- W2966804533 abstract "The resistance against stress corrosion cracking of a metallic material strongly depends on the quality of the present oxide layer as well as material resistance to hydrogen induced cracking. In case of nickel alloy UNS N07718 (alloy 718), the material susceptibility to stress corrosion cracking has been assumed to depend in particular on the material hardness. A systematic study of the corrosion properties of alloy 718 has been conducted with the main objective to investigate the nature of the correlation between aging temperature and the material corrosion performance as this correlation has been reported in the literature.Electrochemical experiments conducted on samples aged at different temperatures indicated a higher localized corrosion resistance for those samples which have been heat treated at lower temperature (8h at 760 °C) compared to those heat treated at higher temperature (8h at 870 °C). However, the observed differences in the corrosion behavior could not be attributed solely to the precipitation of the intermetallic phases, such as γ'+γ'' and δ. Complementary investigations of the oxide layers revealed differences in their composition as a result of the aging temperature. Further, the presence of atomic hydrogen in the material bulk was found to reduce the material ability to build a protective passive layer. The degree of the impairment increased with an increasing heat treatment temperature.No correlation between the hardness of the alloy 718 and its hydrogen embrittlement susceptibility could be demonstrated. In addition, besides the recognized detrimental effect of orthorhombic phase precipitation δ on the hydrogen embrittlement resistance of alloy 718, the hydrogen embrittlement susceptibility of the material was found to correlate with the size and fraction of γ'+γ'' precipitates. Among the tested material variants, the double aged material (8h at 720 °C followed by 8h at 620 °C) revealed the lowest degree of susceptibility. Thus, it is the morphology of the strengthening phase but not the hardness (as suggested in the API specification) that provides the significant contribution to the degradation mechanism of alloy 718 in hydrogen containing environments." @default.
- W2966804533 created "2019-08-13" @default.
- W2966804533 creator A5087582778 @default.
- W2966804533 date "2019-01-01" @default.
- W2966804533 modified "2023-09-23" @default.
- W2966804533 title "Effect of the microstructure of nickel alloy 718 Oil Patch on its corrosion behavior" @default.
- W2966804533 hasPublicationYear "2019" @default.
- W2966804533 type Work @default.
- W2966804533 sameAs 2966804533 @default.
- W2966804533 citedByCount "0" @default.
- W2966804533 crossrefType "dissertation" @default.
- W2966804533 hasAuthorship W2966804533A5087582778 @default.
- W2966804533 hasConcept C107054158 @default.
- W2966804533 hasConcept C121332964 @default.
- W2966804533 hasConcept C153294291 @default.
- W2966804533 hasConcept C191897082 @default.
- W2966804533 hasConcept C192562407 @default.
- W2966804533 hasConcept C20625102 @default.
- W2966804533 hasConcept C27501479 @default.
- W2966804533 hasConcept C2778760603 @default.
- W2966804533 hasConcept C2779851234 @default.
- W2966804533 hasConcept C2780026712 @default.
- W2966804533 hasConcept C87976508 @default.
- W2966804533 hasConcept C92621854 @default.
- W2966804533 hasConceptScore W2966804533C107054158 @default.
- W2966804533 hasConceptScore W2966804533C121332964 @default.
- W2966804533 hasConceptScore W2966804533C153294291 @default.
- W2966804533 hasConceptScore W2966804533C191897082 @default.
- W2966804533 hasConceptScore W2966804533C192562407 @default.
- W2966804533 hasConceptScore W2966804533C20625102 @default.
- W2966804533 hasConceptScore W2966804533C27501479 @default.
- W2966804533 hasConceptScore W2966804533C2778760603 @default.
- W2966804533 hasConceptScore W2966804533C2779851234 @default.
- W2966804533 hasConceptScore W2966804533C2780026712 @default.
- W2966804533 hasConceptScore W2966804533C87976508 @default.
- W2966804533 hasConceptScore W2966804533C92621854 @default.
- W2966804533 hasLocation W29668045331 @default.
- W2966804533 hasOpenAccess W2966804533 @default.
- W2966804533 hasPrimaryLocation W29668045331 @default.
- W2966804533 hasRelatedWork W1985693630 @default.
- W2966804533 hasRelatedWork W1994450590 @default.
- W2966804533 hasRelatedWork W2019814446 @default.
- W2966804533 hasRelatedWork W2022024069 @default.
- W2966804533 hasRelatedWork W2101852535 @default.
- W2966804533 hasRelatedWork W2214421009 @default.
- W2966804533 hasRelatedWork W2276721923 @default.
- W2966804533 hasRelatedWork W2313971829 @default.
- W2966804533 hasRelatedWork W2354894475 @default.
- W2966804533 hasRelatedWork W2361695913 @default.
- W2966804533 hasRelatedWork W2547096436 @default.
- W2966804533 hasRelatedWork W2560083543 @default.
- W2966804533 hasRelatedWork W2561761579 @default.
- W2966804533 hasRelatedWork W2786278440 @default.
- W2966804533 hasRelatedWork W2792467876 @default.
- W2966804533 hasRelatedWork W2883462631 @default.
- W2966804533 hasRelatedWork W2924067924 @default.
- W2966804533 hasRelatedWork W2951749411 @default.
- W2966804533 hasRelatedWork W3149575037 @default.
- W2966804533 hasRelatedWork W2470054742 @default.
- W2966804533 isParatext "false" @default.
- W2966804533 isRetracted "false" @default.
- W2966804533 magId "2966804533" @default.
- W2966804533 workType "dissertation" @default.