- W2977883715 abstract "Isothermal redox kinetics of as-received Co3O4 (AC), 1 h ball milled Co3O4 (BC), and 1 h ball milled Co3O4-15wt.% Fe2O3 (BCF) was investigated at various temperatures (1130, 1100, 1070, and 1040 °C for reduction and 830, 860, and 890°C for re-oxidation) by thermogravimetric method. It was found that mechanical activation with and without Fe2O3 addition decreases the rate of reduction in all isothermal reduction temperatures, while it improves the rate of re-oxidation in lower re-oxidation temperatures. Mechanical activation with and without Fe2O3 addition preserves and decreases the rate of re-oxidation at higher re-oxidation temperatures, respectively. In addition, according to the results, the re-oxidation kinetics was slower than reduction kinetics. A model-free method was used to calculate the redox activation energies. It was found that mechanical activation individually increases the reduction activation energy, while mechanical activation along with Fe2O3 addition decreases the reduction activation energy in comparison with as-received Co3O4. The results showed that reduction activation energies of AC, BC, and BCF samples varies depending on the reacted fraction (α) and are in the range of 140.6 – 166.6 kJ/mol, 175.5 – 213.7 kJ/mol and 111.5 – 121.3 kJ/mol, respectively. The results also showed that although both mechanical activations with and without Fe2O3 addition decreases the re-oxidation activation energy in comparison with as-received cobalt oxide, but the impact of mechanical activation without Fe2O3 addition on activation energy decline, is higher. Moreover, it was found that activation energies for the re-oxidation of AC, BC, and BCF samples are negative, variations depending on the reacted fraction (α), and are in the range of -76.8 to -133.5 kJ/mol, -440.2 to -471.9 kJ/mol, and -190.8 to -196.05 kJ/mol, respectively." @default.
- W2977883715 created "2019-10-10" @default.
- W2977883715 date "2019-08-01" @default.
- W2977883715 modified "2023-09-25" @default.
- W2977883715 title "Isothermal Redox Kinetics of Co3O4-Fe2O3 Nano-Composite as a Thermochemical Heat Storage Material" @default.
- W2977883715 doi "https://doi.org/10.5829/ije.2019.32.08b.17" @default.
- W2977883715 hasPublicationYear "2019" @default.
- W2977883715 type Work @default.
- W2977883715 sameAs 2977883715 @default.
- W2977883715 citedByCount "2" @default.
- W2977883715 countsByYear W29778837152022 @default.
- W2977883715 countsByYear W29778837152023 @default.
- W2977883715 crossrefType "journal-article" @default.
- W2977883715 hasBestOaLocation W29778837151 @default.
- W2977883715 hasConcept C121332964 @default.
- W2977883715 hasConcept C133347239 @default.
- W2977883715 hasConcept C147789679 @default.
- W2977883715 hasConcept C148898269 @default.
- W2977883715 hasConcept C161790260 @default.
- W2977883715 hasConcept C175113610 @default.
- W2977883715 hasConcept C178790620 @default.
- W2977883715 hasConcept C179104552 @default.
- W2977883715 hasConcept C185592680 @default.
- W2977883715 hasConcept C192562407 @default.
- W2977883715 hasConcept C36663273 @default.
- W2977883715 hasConcept C515602321 @default.
- W2977883715 hasConcept C55904794 @default.
- W2977883715 hasConcept C60100273 @default.
- W2977883715 hasConcept C62520636 @default.
- W2977883715 hasConcept C93391505 @default.
- W2977883715 hasConcept C95121573 @default.
- W2977883715 hasConcept C97355855 @default.
- W2977883715 hasConceptScore W2977883715C121332964 @default.
- W2977883715 hasConceptScore W2977883715C133347239 @default.
- W2977883715 hasConceptScore W2977883715C147789679 @default.
- W2977883715 hasConceptScore W2977883715C148898269 @default.
- W2977883715 hasConceptScore W2977883715C161790260 @default.
- W2977883715 hasConceptScore W2977883715C175113610 @default.
- W2977883715 hasConceptScore W2977883715C178790620 @default.
- W2977883715 hasConceptScore W2977883715C179104552 @default.
- W2977883715 hasConceptScore W2977883715C185592680 @default.
- W2977883715 hasConceptScore W2977883715C192562407 @default.
- W2977883715 hasConceptScore W2977883715C36663273 @default.
- W2977883715 hasConceptScore W2977883715C515602321 @default.
- W2977883715 hasConceptScore W2977883715C55904794 @default.
- W2977883715 hasConceptScore W2977883715C60100273 @default.
- W2977883715 hasConceptScore W2977883715C62520636 @default.
- W2977883715 hasConceptScore W2977883715C93391505 @default.
- W2977883715 hasConceptScore W2977883715C95121573 @default.
- W2977883715 hasConceptScore W2977883715C97355855 @default.
- W2977883715 hasIssue "8" @default.
- W2977883715 hasLocation W29778837151 @default.
- W2977883715 hasOpenAccess W2977883715 @default.
- W2977883715 hasPrimaryLocation W29778837151 @default.
- W2977883715 hasRelatedWork W1965133032 @default.
- W2977883715 hasRelatedWork W2029929265 @default.
- W2977883715 hasRelatedWork W2031123321 @default.
- W2977883715 hasRelatedWork W2050790990 @default.
- W2977883715 hasRelatedWork W2075868440 @default.
- W2977883715 hasRelatedWork W2315750086 @default.
- W2977883715 hasRelatedWork W2350484167 @default.
- W2977883715 hasRelatedWork W2354653259 @default.
- W2977883715 hasRelatedWork W2356786937 @default.
- W2977883715 hasRelatedWork W2977883715 @default.
- W2977883715 hasVolume "32" @default.
- W2977883715 isParatext "false" @default.
- W2977883715 isRetracted "false" @default.
- W2977883715 magId "2977883715" @default.
- W2977883715 workType "article" @default.