- W2954342236 abstract "A drill collar with material of 0Cr20Mn21Ni2N serviced in a coastal continental shelf oilfield, has cracked and leaked after a short period of working. Failure analysis of drill collar was performed by a series of experiments, including Chemical analysis, Fractographic analysis, Microstructural analysis, Intergranular attack test, Mechanical property, Residual stress test, EBSD analysis of relationship between crack propagation and crystal orientation. The fractographic observations showed crack initiated from the inner surface and extended to outer surface by the mode of inter-granular and quasi-cleavage trans-granular fracture, many branch cracks were produced during its propagation. Serious corrosion morphology was found both on the inner surface of drill collar and fracture surface, and S and Cl were detected in the corrosion products. The above evidence indicates that the cracking failure mode of drill collar can be described as the Stress Corrosion Cracking (SCC) of austenitic stainless steel. The causes of stress corrosion cracks are attributed to three aspects. Firstly, the microstructures of the materials are sensitized seriously, and there are many precipitated phases at grain boundaries, which result in chromium depletion in the grain boundaries and decrease of corrosion resistance of the materials. Secondly, during service the mud water on the inner surface of drill collar is composed of seawater containing chloride and sulfate radical, which provides corrosive environment for materials. Thirdly, the residual tensile stress on the inner surface of the drill collar reaches 112 MPa, which hinders the formation of passive film on the surface of stainless steel and has adverse effect on the corrosion resistance of the material. In addition, the mechanism of crack formation was studied by EBSD. Corrosion pits of inner-surface of drill collar is intergranular corrosion, which first occurs at random grain boundaries with high misorientation angles, rather than at special grain boundaries such as Σ3. SCC crack initiates from the corrosive pit and propagate along the grain boundary first and gradually transit to transgranular growth with Zigzag fracture morphology along {111}〈110〉 slip system, which proves SCC transgranular crack propagation obeys the slip corrosion mechanism." @default.
- W2954342236 created "2019-07-12" @default.
- W2954342236 creator A5007285539 @default.
- W2954342236 creator A5035827314 @default.
- W2954342236 creator A5079782216 @default.
- W2954342236 creator A5083940130 @default.
- W2954342236 creator A5089606871 @default.
- W2954342236 date "2019-11-01" @default.
- W2954342236 modified "2023-10-18" @default.
- W2954342236 title "Cause analysis and mechanism study of cracks in drilling collars" @default.
- W2954342236 cites W1996734095 @default.
- W2954342236 cites W2000120753 @default.
- W2954342236 cites W2089453061 @default.
- W2954342236 doi "https://doi.org/10.1016/j.engfailanal.2019.07.017" @default.
- W2954342236 hasPublicationYear "2019" @default.
- W2954342236 type Work @default.
- W2954342236 sameAs 2954342236 @default.
- W2954342236 citedByCount "5" @default.
- W2954342236 countsByYear W29543422362020 @default.
- W2954342236 countsByYear W29543422362021 @default.
- W2954342236 countsByYear W29543422362022 @default.
- W2954342236 crossrefType "journal-article" @default.
- W2954342236 hasAuthorship W2954342236A5007285539 @default.
- W2954342236 hasAuthorship W2954342236A5035827314 @default.
- W2954342236 hasAuthorship W2954342236A5079782216 @default.
- W2954342236 hasAuthorship W2954342236A5083940130 @default.
- W2954342236 hasAuthorship W2954342236A5089606871 @default.
- W2954342236 hasConcept C127413603 @default.
- W2954342236 hasConcept C159985019 @default.
- W2954342236 hasConcept C173736775 @default.
- W2954342236 hasConcept C184102282 @default.
- W2954342236 hasConcept C191897082 @default.
- W2954342236 hasConcept C192562407 @default.
- W2954342236 hasConcept C20625102 @default.
- W2954342236 hasConcept C2776088076 @default.
- W2954342236 hasConcept C2778760603 @default.
- W2954342236 hasConcept C2779229422 @default.
- W2954342236 hasConcept C27805521 @default.
- W2954342236 hasConcept C2781448223 @default.
- W2954342236 hasConcept C47908070 @default.
- W2954342236 hasConcept C58396970 @default.
- W2954342236 hasConcept C66938386 @default.
- W2954342236 hasConcept C87976508 @default.
- W2954342236 hasConceptScore W2954342236C127413603 @default.
- W2954342236 hasConceptScore W2954342236C159985019 @default.
- W2954342236 hasConceptScore W2954342236C173736775 @default.
- W2954342236 hasConceptScore W2954342236C184102282 @default.
- W2954342236 hasConceptScore W2954342236C191897082 @default.
- W2954342236 hasConceptScore W2954342236C192562407 @default.
- W2954342236 hasConceptScore W2954342236C20625102 @default.
- W2954342236 hasConceptScore W2954342236C2776088076 @default.
- W2954342236 hasConceptScore W2954342236C2778760603 @default.
- W2954342236 hasConceptScore W2954342236C2779229422 @default.
- W2954342236 hasConceptScore W2954342236C27805521 @default.
- W2954342236 hasConceptScore W2954342236C2781448223 @default.
- W2954342236 hasConceptScore W2954342236C47908070 @default.
- W2954342236 hasConceptScore W2954342236C58396970 @default.
- W2954342236 hasConceptScore W2954342236C66938386 @default.
- W2954342236 hasConceptScore W2954342236C87976508 @default.
- W2954342236 hasLocation W29543422361 @default.
- W2954342236 hasOpenAccess W2954342236 @default.
- W2954342236 hasPrimaryLocation W29543422361 @default.
- W2954342236 hasRelatedWork W1973288572 @default.
- W2954342236 hasRelatedWork W1992486802 @default.
- W2954342236 hasRelatedWork W2045829014 @default.
- W2954342236 hasRelatedWork W2049663946 @default.
- W2954342236 hasRelatedWork W2380902838 @default.
- W2954342236 hasRelatedWork W2384668485 @default.
- W2954342236 hasRelatedWork W2606177818 @default.
- W2954342236 hasRelatedWork W2883324369 @default.
- W2954342236 hasRelatedWork W2954342236 @default.
- W2954342236 hasRelatedWork W4234187648 @default.
- W2954342236 hasVolume "105" @default.
- W2954342236 isParatext "false" @default.
- W2954342236 isRetracted "false" @default.
- W2954342236 magId "2954342236" @default.
- W2954342236 workType "article" @default.