- W2965540926 abstract "In this work, an effort has been made for multimaterial three-dimensional printing of functionally graded prototypes of polylactic acid matrix (tensile specimens as per ASTM D638 type IV) followed by characterization of mechanical and surface properties. The work is an extension of previous reported studies on twin-screw extrusion process for the preparation of multimaterial wires as feedstock filaments in possible three-dimensional printing applications. The results of the study suggest that the highest peak strength (46.28 MPa) and break strength (41.65 MPa) was obtained for multimaterial three-dimensional printed samples at infill density 100%, infill angle 45°, and infill speed of 90 mm/s on commercial open source fused deposition modeling setup. Further surface hardness measurements performed on two extreme surfaces (top surface comprising magnetite (Fe 3 O 4 )-reinforced polylactic acid and bottom with polylactic acid without any reinforcement) revealed that the hardness for the bottom layer was more than the hardness for the top layer. From fractured surface analysis (using photomicrographs), it has been observed that the three-dimensional printed samples with low infill density resulted into more void formation due to which the performance while mechanical testing was poor in comparison to samples printed with higher infill density. The results are also supported by rendered images of photomicrographs, which revealed that high roughness value of samples printed with low infill density was also one of the reasons for poor mechanical performance of multimaterial three-dimensional printed functionally graded prototypes." @default.
- W2965540926 created "2019-08-13" @default.
- W2965540926 creator A5007534864 @default.
- W2965540926 creator A5037212191 @default.
- W2965540926 creator A5060718099 @default.
- W2965540926 creator A5085210742 @default.
- W2965540926 date "2019-08-06" @default.
- W2965540926 modified "2023-10-16" @default.
- W2965540926 title "Multimaterial printing and characterization for mechanical and surface properties of functionally graded prototype" @default.
- W2965540926 cites W1489485921 @default.
- W2965540926 cites W2076658816 @default.
- W2965540926 cites W2082402358 @default.
- W2965540926 cites W2085911112 @default.
- W2965540926 cites W2284024842 @default.
- W2965540926 cites W2342789023 @default.
- W2965540926 cites W2527810566 @default.
- W2965540926 cites W2536032352 @default.
- W2965540926 cites W2566005376 @default.
- W2965540926 cites W2589631631 @default.
- W2965540926 cites W2598999669 @default.
- W2965540926 cites W2600716145 @default.
- W2965540926 cites W2602424030 @default.
- W2965540926 cites W2613577497 @default.
- W2965540926 cites W2613920225 @default.
- W2965540926 cites W2617594473 @default.
- W2965540926 cites W2733952291 @default.
- W2965540926 cites W2740821549 @default.
- W2965540926 cites W2751127761 @default.
- W2965540926 cites W2753845874 @default.
- W2965540926 cites W2754093714 @default.
- W2965540926 cites W2761339929 @default.
- W2965540926 cites W2772702140 @default.
- W2965540926 cites W2789511396 @default.
- W2965540926 cites W2792602595 @default.
- W2965540926 cites W2887763286 @default.
- W2965540926 cites W2956021740 @default.
- W2965540926 cites W815080081 @default.
- W2965540926 doi "https://doi.org/10.1177/0954406219867984" @default.
- W2965540926 hasPublicationYear "2019" @default.
- W2965540926 type Work @default.
- W2965540926 sameAs 2965540926 @default.
- W2965540926 citedByCount "20" @default.
- W2965540926 countsByYear W29655409262019 @default.
- W2965540926 countsByYear W29655409262020 @default.
- W2965540926 countsByYear W29655409262021 @default.
- W2965540926 countsByYear W29655409262022 @default.
- W2965540926 countsByYear W29655409262023 @default.
- W2965540926 crossrefType "journal-article" @default.
- W2965540926 hasAuthorship W2965540926A5007534864 @default.
- W2965540926 hasAuthorship W2965540926A5037212191 @default.
- W2965540926 hasAuthorship W2965540926A5060718099 @default.
- W2965540926 hasAuthorship W2965540926A5085210742 @default.
- W2965540926 hasConcept C107365816 @default.
- W2965540926 hasConcept C112950240 @default.
- W2965540926 hasConcept C127413603 @default.
- W2965540926 hasConcept C159985019 @default.
- W2965540926 hasConcept C192562407 @default.
- W2965540926 hasConcept C2778958987 @default.
- W2965540926 hasConcept C2781162966 @default.
- W2965540926 hasConcept C2781219549 @default.
- W2965540926 hasConcept C521977710 @default.
- W2965540926 hasConcept C524769229 @default.
- W2965540926 hasConcept C66938386 @default.
- W2965540926 hasConceptScore W2965540926C107365816 @default.
- W2965540926 hasConceptScore W2965540926C112950240 @default.
- W2965540926 hasConceptScore W2965540926C127413603 @default.
- W2965540926 hasConceptScore W2965540926C159985019 @default.
- W2965540926 hasConceptScore W2965540926C192562407 @default.
- W2965540926 hasConceptScore W2965540926C2778958987 @default.
- W2965540926 hasConceptScore W2965540926C2781162966 @default.
- W2965540926 hasConceptScore W2965540926C2781219549 @default.
- W2965540926 hasConceptScore W2965540926C521977710 @default.
- W2965540926 hasConceptScore W2965540926C524769229 @default.
- W2965540926 hasConceptScore W2965540926C66938386 @default.
- W2965540926 hasIssue "19-20" @default.
- W2965540926 hasLocation W29655409261 @default.
- W2965540926 hasOpenAccess W2965540926 @default.
- W2965540926 hasPrimaryLocation W29655409261 @default.
- W2965540926 hasRelatedWork W2045171965 @default.
- W2965540926 hasRelatedWork W2089085266 @default.
- W2965540926 hasRelatedWork W2354203570 @default.
- W2965540926 hasRelatedWork W2795554382 @default.
- W2965540926 hasRelatedWork W3087400716 @default.
- W2965540926 hasRelatedWork W3128926079 @default.
- W2965540926 hasRelatedWork W3213099864 @default.
- W2965540926 hasRelatedWork W4212977460 @default.
- W2965540926 hasRelatedWork W4285533892 @default.
- W2965540926 hasRelatedWork W4380624596 @default.
- W2965540926 hasVolume "233" @default.
- W2965540926 isParatext "false" @default.
- W2965540926 isRetracted "false" @default.
- W2965540926 magId "2965540926" @default.
- W2965540926 workType "article" @default.