- W2968853971 abstract "In this study, bond properties of glass fibre reinforced polymer (GFRP) bars embedded in high-strength concrete (HSC) were experimentally investigated using a pull-out test. The experimental program consisted of testing 84 pull-out specimens prepared according to ACI 440.3R-12 standard. The testing of the specimens was carried out considering bar diameter (9.5, 12.7 and 15.9 mm), embedment length (2.5, 5, 7.5 and 10 times bar diameter) and surface configuration (helical wrapping with slight sand coating (HW-SC) and sand coating (SC)) as the main parameters. Twelve pull-out specimens reinforced with 16 mm steel bar were also tested for comparison purposes. Most of the specimens failed by a pull-out mode. Visual inspection of the tested specimens reinforced with GFRP (HW-SC) bars showed that the pull-out failure was due to the damage of outer bar surface, whilst the detachment of the sand coating was responsible for the bond failure of GFRP (SC) reinforced specimens. The bond stress – slip behaviour of GFRP (HW-SC) bars is different from that of GFRP (SC) bars and it was also found that GFRP (SC) bars gave a better bond performance than GFRP (HW-SC) bars. It was observed that the reduction rate of bond strength of both GFRP types with increasing the bar diameter and the embedment length was reduced in the case of high-strength concrete. Bond strength predictions obtained from ACI-440.1R, CSAS806, CSA-S6 and JSCE design codes were compared with the experimental results. Overall, all design guidelines were conservative in predicting bond strength of both GFRP bars in HSC and ACI predictions were closer to the tested results than other codes." @default.
- W2968853971 created "2019-08-22" @default.
- W2968853971 creator A5024242778 @default.
- W2968853971 creator A5047471695 @default.
- W2968853971 creator A5076198747 @default.
- W2968853971 date "2019-12-01" @default.
- W2968853971 modified "2023-10-15" @default.
- W2968853971 title "Bond between glass fibre reinforced polymer bars and high - strength concrete" @default.
- W2968853971 cites W1972115104 @default.
- W2968853971 cites W1972346300 @default.
- W2968853971 cites W1973375031 @default.
- W2968853971 cites W1979659224 @default.
- W2968853971 cites W1980422154 @default.
- W2968853971 cites W1988432363 @default.
- W2968853971 cites W1994997039 @default.
- W2968853971 cites W1997300581 @default.
- W2968853971 cites W1997712501 @default.
- W2968853971 cites W2045526541 @default.
- W2968853971 cites W2045735107 @default.
- W2968853971 cites W2048308123 @default.
- W2968853971 cites W2061329829 @default.
- W2968853971 cites W2065566730 @default.
- W2968853971 cites W2066203345 @default.
- W2968853971 cites W2069693235 @default.
- W2968853971 cites W2081635709 @default.
- W2968853971 cites W2106985403 @default.
- W2968853971 cites W2112394540 @default.
- W2968853971 cites W2142402509 @default.
- W2968853971 cites W2162766690 @default.
- W2968853971 cites W2292312195 @default.
- W2968853971 cites W2354804155 @default.
- W2968853971 cites W2597943520 @default.
- W2968853971 cites W2616649059 @default.
- W2968853971 doi "https://doi.org/10.1016/j.istruc.2019.08.003" @default.
- W2968853971 hasPublicationYear "2019" @default.
- W2968853971 type Work @default.
- W2968853971 sameAs 2968853971 @default.
- W2968853971 citedByCount "16" @default.
- W2968853971 countsByYear W29688539712020 @default.
- W2968853971 countsByYear W29688539712021 @default.
- W2968853971 countsByYear W29688539712022 @default.
- W2968853971 countsByYear W29688539712023 @default.
- W2968853971 crossrefType "journal-article" @default.
- W2968853971 hasAuthorship W2968853971A5024242778 @default.
- W2968853971 hasAuthorship W2968853971A5047471695 @default.
- W2968853971 hasAuthorship W2968853971A5076198747 @default.
- W2968853971 hasBestOaLocation W29688539712 @default.
- W2968853971 hasConcept C121332964 @default.
- W2968853971 hasConcept C127413603 @default.
- W2968853971 hasConcept C153294291 @default.
- W2968853971 hasConcept C159096172 @default.
- W2968853971 hasConcept C159985019 @default.
- W2968853971 hasConcept C177229083 @default.
- W2968853971 hasConcept C188721877 @default.
- W2968853971 hasConcept C192562407 @default.
- W2968853971 hasConcept C2777488572 @default.
- W2968853971 hasConcept C2779227376 @default.
- W2968853971 hasConcept C62464604 @default.
- W2968853971 hasConcept C66938386 @default.
- W2968853971 hasConcept C68928338 @default.
- W2968853971 hasConcept C76344452 @default.
- W2968853971 hasConceptScore W2968853971C121332964 @default.
- W2968853971 hasConceptScore W2968853971C127413603 @default.
- W2968853971 hasConceptScore W2968853971C153294291 @default.
- W2968853971 hasConceptScore W2968853971C159096172 @default.
- W2968853971 hasConceptScore W2968853971C159985019 @default.
- W2968853971 hasConceptScore W2968853971C177229083 @default.
- W2968853971 hasConceptScore W2968853971C188721877 @default.
- W2968853971 hasConceptScore W2968853971C192562407 @default.
- W2968853971 hasConceptScore W2968853971C2777488572 @default.
- W2968853971 hasConceptScore W2968853971C2779227376 @default.
- W2968853971 hasConceptScore W2968853971C62464604 @default.
- W2968853971 hasConceptScore W2968853971C66938386 @default.
- W2968853971 hasConceptScore W2968853971C68928338 @default.
- W2968853971 hasConceptScore W2968853971C76344452 @default.
- W2968853971 hasLocation W29688539711 @default.
- W2968853971 hasLocation W29688539712 @default.
- W2968853971 hasOpenAccess W2968853971 @default.
- W2968853971 hasPrimaryLocation W29688539711 @default.
- W2968853971 hasRelatedWork W1502496255 @default.
- W2968853971 hasRelatedWork W1997691451 @default.
- W2968853971 hasRelatedWork W2056029287 @default.
- W2968853971 hasRelatedWork W2384656084 @default.
- W2968853971 hasRelatedWork W2549313834 @default.
- W2968853971 hasRelatedWork W2743346270 @default.
- W2968853971 hasRelatedWork W4289868979 @default.
- W2968853971 hasRelatedWork W4361222951 @default.
- W2968853971 hasRelatedWork W2184923763 @default.
- W2968853971 hasRelatedWork W3100768804 @default.
- W2968853971 hasVolume "22" @default.
- W2968853971 isParatext "false" @default.
- W2968853971 isRetracted "false" @default.
- W2968853971 magId "2968853971" @default.
- W2968853971 workType "article" @default.