- W3011189724 abstract "Abstract Electrodeposition of Sn within porous anodic aluminum oxide (AAO) template was used to synthesize Sn nanowires. Ag seed layer was sputtered upon AAO template firstly, then the Sn nanowires were electroplated upon the seed layer. After electrodeposition the Ag seed layer was removed and the AAO template was dissolved in order to obtain Sn nanowires finally. The diameter of Sn nanowires was about 200 nm, being consistent with the template pore size, while the length of nanowires had a linear growth rate of approximately 2.49 μm/min. X-ray diffraction (XRD) and electron diffraction revealed that individual Sn nanowire was single crystal without preferential growth direction. The surface of the nanowire was wrapped by a thin SnO film (~5 nm thick), as verified by transmission electron microscopy (TEM) observation and X-ray photoelectron spectrometer (XPS) analyses. The synthesized Sn nanowire powders had a dark brown color, which comes from the surface SnO layer. Through the differential scanning calorimetry (DSC) analysis, the melting point of Sn nanowires was determined as 231.73 °C, which is about 2.7% lower than the pure Sn particles. Fabrication of Sn nanosolders from Sn nanowires was tried using liquid bath melting method. It was found that Sn nanowires could convert into spheroidal nanosolder in liquid paraffin, which demonstrated a novel technology to fabricate nanosolders used for nanoscale interconnections." @default.
- W3011189724 created "2020-03-23" @default.
- W3011189724 creator A5004449255 @default.
- W3011189724 creator A5051246236 @default.
- W3011189724 creator A5067829822 @default.
- W3011189724 date "2020-05-01" @default.
- W3011189724 modified "2023-10-12" @default.
- W3011189724 title "Synthesis of Sn nanowire by template electrodeposition and its conversion into Sn nanosolder" @default.
- W3011189724 cites W1885097981 @default.
- W3011189724 cites W1964920066 @default.
- W3011189724 cites W1974448790 @default.
- W3011189724 cites W1975527883 @default.
- W3011189724 cites W1987004587 @default.
- W3011189724 cites W1991527849 @default.
- W3011189724 cites W2001838538 @default.
- W3011189724 cites W2008281021 @default.
- W3011189724 cites W2022951513 @default.
- W3011189724 cites W2052368681 @default.
- W3011189724 cites W2061406131 @default.
- W3011189724 cites W2067514391 @default.
- W3011189724 cites W2070267584 @default.
- W3011189724 cites W2080866433 @default.
- W3011189724 cites W2126775683 @default.
- W3011189724 cites W2147949334 @default.
- W3011189724 cites W2328353762 @default.
- W3011189724 cites W2332189281 @default.
- W3011189724 cites W2492045251 @default.
- W3011189724 cites W2560753505 @default.
- W3011189724 cites W2564019181 @default.
- W3011189724 cites W2565599824 @default.
- W3011189724 cites W2613285647 @default.
- W3011189724 cites W2762524648 @default.
- W3011189724 cites W2787942241 @default.
- W3011189724 cites W2801373848 @default.
- W3011189724 cites W2803331352 @default.
- W3011189724 cites W2809077969 @default.
- W3011189724 cites W2903901817 @default.
- W3011189724 cites W2903956188 @default.
- W3011189724 cites W2991601008 @default.
- W3011189724 doi "https://doi.org/10.1016/j.matchar.2020.110278" @default.
- W3011189724 hasPublicationYear "2020" @default.
- W3011189724 type Work @default.
- W3011189724 sameAs 3011189724 @default.
- W3011189724 citedByCount "8" @default.
- W3011189724 countsByYear W30111897242021 @default.
- W3011189724 countsByYear W30111897242022 @default.
- W3011189724 countsByYear W30111897242023 @default.
- W3011189724 crossrefType "journal-article" @default.
- W3011189724 hasAuthorship W3011189724A5004449255 @default.
- W3011189724 hasAuthorship W3011189724A5051246236 @default.
- W3011189724 hasAuthorship W3011189724A5067829822 @default.
- W3011189724 hasBestOaLocation W30111897241 @default.
- W3011189724 hasConcept C127413603 @default.
- W3011189724 hasConcept C171250308 @default.
- W3011189724 hasConcept C191897082 @default.
- W3011189724 hasConcept C192562407 @default.
- W3011189724 hasConcept C42360764 @default.
- W3011189724 hasConcept C74214498 @default.
- W3011189724 hasConceptScore W3011189724C127413603 @default.
- W3011189724 hasConceptScore W3011189724C171250308 @default.
- W3011189724 hasConceptScore W3011189724C191897082 @default.
- W3011189724 hasConceptScore W3011189724C192562407 @default.
- W3011189724 hasConceptScore W3011189724C42360764 @default.
- W3011189724 hasConceptScore W3011189724C74214498 @default.
- W3011189724 hasFunder F4320327511 @default.
- W3011189724 hasFunder F4320335777 @default.
- W3011189724 hasLocation W30111897241 @default.
- W3011189724 hasOpenAccess W3011189724 @default.
- W3011189724 hasPrimaryLocation W30111897241 @default.
- W3011189724 hasRelatedWork W1966077344 @default.
- W3011189724 hasRelatedWork W1996409043 @default.
- W3011189724 hasRelatedWork W2052264804 @default.
- W3011189724 hasRelatedWork W2055171879 @default.
- W3011189724 hasRelatedWork W2064285767 @default.
- W3011189724 hasRelatedWork W2312373875 @default.
- W3011189724 hasRelatedWork W2315812898 @default.
- W3011189724 hasRelatedWork W2738025024 @default.
- W3011189724 hasRelatedWork W3111646793 @default.
- W3011189724 hasRelatedWork W833304027 @default.
- W3011189724 hasVolume "163" @default.
- W3011189724 isParatext "false" @default.
- W3011189724 isRetracted "false" @default.
- W3011189724 magId "3011189724" @default.
- W3011189724 workType "article" @default.