- W295673069 abstract "This study has been investigated for tensile properties with lead-free brass containing 1 wt.% of Bi. And also characteristic of corrosion resistance was analyzed by polarization test. An increase of tempering temperature was found to tend to decrease tensile strength, and percentage of elongation was shown to be the lowest value at . On the other hand, the elongation was increased with an increase of tempering temperature after . The change of mechanical properties was closely related with the content and shape of acicular Witmansttten formed at the interface of phase as well as in phase. Tensile strength had a tendency to be decreased with an increase of test temperature. The elongation was shown to be the lowest value at around , while it began to increase as test temperature rose after . It might be speculated that the reason that elongation was decreased was found to form bismuth film at the interface of phase leading to be easily brittle when loaded by tensile stress. The lead-free brass containing 1 wt.% of Bi had similar characteristic of corrosion resistance with a free-cutting brass with 3.4 wt. % of Pb in spite of higher fraction of phase." @default.
- W295673069 created "2016-06-24" @default.
- W295673069 creator A5004058965 @default.
- W295673069 creator A5006994078 @default.
- W295673069 creator A5042813515 @default.
- W295673069 creator A5060552071 @default.
- W295673069 creator A5067379413 @default.
- W295673069 date "2011-01-01" @default.
- W295673069 modified "2023-10-15" @default.
- W295673069 title "Characteristics of Tensile Strength and Corrosion Resistance of Lead- free Brass Containing 1 wt.% of Bi" @default.
- W295673069 hasPublicationYear "2011" @default.
- W295673069 type Work @default.
- W295673069 sameAs 295673069 @default.
- W295673069 citedByCount "0" @default.
- W295673069 crossrefType "journal-article" @default.
- W295673069 hasAuthorship W295673069A5004058965 @default.
- W295673069 hasAuthorship W295673069A5006994078 @default.
- W295673069 hasAuthorship W295673069A5042813515 @default.
- W295673069 hasAuthorship W295673069A5060552071 @default.
- W295673069 hasAuthorship W295673069A5067379413 @default.
- W295673069 hasConcept C112950240 @default.
- W295673069 hasConcept C136478896 @default.
- W295673069 hasConcept C152106835 @default.
- W295673069 hasConcept C159985019 @default.
- W295673069 hasConcept C182508753 @default.
- W295673069 hasConcept C191897082 @default.
- W295673069 hasConcept C192562407 @default.
- W295673069 hasConcept C20625102 @default.
- W295673069 hasConcept C207948433 @default.
- W295673069 hasConcept C2780033417 @default.
- W295673069 hasConcept C33947775 @default.
- W295673069 hasConcept C544778455 @default.
- W295673069 hasConcept C87976508 @default.
- W295673069 hasConceptScore W295673069C112950240 @default.
- W295673069 hasConceptScore W295673069C136478896 @default.
- W295673069 hasConceptScore W295673069C152106835 @default.
- W295673069 hasConceptScore W295673069C159985019 @default.
- W295673069 hasConceptScore W295673069C182508753 @default.
- W295673069 hasConceptScore W295673069C191897082 @default.
- W295673069 hasConceptScore W295673069C192562407 @default.
- W295673069 hasConceptScore W295673069C20625102 @default.
- W295673069 hasConceptScore W295673069C207948433 @default.
- W295673069 hasConceptScore W295673069C2780033417 @default.
- W295673069 hasConceptScore W295673069C33947775 @default.
- W295673069 hasConceptScore W295673069C544778455 @default.
- W295673069 hasConceptScore W295673069C87976508 @default.
- W295673069 hasIssue "3" @default.
- W295673069 hasLocation W2956730691 @default.
- W295673069 hasOpenAccess W295673069 @default.
- W295673069 hasPrimaryLocation W2956730691 @default.
- W295673069 hasRelatedWork W120137703 @default.
- W295673069 hasRelatedWork W1978198290 @default.
- W295673069 hasRelatedWork W1993973153 @default.
- W295673069 hasRelatedWork W1997245191 @default.
- W295673069 hasRelatedWork W2030753917 @default.
- W295673069 hasRelatedWork W2089453440 @default.
- W295673069 hasRelatedWork W2315486213 @default.
- W295673069 hasRelatedWork W2328257393 @default.
- W295673069 hasRelatedWork W2329222097 @default.
- W295673069 hasRelatedWork W2331634670 @default.
- W295673069 hasRelatedWork W2367227534 @default.
- W295673069 hasRelatedWork W2406955855 @default.
- W295673069 hasRelatedWork W2522542283 @default.
- W295673069 hasRelatedWork W2593546670 @default.
- W295673069 hasRelatedWork W2901894126 @default.
- W295673069 hasRelatedWork W2993148529 @default.
- W295673069 hasRelatedWork W2999282549 @default.
- W295673069 hasRelatedWork W804494955 @default.
- W295673069 hasRelatedWork W806678303 @default.
- W295673069 hasRelatedWork W836407280 @default.
- W295673069 hasVolume "24" @default.
- W295673069 isParatext "false" @default.
- W295673069 isRetracted "false" @default.
- W295673069 magId "295673069" @default.
- W295673069 workType "article" @default.