- W3004936161 abstract "After failure of a refinery boiler, some cracks were detected in its tubes made of 2.25Cr-1Mo steel. The tubes were in the boiler superheater section. To determine causes of the cracking, samples were taken from the tubes, and different microscopical and analytical techniques such as scanning electron microscopy (SEM) and mechanical tests were used. Furthermore, finite element analysis (FEA) was used to evaluate the stress conditions in one of the cracked tubes. The results of analysis showed that the tube material was in accordance with the ASTM A213 chemical composition requirement however based on the calculated J-factor, the material was susceptible to temper embrittlement. The FEA results showed tensile residual stress formed at welding zone due to non-alignment before tubes welding. Considering the intergranular propagation of the cracks, the hardness of HAZ and other findings, it was concluded that stress corrosion cracking was the major damage mechanism." @default.
- W3004936161 created "2020-02-14" @default.
- W3004936161 creator A5001914347 @default.
- W3004936161 creator A5022515144 @default.
- W3004936161 creator A5042028317 @default.
- W3004936161 creator A5072299283 @default.
- W3004936161 date "2020-03-01" @default.
- W3004936161 modified "2023-10-14" @default.
- W3004936161 title "Failure analysis of cracked 2.25Cr–1.0Mo steel tubes of an oil refinery boiler" @default.
- W3004936161 cites W1963625216 @default.
- W3004936161 cites W1966448497 @default.
- W3004936161 cites W1986099584 @default.
- W3004936161 cites W1986930071 @default.
- W3004936161 cites W1990351643 @default.
- W3004936161 cites W2005493894 @default.
- W3004936161 cites W2006150854 @default.
- W3004936161 cites W2029566122 @default.
- W3004936161 cites W2043951383 @default.
- W3004936161 cites W2050409353 @default.
- W3004936161 cites W2066830803 @default.
- W3004936161 cites W2074974916 @default.
- W3004936161 cites W2086804203 @default.
- W3004936161 cites W2089017750 @default.
- W3004936161 cites W2375357175 @default.
- W3004936161 cites W2611169671 @default.
- W3004936161 cites W2613905162 @default.
- W3004936161 cites W2767224677 @default.
- W3004936161 cites W2883196013 @default.
- W3004936161 doi "https://doi.org/10.1016/j.engfailanal.2020.104435" @default.
- W3004936161 hasPublicationYear "2020" @default.
- W3004936161 type Work @default.
- W3004936161 sameAs 3004936161 @default.
- W3004936161 citedByCount "11" @default.
- W3004936161 countsByYear W30049361612021 @default.
- W3004936161 countsByYear W30049361612022 @default.
- W3004936161 countsByYear W30049361612023 @default.
- W3004936161 crossrefType "journal-article" @default.
- W3004936161 hasAuthorship W3004936161A5001914347 @default.
- W3004936161 hasAuthorship W3004936161A5022515144 @default.
- W3004936161 hasAuthorship W3004936161A5042028317 @default.
- W3004936161 hasAuthorship W3004936161A5072299283 @default.
- W3004936161 hasConcept C105168734 @default.
- W3004936161 hasConcept C127413603 @default.
- W3004936161 hasConcept C142282041 @default.
- W3004936161 hasConcept C159985019 @default.
- W3004936161 hasConcept C184102282 @default.
- W3004936161 hasConcept C191897082 @default.
- W3004936161 hasConcept C192562407 @default.
- W3004936161 hasConcept C19474535 @default.
- W3004936161 hasConcept C20625102 @default.
- W3004936161 hasConcept C2778760603 @default.
- W3004936161 hasConcept C2780013297 @default.
- W3004936161 hasConcept C37292000 @default.
- W3004936161 hasConcept C47561241 @default.
- W3004936161 hasConcept C548081761 @default.
- W3004936161 hasConcept C58396970 @default.
- W3004936161 hasConceptScore W3004936161C105168734 @default.
- W3004936161 hasConceptScore W3004936161C127413603 @default.
- W3004936161 hasConceptScore W3004936161C142282041 @default.
- W3004936161 hasConceptScore W3004936161C159985019 @default.
- W3004936161 hasConceptScore W3004936161C184102282 @default.
- W3004936161 hasConceptScore W3004936161C191897082 @default.
- W3004936161 hasConceptScore W3004936161C192562407 @default.
- W3004936161 hasConceptScore W3004936161C19474535 @default.
- W3004936161 hasConceptScore W3004936161C20625102 @default.
- W3004936161 hasConceptScore W3004936161C2778760603 @default.
- W3004936161 hasConceptScore W3004936161C2780013297 @default.
- W3004936161 hasConceptScore W3004936161C37292000 @default.
- W3004936161 hasConceptScore W3004936161C47561241 @default.
- W3004936161 hasConceptScore W3004936161C548081761 @default.
- W3004936161 hasConceptScore W3004936161C58396970 @default.
- W3004936161 hasLocation W30049361611 @default.
- W3004936161 hasOpenAccess W3004936161 @default.
- W3004936161 hasPrimaryLocation W30049361611 @default.
- W3004936161 hasRelatedWork W132565280 @default.
- W3004936161 hasRelatedWork W2041097107 @default.
- W3004936161 hasRelatedWork W2062700662 @default.
- W3004936161 hasRelatedWork W2230276082 @default.
- W3004936161 hasRelatedWork W2252958172 @default.
- W3004936161 hasRelatedWork W2507498813 @default.
- W3004936161 hasRelatedWork W2609467133 @default.
- W3004936161 hasRelatedWork W4241719453 @default.
- W3004936161 hasRelatedWork W815299756 @default.
- W3004936161 hasRelatedWork W1571280065 @default.
- W3004936161 hasVolume "110" @default.
- W3004936161 isParatext "false" @default.
- W3004936161 isRetracted "false" @default.
- W3004936161 magId "3004936161" @default.
- W3004936161 workType "article" @default.