- W3008557537 abstract "Composite ceramic cores reinforced by different contents of mullite fibers were prepared via injection molding. With increasing mullite fibers, the porosity showed near-exponential increase due to the accumulation of fibers, and the leaching rate showed the similar tendency attributed to the increasing porosity for the permeation of alkali solution. At room temperature or 1550 °C, the flexural strength increased as the fibers contents were below 3 wt%, due to the micro-cracking and fiber extraction; however, the flexural strength degraded as the mullite fibers contents was 4 wt%, due to the high porosity. Compared to the others, the ceramic cores with 3 wt% mullite fibers showed excellent properties, including apparent porosity of 35.2%, linear shrinkage of 0.81%, flexural strength being 25.5 MPa at room temperature and 22.3 MPa at 1550 °C, creep deformation of 0.12 mm and leaching rate of 0.34 g/min, well meeting the demands of hollow blades casting. This paper may provide new guidance for high-property ceramic cores." @default.
- W3008557537 created "2020-03-06" @default.
- W3008557537 creator A5005929195 @default.
- W3008557537 creator A5022526821 @default.
- W3008557537 creator A5057985269 @default.
- W3008557537 creator A5064910189 @default.
- W3008557537 creator A5088005868 @default.
- W3008557537 date "2020-07-01" @default.
- W3008557537 modified "2023-10-18" @default.
- W3008557537 title "Microstructure evolution and properties of silica-based ceramic cores reinforced by mullite fibers" @default.
- W3008557537 cites W1969191356 @default.
- W3008557537 cites W1969558281 @default.
- W3008557537 cites W2010752427 @default.
- W3008557537 cites W2015959829 @default.
- W3008557537 cites W2029985710 @default.
- W3008557537 cites W2056503020 @default.
- W3008557537 cites W2078199126 @default.
- W3008557537 cites W2120427003 @default.
- W3008557537 cites W2281980189 @default.
- W3008557537 cites W2286583847 @default.
- W3008557537 cites W2286879068 @default.
- W3008557537 cites W2468337775 @default.
- W3008557537 cites W2549122938 @default.
- W3008557537 cites W2575854210 @default.
- W3008557537 cites W2604692041 @default.
- W3008557537 cites W2756266072 @default.
- W3008557537 cites W2759154781 @default.
- W3008557537 cites W2794803194 @default.
- W3008557537 cites W2803894133 @default.
- W3008557537 cites W2883990451 @default.
- W3008557537 cites W2891107209 @default.
- W3008557537 cites W67926984 @default.
- W3008557537 doi "https://doi.org/10.1016/j.jallcom.2020.154494" @default.
- W3008557537 hasPublicationYear "2020" @default.
- W3008557537 type Work @default.
- W3008557537 sameAs 3008557537 @default.
- W3008557537 citedByCount "28" @default.
- W3008557537 countsByYear W30085575372020 @default.
- W3008557537 countsByYear W30085575372021 @default.
- W3008557537 countsByYear W30085575372022 @default.
- W3008557537 countsByYear W30085575372023 @default.
- W3008557537 crossrefType "journal-article" @default.
- W3008557537 hasAuthorship W3008557537A5005929195 @default.
- W3008557537 hasAuthorship W3008557537A5022526821 @default.
- W3008557537 hasAuthorship W3008557537A5057985269 @default.
- W3008557537 hasAuthorship W3008557537A5064910189 @default.
- W3008557537 hasAuthorship W3008557537A5088005868 @default.
- W3008557537 hasConcept C134132462 @default.
- W3008557537 hasConcept C159985019 @default.
- W3008557537 hasConcept C178405089 @default.
- W3008557537 hasConcept C180145272 @default.
- W3008557537 hasConcept C192562407 @default.
- W3008557537 hasConcept C2781436864 @default.
- W3008557537 hasConcept C519885992 @default.
- W3008557537 hasConcept C6648577 @default.
- W3008557537 hasConcept C67558686 @default.
- W3008557537 hasConcept C87976508 @default.
- W3008557537 hasConceptScore W3008557537C134132462 @default.
- W3008557537 hasConceptScore W3008557537C159985019 @default.
- W3008557537 hasConceptScore W3008557537C178405089 @default.
- W3008557537 hasConceptScore W3008557537C180145272 @default.
- W3008557537 hasConceptScore W3008557537C192562407 @default.
- W3008557537 hasConceptScore W3008557537C2781436864 @default.
- W3008557537 hasConceptScore W3008557537C519885992 @default.
- W3008557537 hasConceptScore W3008557537C6648577 @default.
- W3008557537 hasConceptScore W3008557537C67558686 @default.
- W3008557537 hasConceptScore W3008557537C87976508 @default.
- W3008557537 hasFunder F4320324173 @default.
- W3008557537 hasFunder F4320335787 @default.
- W3008557537 hasLocation W30085575371 @default.
- W3008557537 hasOpenAccess W3008557537 @default.
- W3008557537 hasPrimaryLocation W30085575371 @default.
- W3008557537 hasRelatedWork W2000378395 @default.
- W3008557537 hasRelatedWork W2000721444 @default.
- W3008557537 hasRelatedWork W2004850945 @default.
- W3008557537 hasRelatedWork W2055916914 @default.
- W3008557537 hasRelatedWork W2074697892 @default.
- W3008557537 hasRelatedWork W2075580692 @default.
- W3008557537 hasRelatedWork W2352860339 @default.
- W3008557537 hasRelatedWork W2366934632 @default.
- W3008557537 hasRelatedWork W2371400253 @default.
- W3008557537 hasRelatedWork W2383728625 @default.
- W3008557537 hasVolume "829" @default.
- W3008557537 isParatext "false" @default.
- W3008557537 isRetracted "false" @default.
- W3008557537 magId "3008557537" @default.
- W3008557537 workType "article" @default.