- W2967113445 abstract "This study investigates the mechanical and corrosion properties of as-built and annealed equiatomic CoCrFeMnNi alloy produced by laser-based directed energy deposition (DED) Additive Manufacturing (AM). The high cooling rates of DED produced a single-phase, cellular microstructure with cells on the order of 4 μm in diameter and inter-cellular regions that were enriched in Mn and Ni. Annealing created a chemically homogeneous recrystallized microstructure with a high density of annealing twins. The average yield strength of the as-built condition was 424 MPa and exceeded the annealed condition (232 MPa), however; the strain hardening rate was lower for the as-built material stemming from higher dislocation density associated with DED parts and the fine cell size. In general, the yield strength, ultimate tensile strength, and elongation-to-failure for the as-built material exceeded values from previous studies that explored other AM techniques to produce the CoCrFeMnNi alloy. Ductile fracture occurred for all specimens with dimple initiation associated with nanoscale oxide inclusions. The breakdown potential (onset of pitting corrosion) was similar for the as-built and annealed conditions at 0.40 VAg/AgCl when immersed in 0.6 M NaCl. Pit morphology/propagation for the as-built condition exhibited preferential corrosion of inter-cellular Ni/Mn regions leading to a tortuous pit bottom and cover, while the annealed conditions pits resembled lacy pits similar to 304 L steel. A passive oxide film depleted in Cr cations with substantial incorporation of Mn cations is proposed as the primary mechanism for local corrosion susceptibility of the CoCrFeMnNi alloy." @default.
- W2967113445 created "2019-08-22" @default.
- W2967113445 creator A5000999330 @default.
- W2967113445 creator A5006904534 @default.
- W2967113445 creator A5010279761 @default.
- W2967113445 creator A5016768188 @default.
- W2967113445 creator A5016883455 @default.
- W2967113445 creator A5042486596 @default.
- W2967113445 creator A5045344754 @default.
- W2967113445 creator A5046185564 @default.
- W2967113445 creator A5049550408 @default.
- W2967113445 creator A5054376511 @default.
- W2967113445 creator A5079845699 @default.
- W2967113445 creator A5086926089 @default.
- W2967113445 date "2019-10-01" @default.
- W2967113445 modified "2023-10-05" @default.
- W2967113445 title "Mechanical and Corrosion Properties of Additively Manufactured CoCrFeMnNi High Entropy Alloy" @default.
- W2967113445 cites W1110110480 @default.
- W2967113445 cites W1149067067 @default.
- W2967113445 cites W1430355326 @default.
- W2967113445 cites W1971401536 @default.
- W2967113445 cites W1974916854 @default.
- W2967113445 cites W1978497078 @default.
- W2967113445 cites W1978634896 @default.
- W2967113445 cites W1980933061 @default.
- W2967113445 cites W1982659627 @default.
- W2967113445 cites W1986562743 @default.
- W2967113445 cites W1990655944 @default.
- W2967113445 cites W1995781421 @default.
- W2967113445 cites W1996451095 @default.
- W2967113445 cites W1999950656 @default.
- W2967113445 cites W2001027811 @default.
- W2967113445 cites W2001642333 @default.
- W2967113445 cites W2003975937 @default.
- W2967113445 cites W2009646743 @default.
- W2967113445 cites W2014653052 @default.
- W2967113445 cites W2024654735 @default.
- W2967113445 cites W2029022131 @default.
- W2967113445 cites W2035069448 @default.
- W2967113445 cites W2035742184 @default.
- W2967113445 cites W2035961263 @default.
- W2967113445 cites W2037346886 @default.
- W2967113445 cites W2041915485 @default.
- W2967113445 cites W2042386708 @default.
- W2967113445 cites W2047064755 @default.
- W2967113445 cites W2058085399 @default.
- W2967113445 cites W2063241169 @default.
- W2967113445 cites W2066578528 @default.
- W2967113445 cites W2070540993 @default.
- W2967113445 cites W2077134271 @default.
- W2967113445 cites W2079837718 @default.
- W2967113445 cites W2082143808 @default.
- W2967113445 cites W2090244344 @default.
- W2967113445 cites W2090989574 @default.
- W2967113445 cites W2095333217 @default.
- W2967113445 cites W2116021661 @default.
- W2967113445 cites W2117420780 @default.
- W2967113445 cites W2130315953 @default.
- W2967113445 cites W2288827195 @default.
- W2967113445 cites W2329196226 @default.
- W2967113445 cites W2340511858 @default.
- W2967113445 cites W2342455723 @default.
- W2967113445 cites W2370998538 @default.
- W2967113445 cites W2483357472 @default.
- W2967113445 cites W2503161491 @default.
- W2967113445 cites W2520167087 @default.
- W2967113445 cites W2534691303 @default.
- W2967113445 cites W2536370708 @default.
- W2967113445 cites W2545577671 @default.
- W2967113445 cites W2551355684 @default.
- W2967113445 cites W2556944620 @default.
- W2967113445 cites W2563830016 @default.
- W2967113445 cites W2574020411 @default.
- W2967113445 cites W2593338964 @default.
- W2967113445 cites W2669160295 @default.
- W2967113445 cites W2726289758 @default.
- W2967113445 cites W2736831392 @default.
- W2967113445 cites W2744531604 @default.
- W2967113445 cites W2750470740 @default.
- W2967113445 cites W2754825399 @default.
- W2967113445 cites W2762253718 @default.
- W2967113445 cites W2770800476 @default.
- W2967113445 cites W2770949273 @default.
- W2967113445 cites W2772933957 @default.
- W2967113445 cites W2774518900 @default.
- W2967113445 cites W2789828320 @default.
- W2967113445 cites W2791063905 @default.
- W2967113445 cites W2791441665 @default.
- W2967113445 cites W2792901951 @default.
- W2967113445 cites W2796887263 @default.
- W2967113445 cites W2796927376 @default.
- W2967113445 cites W2800486592 @default.
- W2967113445 cites W2803213951 @default.
- W2967113445 cites W2804539599 @default.
- W2967113445 cites W2810696792 @default.
- W2967113445 cites W2870946992 @default.
- W2967113445 cites W2883441668 @default.
- W2967113445 cites W2884242709 @default.