159985019 @default.
• W2945646225 hasConceptScore W2945646225C168553754 @default.
• W2945646225 hasConceptScore W2945646225C171250308 @default.
• W2945646225 hasConceptScore W2945646225C185592680 @default.
• W2945646225 hasConceptScore W2945646225C19067145 @default.
• W2945646225 hasConceptScore W2945646225C192562407 @default.
• W2945646225 hasConceptScore W2945646225C26771246 @default.
• W2945646225 hasConceptScore W2945646225C26873012 @default.
• W2945646225 hasConceptScore W2945646225C2781195486 @default.
• W2945646225 hasConceptScore W2945646225C41008148 @default.
• W2945646225 hasConceptScore W2945646225C43617362 @default.
• W2945646225 hasConceptScore W2945646225C54101563 @default.
• W2945646225 hasLocation W29456462251 @default.
• W2945646225 hasOpenAccess W2945646225 @default.
• W2945646225 hasPrimaryLocation W29456462251 @default.
• W2945646225 hasRelatedWork W1983853686 @default.
• W2945646225 hasRelatedWork W1997136974 @default.
• W2945646225 hasRelatedWork W1997172342 @default.
• W2945646225 hasRelatedWork W2018307724 @default.
• W2945646225 hasRelatedWork W2018365980 @default.
• W2945646225 hasRelatedWork W2020738512 @default.
• W2945646225 hasRelatedWork W2040299525 @default.
• W2945646225 hasRelatedWork W2049885551 @default.
• W2945646225 hasRelatedWork W2057312829 @default.
• W2945646225 hasRelatedWork W2059242029 @default.
• W2945646225 hasRelatedWork W2060681495 @default.
• W2945646225 hasRelatedWork W2314451935 @default.
• W2945646225 hasRelatedWork W2477343870 @default.
• W2945646225 hasRelatedWork W2498586040 @default.
• W2945646225 hasRelatedWork W2602768653 @default.
• W2945646225 hasRelatedWork W3081789741 @default.
• W2945646225 hasRelatedWork W3163508035 @default.
• W2945646225 hasRelatedWork W3176800141 @default.
• W2945646225 hasRelatedWork W85837368 @default.
• W2945646225 isParatext "false" @default.
• W2945646225 isRetracted "false" @default.
• W2945646225 magId "2945646225" @default.
• W2945646225 workType "dissertation" @default.