- W2998448269 abstract "A simple one-step solventless in-situ reduction method was developed to prepare silver nanoparticle (AgNP) based polymer composites using different silver precursors and thermoplastic polymers. This method utilizes the mild reducing environment of thermoplastic polymer melts to convert silver precursors to AgNPs during the extrusion process. Complete reduction of Ag2O with broad AgNP size distribution (20 ± 18 nm) in polyamide 6 (PA6) was obtained after 5 min processing. For same matrix, the uniformity of AgNPs improved significantly after 10 min processing time, associated with a slight increase in the particle diameter (26 ± 9 nm). No significant impact of in-situ AgNP synthesis method on chemical and macromolecular characteristics of polyamide 6 was detected. When this method was used to synthesize AgNPs in polylactic acid and polypropylene, the influence of surface energy of polymer melt was evident. Reduction of Ag2O in polylactic acid (at 165 °C) was slower compared to PA6 and 95 ± 3% Ag2O reduction was achieved after 10 min of processing. When polypropylene was used as the matrix, only 60% reduction of Ag2O was achieved, possibly due to poor wetting of the silver precursor, owing to the low surface energy of polypropylene. AgNP-PA6 composites were also successfully prepared using Ag2CO3 and Ag-palmitate as precursors. To demonstrate the potential application of such composites in food packaging, the silver release and antibacterial activity of AgNP-PA6 composite were also studied. Though the composites released 500 times less silver compared to the permitted limits of different safety standards, they exhibited an excellent antibacterial activity against a typical food pathogen (Listeria monocytogenes) already at a low level of AgNP loading i.e. 0.5 wt%." @default.
- W2998448269 created "2020-01-10" @default.
- W2998448269 creator A5004170326 @default.
- W2998448269 creator A5010844954 @default.
- W2998448269 creator A5015623253 @default.
- W2998448269 creator A5016162911 @default.
- W2998448269 creator A5017619371 @default.
- W2998448269 creator A5017800446 @default.
- W2998448269 creator A5026919917 @default.
- W2998448269 creator A5029113146 @default.
- W2998448269 creator A5047907208 @default.
- W2998448269 creator A5060781584 @default.
- W2998448269 creator A5077428057 @default.
- W2998448269 date "2020-06-01" @default.
- W2998448269 modified "2023-10-12" @default.
- W2998448269 title "Polymer-assisted in-situ thermal reduction of silver precursors: A solventless route for silver nanoparticles-polymer composites" @default.
- W2998448269 cites W1487003624 @default.
- W2998448269 cites W1604779842 @default.
- W2998448269 cites W1966565115 @default.
- W2998448269 cites W1969347970 @default.
- W2998448269 cites W1969715566 @default.
- W2998448269 cites W1972127805 @default.
- W2998448269 cites W1973395616 @default.
- W2998448269 cites W1974618548 @default.
- W2998448269 cites W1975645292 @default.
- W2998448269 cites W1976624408 @default.
- W2998448269 cites W1977117500 @default.
- W2998448269 cites W1978814667 @default.
- W2998448269 cites W1984058967 @default.
- W2998448269 cites W1992707428 @default.
- W2998448269 cites W1995468808 @default.
- W2998448269 cites W2005460236 @default.
- W2998448269 cites W2006699019 @default.
- W2998448269 cites W2016401079 @default.
- W2998448269 cites W2024242353 @default.
- W2998448269 cites W2026239476 @default.
- W2998448269 cites W2028257185 @default.
- W2998448269 cites W2031610403 @default.
- W2998448269 cites W2032194447 @default.
- W2998448269 cites W2033342773 @default.
- W2998448269 cites W2034892108 @default.
- W2998448269 cites W2036352103 @default.
- W2998448269 cites W2037205172 @default.
- W2998448269 cites W2038975782 @default.
- W2998448269 cites W2042012727 @default.
- W2998448269 cites W2049833269 @default.
- W2998448269 cites W2062014510 @default.
- W2998448269 cites W2063369026 @default.
- W2998448269 cites W2065681623 @default.
- W2998448269 cites W2066087901 @default.
- W2998448269 cites W2067731923 @default.
- W2998448269 cites W2074323736 @default.
- W2998448269 cites W2075550184 @default.
- W2998448269 cites W2076033853 @default.
- W2998448269 cites W2076263143 @default.
- W2998448269 cites W2078308145 @default.
- W2998448269 cites W2081078405 @default.
- W2998448269 cites W2087715054 @default.
- W2998448269 cites W2095677666 @default.
- W2998448269 cites W2103283361 @default.
- W2998448269 cites W2104389112 @default.
- W2998448269 cites W2126153257 @default.
- W2998448269 cites W2153799777 @default.
- W2998448269 cites W2156242543 @default.
- W2998448269 cites W2158147221 @default.
- W2998448269 cites W2159497883 @default.
- W2998448269 cites W2161075122 @default.
- W2998448269 cites W2161477467 @default.
- W2998448269 cites W2220528754 @default.
- W2998448269 cites W2293323667 @default.
- W2998448269 cites W2312248536 @default.
- W2998448269 cites W2325859242 @default.
- W2998448269 cites W2332072634 @default.
- W2998448269 cites W2333032832 @default.
- W2998448269 cites W2334960539 @default.
- W2998448269 cites W2412120740 @default.
- W2998448269 cites W2416172820 @default.
- W2998448269 cites W2468056369 @default.
- W2998448269 cites W2496095656 @default.
- W2998448269 cites W2513459504 @default.
- W2998448269 cites W2519678626 @default.
- W2998448269 cites W2588006075 @default.
- W2998448269 cites W2606054929 @default.
- W2998448269 cites W2613112072 @default.
- W2998448269 cites W2625576589 @default.
- W2998448269 cites W2784103179 @default.
- W2998448269 cites W2803206884 @default.
- W2998448269 cites W2887736555 @default.
- W2998448269 cites W2892326645 @default.
- W2998448269 cites W2906942922 @default.
- W2998448269 cites W2910675290 @default.
- W2998448269 cites W2919617247 @default.
- W2998448269 cites W2968060816 @default.
- W2998448269 doi "https://doi.org/10.1016/j.cej.2019.123983" @default.
- W2998448269 hasPublicationYear "2020" @default.
- W2998448269 type Work @default.
- W2998448269 sameAs 2998448269 @default.
- W2998448269 citedByCount "25" @default.