- W3004289800 abstract "Limiting the cracking of gibbsites during calcination can reduce the content of ultrafine particles in the smelter grade alumina product and increase the quality of products. However, the investigation on the cracking behaviour and mechanism of gibbsites during calcination remains a challenge. In this study, we focus on the cracking behaviour and mechanism of gibbsite grain boundary during calcination. We first observe the cracking behaviour of the gibbsite grain boundary during calcination and propose a cracking mechanism. Based on the observed crack evolution at the gibbsite grain boundary, we found that the cracking of gibbsite grain boundary is initiated on the surface of particles, and then the cracks grow into the inner side of particles with the calcination. We also investigate the impact of the crystallite size and the c-axis angle between crystallites on gibbsite grain boundary. As a result, the increased crystallite size and the c-axis angle between crystallites can result in increased crack size at the gibbsite grain boundary." @default.
- W3004289800 created "2020-02-07" @default.
- W3004289800 creator A5022694204 @default.
- W3004289800 creator A5041714665 @default.
- W3004289800 creator A5057626290 @default.
- W3004289800 creator A5090437166 @default.
- W3004289800 date "2020-06-01" @default.
- W3004289800 modified "2023-09-24" @default.
- W3004289800 title "Cracking behaviour and mechanism at grain boundary of gibbsite during calcination" @default.
- W3004289800 cites W1522353651 @default.
- W3004289800 cites W1966087345 @default.
- W3004289800 cites W1969232676 @default.
- W3004289800 cites W1983315875 @default.
- W3004289800 cites W1984940592 @default.
- W3004289800 cites W1985721114 @default.
- W3004289800 cites W1996587875 @default.
- W3004289800 cites W2004730300 @default.
- W3004289800 cites W2024137321 @default.
- W3004289800 cites W2059341092 @default.
- W3004289800 cites W2059797366 @default.
- W3004289800 cites W2070739268 @default.
- W3004289800 cites W2090132888 @default.
- W3004289800 cites W2301116542 @default.
- W3004289800 cites W2345991166 @default.
- W3004289800 cites W2600160710 @default.
- W3004289800 cites W2753784616 @default.
- W3004289800 cites W499940 @default.
- W3004289800 doi "https://doi.org/10.1016/j.ceramint.2020.01.248" @default.
- W3004289800 hasPublicationYear "2020" @default.
- W3004289800 type Work @default.
- W3004289800 sameAs 3004289800 @default.
- W3004289800 citedByCount "1" @default.
- W3004289800 countsByYear W30042898002021 @default.
- W3004289800 crossrefType "journal-article" @default.
- W3004289800 hasAuthorship W3004289800A5022694204 @default.
- W3004289800 hasAuthorship W3004289800A5041714665 @default.
- W3004289800 hasAuthorship W3004289800A5057626290 @default.
- W3004289800 hasAuthorship W3004289800A5090437166 @default.
- W3004289800 hasConcept C10912530 @default.
- W3004289800 hasConcept C127313418 @default.
- W3004289800 hasConcept C127413603 @default.
- W3004289800 hasConcept C137637335 @default.
- W3004289800 hasConcept C159985019 @default.
- W3004289800 hasConcept C161790260 @default.
- W3004289800 hasConcept C185592680 @default.
- W3004289800 hasConcept C191897082 @default.
- W3004289800 hasConcept C192191005 @default.
- W3004289800 hasConcept C192562407 @default.
- W3004289800 hasConcept C199289684 @default.
- W3004289800 hasConcept C2777882336 @default.
- W3004289800 hasConcept C2777975867 @default.
- W3004289800 hasConcept C2779870107 @default.
- W3004289800 hasConcept C42360764 @default.
- W3004289800 hasConcept C47908070 @default.
- W3004289800 hasConcept C513153333 @default.
- W3004289800 hasConcept C55493867 @default.
- W3004289800 hasConcept C58396970 @default.
- W3004289800 hasConcept C7082614 @default.
- W3004289800 hasConcept C87976508 @default.
- W3004289800 hasConceptScore W3004289800C10912530 @default.
- W3004289800 hasConceptScore W3004289800C127313418 @default.
- W3004289800 hasConceptScore W3004289800C127413603 @default.
- W3004289800 hasConceptScore W3004289800C137637335 @default.
- W3004289800 hasConceptScore W3004289800C159985019 @default.
- W3004289800 hasConceptScore W3004289800C161790260 @default.
- W3004289800 hasConceptScore W3004289800C185592680 @default.
- W3004289800 hasConceptScore W3004289800C191897082 @default.
- W3004289800 hasConceptScore W3004289800C192191005 @default.
- W3004289800 hasConceptScore W3004289800C192562407 @default.
- W3004289800 hasConceptScore W3004289800C199289684 @default.
- W3004289800 hasConceptScore W3004289800C2777882336 @default.
- W3004289800 hasConceptScore W3004289800C2777975867 @default.
- W3004289800 hasConceptScore W3004289800C2779870107 @default.
- W3004289800 hasConceptScore W3004289800C42360764 @default.
- W3004289800 hasConceptScore W3004289800C47908070 @default.
- W3004289800 hasConceptScore W3004289800C513153333 @default.
- W3004289800 hasConceptScore W3004289800C55493867 @default.
- W3004289800 hasConceptScore W3004289800C58396970 @default.
- W3004289800 hasConceptScore W3004289800C7082614 @default.
- W3004289800 hasConceptScore W3004289800C87976508 @default.
- W3004289800 hasFunder F4320334704 @default.
- W3004289800 hasLocation W30042898001 @default.
- W3004289800 hasOpenAccess W3004289800 @default.
- W3004289800 hasPrimaryLocation W30042898001 @default.
- W3004289800 hasRelatedWork W10013341 @default.
- W3004289800 hasRelatedWork W10091306 @default.
- W3004289800 hasRelatedWork W19689190 @default.
- W3004289800 hasRelatedWork W21536868 @default.
- W3004289800 hasRelatedWork W26460239 @default.
- W3004289800 hasRelatedWork W41050844 @default.
- W3004289800 hasRelatedWork W50801648 @default.
- W3004289800 hasRelatedWork W6995036 @default.
- W3004289800 hasRelatedWork W7703722 @default.
- W3004289800 hasRelatedWork W45630297 @default.
- W3004289800 isParatext "false" @default.
- W3004289800 isRetracted "false" @default.
- W3004289800 magId "3004289800" @default.
- W3004289800 workType "article" @default.