- W2954740659 abstract "In this work, wood plastic composites (WPCs) were prepared from a selected recycled poly(ethylene terephthalate) (rPET)/poly(butylene adipate-co-terephthalate) (PBAT) blend ratio. The 70/30 (wt%/wt%) (rPET)/PBAT blend was incorporated with six loadings of wood flour (WF) (5–30 wt%) through melt mixing on a twin screw extruder, followed by injection molding. The mechanical properties of the WPCs, in terms of the impact, tensile and flexural strength, Young’s modulus and elongation at break were determined as a function of the WF content. The results showed that the impact strength and elongation at break of the WPCs were all lower than those of the neat blend. However, the WPCs at 5–15 wt% WF and all had higher impact strength and elongation at break than the neat rPET, respectively. In contrast, the tensile strength of all the WPCs was much lower than that of the neat rPET, and only at high WF content (20–30 wt%) exhibited higher tensile strength than the neat blend. In addition, the Young’s modulus and flexural strength of the WPCs were all higher than those of the neat blend. However, the WPCs at 5 and 10 wt% WF had lower Young’s modulus than the neat rPET, while all the WPCs had lower flexural strength than the neat rPET. Moreover, the WF acted as a nucleating agent, which consequently gave rise to the increased crystallization temperature, degree of crystallinity and melting temperature of the rPET component in WPCs, as revealed by the differential scanning calorimetry. However, thermogravimetric analysis showed a decrease in the thermal stability of the rPET/PBAT blend upon addition of WF. Meanwhile, all the WPCs exhibited an enhanced water uptake over the neat blend (up to 5.7-fold at 30 wt% WF)." @default.
- W2954740659 created "2019-07-12" @default.
- W2954740659 creator A5000982852 @default.
- W2954740659 creator A5006407812 @default.
- W2954740659 creator A5026004416 @default.
- W2954740659 creator A5051093809 @default.
- W2954740659 creator A5059866345 @default.
- W2954740659 date "2019-06-29" @default.
- W2954740659 modified "2023-09-24" @default.
- W2954740659 title "Wood plastic composites based on recycled poly(ethylene terephthalate) and poly(butylene adipate- co -terephthalate)" @default.
- W2954740659 hasPublicationYear "2019" @default.
- W2954740659 type Work @default.
- W2954740659 sameAs 2954740659 @default.
- W2954740659 citedByCount "0" @default.
- W2954740659 crossrefType "journal-article" @default.
- W2954740659 hasAuthorship W2954740659A5000982852 @default.
- W2954740659 hasAuthorship W2954740659A5006407812 @default.
- W2954740659 hasAuthorship W2954740659A5026004416 @default.
- W2954740659 hasAuthorship W2954740659A5051093809 @default.
- W2954740659 hasAuthorship W2954740659A5059866345 @default.
- W2954740659 hasConcept C102267420 @default.
- W2954740659 hasConcept C112950240 @default.
- W2954740659 hasConcept C121332964 @default.
- W2954740659 hasConcept C159985019 @default.
- W2954740659 hasConcept C178405089 @default.
- W2954740659 hasConcept C192562407 @default.
- W2954740659 hasConcept C201865488 @default.
- W2954740659 hasConcept C2779805667 @default.
- W2954740659 hasConcept C33947775 @default.
- W2954740659 hasConcept C39519442 @default.
- W2954740659 hasConcept C46275449 @default.
- W2954740659 hasConcept C809718 @default.
- W2954740659 hasConcept C97355855 @default.
- W2954740659 hasConceptScore W2954740659C102267420 @default.
- W2954740659 hasConceptScore W2954740659C112950240 @default.
- W2954740659 hasConceptScore W2954740659C121332964 @default.
- W2954740659 hasConceptScore W2954740659C159985019 @default.
- W2954740659 hasConceptScore W2954740659C178405089 @default.
- W2954740659 hasConceptScore W2954740659C192562407 @default.
- W2954740659 hasConceptScore W2954740659C201865488 @default.
- W2954740659 hasConceptScore W2954740659C2779805667 @default.
- W2954740659 hasConceptScore W2954740659C33947775 @default.
- W2954740659 hasConceptScore W2954740659C39519442 @default.
- W2954740659 hasConceptScore W2954740659C46275449 @default.
- W2954740659 hasConceptScore W2954740659C809718 @default.
- W2954740659 hasConceptScore W2954740659C97355855 @default.
- W2954740659 hasIssue "2" @default.
- W2954740659 hasLocation W29547406591 @default.
- W2954740659 hasOpenAccess W2954740659 @default.
- W2954740659 hasPrimaryLocation W29547406591 @default.
- W2954740659 hasRelatedWork W1981068156 @default.
- W2954740659 hasRelatedWork W2057156533 @default.
- W2954740659 hasRelatedWork W2091744907 @default.
- W2954740659 hasRelatedWork W2158483042 @default.
- W2954740659 hasRelatedWork W2325700346 @default.
- W2954740659 hasRelatedWork W2347948498 @default.
- W2954740659 hasRelatedWork W2465069227 @default.
- W2954740659 hasRelatedWork W2617034285 @default.
- W2954740659 hasRelatedWork W2795481857 @default.
- W2954740659 hasRelatedWork W2894788146 @default.
- W2954740659 hasRelatedWork W2898463750 @default.
- W2954740659 hasRelatedWork W2906344244 @default.
- W2954740659 hasRelatedWork W2924512298 @default.
- W2954740659 hasRelatedWork W3013761030 @default.
- W2954740659 hasRelatedWork W3041282165 @default.
- W2954740659 hasRelatedWork W3126772127 @default.
- W2954740659 hasRelatedWork W3155545812 @default.
- W2954740659 hasRelatedWork W3201603171 @default.
- W2954740659 hasRelatedWork W342753262 @default.
- W2954740659 hasRelatedWork W72424728 @default.
- W2954740659 hasVolume "29" @default.
- W2954740659 isParatext "false" @default.
- W2954740659 isRetracted "false" @default.
- W2954740659 magId "2954740659" @default.
- W2954740659 workType "article" @default.