- W3007404895 abstract "Abstract To protect operators of equipment using neutron radiation, an alternative material is needed as a neutron shielding which is lightweight and has a high neutron absorption. One alternative material that can be used is wood dust. In this study pure wood sawdust and 30% borax-wood composites were investigated as alternatives to shielding neutrons. Mixing wood sawdust and borax was done using HEM (High Energy Milling) for 1 hour, then pressed at 2000 Psi using a manual press with variations in thickness of 5 mm, 10 mm, 15 mm and 20 mm. SEM characterization results show, the grain size of wood in pure wood and 30% boraxwood composites is still quite large around 50 μm, the EDS results show no significant difference in wood content and 30% borax-wood composites. XRD characterization results showed no new phases were formed in the 30% borax-wood composite. The results of observations with optical microscopy showed that 30% borax-wood composite which were compressed did not form pores but were not evenly distributed. From the compressive test data, there was a decrease in the compressive ability of 30% borax-wood composites compared to pure wood dust from 226.6 N to 110.4 N. The neutron absorption test results using the Neutron Radiography technique with the film technique showed the addition of 30% borax to sawdust increased the neutron absorption rate by an average of 19.05% in wood to 20.24% in 30% borax-wood composites and increased the attenuation coefficient of 0.36 cm· in pure wood to 0.53 cm 1 in 30% borax-wood composite." @default.
- W3007404895 created "2020-03-06" @default.
- W3007404895 creator A5027569226 @default.
- W3007404895 creator A5041611952 @default.
- W3007404895 creator A5049118856 @default.
- W3007404895 creator A5074141738 @default.
- W3007404895 date "2020-01-01" @default.
- W3007404895 modified "2023-10-14" @default.
- W3007404895 title "Characterization of wood-borax composites as alternative neutron shielding material using neutron radiography techniques" @default.
- W3007404895 doi "https://doi.org/10.1088/1742-6596/1436/1/012080" @default.
- W3007404895 hasPublicationYear "2020" @default.
- W3007404895 type Work @default.
- W3007404895 sameAs 3007404895 @default.
- W3007404895 citedByCount "1" @default.
- W3007404895 countsByYear W30074048952022 @default.
- W3007404895 crossrefType "journal-article" @default.
- W3007404895 hasAuthorship W3007404895A5027569226 @default.
- W3007404895 hasAuthorship W3007404895A5041611952 @default.
- W3007404895 hasAuthorship W3007404895A5049118856 @default.
- W3007404895 hasAuthorship W3007404895A5074141738 @default.
- W3007404895 hasBestOaLocation W30074048951 @default.
- W3007404895 hasConcept C104779481 @default.
- W3007404895 hasConcept C120665830 @default.
- W3007404895 hasConcept C121332964 @default.
- W3007404895 hasConcept C127413603 @default.
- W3007404895 hasConcept C142923127 @default.
- W3007404895 hasConcept C152568617 @default.
- W3007404895 hasConcept C159774933 @default.
- W3007404895 hasConcept C159985019 @default.
- W3007404895 hasConcept C178790620 @default.
- W3007404895 hasConcept C185592680 @default.
- W3007404895 hasConcept C192562407 @default.
- W3007404895 hasConcept C206139338 @default.
- W3007404895 hasConcept C27251351 @default.
- W3007404895 hasConcept C2777264276 @default.
- W3007404895 hasConcept C2780308376 @default.
- W3007404895 hasConcept C30407753 @default.
- W3007404895 hasConcept C30421969 @default.
- W3007404895 hasConcept C528095902 @default.
- W3007404895 hasConcept C62520636 @default.
- W3007404895 hasConceptScore W3007404895C104779481 @default.
- W3007404895 hasConceptScore W3007404895C120665830 @default.
- W3007404895 hasConceptScore W3007404895C121332964 @default.
- W3007404895 hasConceptScore W3007404895C127413603 @default.
- W3007404895 hasConceptScore W3007404895C142923127 @default.
- W3007404895 hasConceptScore W3007404895C152568617 @default.
- W3007404895 hasConceptScore W3007404895C159774933 @default.
- W3007404895 hasConceptScore W3007404895C159985019 @default.
- W3007404895 hasConceptScore W3007404895C178790620 @default.
- W3007404895 hasConceptScore W3007404895C185592680 @default.
- W3007404895 hasConceptScore W3007404895C192562407 @default.
- W3007404895 hasConceptScore W3007404895C206139338 @default.
- W3007404895 hasConceptScore W3007404895C27251351 @default.
- W3007404895 hasConceptScore W3007404895C2777264276 @default.
- W3007404895 hasConceptScore W3007404895C2780308376 @default.
- W3007404895 hasConceptScore W3007404895C30407753 @default.
- W3007404895 hasConceptScore W3007404895C30421969 @default.
- W3007404895 hasConceptScore W3007404895C528095902 @default.
- W3007404895 hasConceptScore W3007404895C62520636 @default.
- W3007404895 hasIssue "1" @default.
- W3007404895 hasLocation W30074048951 @default.
- W3007404895 hasOpenAccess W3007404895 @default.
- W3007404895 hasPrimaryLocation W30074048951 @default.
- W3007404895 hasRelatedWork W2030968263 @default.
- W3007404895 hasRelatedWork W2043177031 @default.
- W3007404895 hasRelatedWork W2073095088 @default.
- W3007404895 hasRelatedWork W2698765881 @default.
- W3007404895 hasRelatedWork W2793773039 @default.
- W3007404895 hasRelatedWork W3007404895 @default.
- W3007404895 hasRelatedWork W3098906441 @default.
- W3007404895 hasRelatedWork W3099073920 @default.
- W3007404895 hasRelatedWork W3104847889 @default.
- W3007404895 hasRelatedWork W4220975215 @default.
- W3007404895 hasVolume "1436" @default.
- W3007404895 isParatext "false" @default.
- W3007404895 isRetracted "false" @default.
- W3007404895 magId "3007404895" @default.
- W3007404895 workType "article" @default.