- W2969355875 abstract "The microporous poly(l-lactic acid) (PLLA) materials were prepared by uniaxial stretching PLLA/20 wt% silica (SiO2) composites. The SiO2 fillers with particle size of 15 nm, 200 nm, 500 nm, 1 μm, 2 μm, and 5 μm were selected to investigate the effect of particle size of fillers on the microstructures and physical properties of the microporous PLLA materials. Micropores were formed due to the debonding at the interface between PLLA and SiO2. The composites with SiO2 particle size of 15 nm, 200 nm, 500 nm, 1 μm, 2 μm, and 5 μm began to debond at 1.4, 1.0, 1.0, 1.0, 0.9, and 0.7, respectively. With the increase of SiO2 particle size, the micropore diameter was enlarged at the same stretching ratio, while the particle number of SiO2 was decreased, however, the porosity was still increased. The mechanical properties, thermal insulation properties, and water vapor permeation properties of microporous PLLA samples were all improved compared with that of undrawn PLLA." @default.
- W2969355875 created "2019-08-29" @default.
- W2969355875 creator A5049340999 @default.
- W2969355875 creator A5078464541 @default.
- W2969355875 creator A5087758903 @default.
- W2969355875 date "2019-10-01" @default.
- W2969355875 modified "2023-09-26" @default.
- W2969355875 title "Effect of silica particle size on the microstructure and physical properties of microporous poly(L-lactic acid) produced by uniaxial stretching" @default.
- W2969355875 cites W1522565972 @default.
- W2969355875 cites W1964905246 @default.
- W2969355875 cites W1984017425 @default.
- W2969355875 cites W2013310766 @default.
- W2969355875 cites W2028466812 @default.
- W2969355875 cites W2035200786 @default.
- W2969355875 cites W2041554814 @default.
- W2969355875 cites W2044545591 @default.
- W2969355875 cites W2047404494 @default.
- W2969355875 cites W2053266396 @default.
- W2969355875 cites W2058905557 @default.
- W2969355875 cites W2067615468 @default.
- W2969355875 cites W2069094067 @default.
- W2969355875 cites W2086401134 @default.
- W2969355875 cites W2098718451 @default.
- W2969355875 cites W2103438534 @default.
- W2969355875 cites W2136214937 @default.
- W2969355875 cites W2164824911 @default.
- W2969355875 cites W2194224170 @default.
- W2969355875 cites W2278832929 @default.
- W2969355875 cites W2324426323 @default.
- W2969355875 cites W2334825512 @default.
- W2969355875 cites W2337351874 @default.
- W2969355875 cites W2595369245 @default.
- W2969355875 cites W2760850801 @default.
- W2969355875 cites W2792811756 @default.
- W2969355875 cites W2800924366 @default.
- W2969355875 cites W2802422026 @default.
- W2969355875 cites W2811216174 @default.
- W2969355875 cites W2892142261 @default.
- W2969355875 doi "https://doi.org/10.1016/j.polymertesting.2019.106051" @default.
- W2969355875 hasPublicationYear "2019" @default.
- W2969355875 type Work @default.
- W2969355875 sameAs 2969355875 @default.
- W2969355875 citedByCount "1" @default.
- W2969355875 countsByYear W29693558752023 @default.
- W2969355875 crossrefType "journal-article" @default.
- W2969355875 hasAuthorship W2969355875A5049340999 @default.
- W2969355875 hasAuthorship W2969355875A5078464541 @default.
- W2969355875 hasAuthorship W2969355875A5087758903 @default.
- W2969355875 hasBestOaLocation W29693558751 @default.
- W2969355875 hasConcept C111368507 @default.
- W2969355875 hasConcept C127313418 @default.
- W2969355875 hasConcept C127413603 @default.
- W2969355875 hasConcept C159985019 @default.
- W2969355875 hasConcept C187530423 @default.
- W2969355875 hasConcept C192562407 @default.
- W2969355875 hasConcept C2778517922 @default.
- W2969355875 hasConcept C42360764 @default.
- W2969355875 hasConcept C6648577 @default.
- W2969355875 hasConcept C86381522 @default.
- W2969355875 hasConcept C87976508 @default.
- W2969355875 hasConceptScore W2969355875C111368507 @default.
- W2969355875 hasConceptScore W2969355875C127313418 @default.
- W2969355875 hasConceptScore W2969355875C127413603 @default.
- W2969355875 hasConceptScore W2969355875C159985019 @default.
- W2969355875 hasConceptScore W2969355875C187530423 @default.
- W2969355875 hasConceptScore W2969355875C192562407 @default.
- W2969355875 hasConceptScore W2969355875C2778517922 @default.
- W2969355875 hasConceptScore W2969355875C42360764 @default.
- W2969355875 hasConceptScore W2969355875C6648577 @default.
- W2969355875 hasConceptScore W2969355875C86381522 @default.
- W2969355875 hasConceptScore W2969355875C87976508 @default.
- W2969355875 hasFunder F4320321001 @default.
- W2969355875 hasFunder F4320335777 @default.
- W2969355875 hasLocation W29693558751 @default.
- W2969355875 hasOpenAccess W2969355875 @default.
- W2969355875 hasPrimaryLocation W29693558751 @default.
- W2969355875 hasRelatedWork W2058945371 @default.
- W2969355875 hasRelatedWork W2075580692 @default.
- W2969355875 hasRelatedWork W2093275523 @default.
- W2969355875 hasRelatedWork W2108454985 @default.
- W2969355875 hasRelatedWork W2111421561 @default.
- W2969355875 hasRelatedWork W2288127563 @default.
- W2969355875 hasRelatedWork W2351679394 @default.
- W2969355875 hasRelatedWork W2384279159 @default.
- W2969355875 hasRelatedWork W2483054628 @default.
- W2969355875 hasRelatedWork W2998742806 @default.
- W2969355875 hasVolume "79" @default.
- W2969355875 isParatext "false" @default.
- W2969355875 isRetracted "false" @default.
- W2969355875 magId "2969355875" @default.
- W2969355875 workType "article" @default.