- W3011323209 abstract "A series of (TiNbZrTa)Nx coatings with a thickness of ~1.1 μm were deposited using reactive magnetron sputtering with segmented targets. The deposition temperature was varied from room temperature to 700 °C resulting in coatings with different microstructures. The coatings were characterized by electron microscopy, atomic force microscopy, compositional analysis, and X-ray diffraction. Effects of the deposition temperature on the electrical, mechanical and corrosion properties were studied with four-point probe, nanoindentation and potentiodynamic polarization measurements, respectively. X-ray photoelectron spectroscopy (XPS) analyses reveal a gradual change in the chemical state of all elements with increasing growth temperature from nitridic at room temperature to metallic at 700 °C. A NaCl-type structure with (001) preferred orientation was observed in the coating deposited at 400 °C, while an hcp structure was found for the coatings deposited above 400 °C. The resistivities of the TiNbZrTa nitride coatings were found to be around 200 μΩcm. In 0.1 M H2SO4 aqueous solution, a corrosion current density of 2.8 × 10−8 A/cm2 and a passive behaviour up to 1.5 V vs. Ag/AgCl were found for the most corrosion resistant coating. The latter corrosion current is about two orders of magnitude lower than that found for a reference hyper-duplex stainless steel." @default.
- W3011323209 created "2020-03-23" @default.
- W3011323209 creator A5020723421 @default.
- W3011323209 creator A5035823261 @default.
- W3011323209 creator A5036498106 @default.
- W3011323209 creator A5044791400 @default.
- W3011323209 creator A5048978284 @default.
- W3011323209 creator A5058652933 @default.
- W3011323209 creator A5065384023 @default.
- W3011323209 creator A5070827561 @default.
- W3011323209 creator A5072094182 @default.
- W3011323209 date "2020-05-01" @default.
- W3011323209 modified "2023-10-18" @default.
- W3011323209 title "Microstructure and mechanical, electrical, and electrochemical properties of sputter-deposited multicomponent (TiNbZrTa)Nx coatings" @default.
- W3011323209 cites W1231284236 @default.
- W3011323209 cites W1968584854 @default.
- W3011323209 cites W1981966175 @default.
- W3011323209 cites W1987587376 @default.
- W3011323209 cites W1991417089 @default.
- W3011323209 cites W1991897258 @default.
- W3011323209 cites W2002468578 @default.
- W3011323209 cites W2003975937 @default.
- W3011323209 cites W2004661440 @default.
- W3011323209 cites W2009642697 @default.
- W3011323209 cites W2012192823 @default.
- W3011323209 cites W2019736948 @default.
- W3011323209 cites W2020622168 @default.
- W3011323209 cites W2026913983 @default.
- W3011323209 cites W2033957529 @default.
- W3011323209 cites W2034781296 @default.
- W3011323209 cites W2035620986 @default.
- W3011323209 cites W2044540034 @default.
- W3011323209 cites W2052018997 @default.
- W3011323209 cites W2058085399 @default.
- W3011323209 cites W2058979314 @default.
- W3011323209 cites W2065586390 @default.
- W3011323209 cites W2073134589 @default.
- W3011323209 cites W2076104250 @default.
- W3011323209 cites W2082299438 @default.
- W3011323209 cites W2086933933 @default.
- W3011323209 cites W2114544041 @default.
- W3011323209 cites W2126044579 @default.
- W3011323209 cites W2152773302 @default.
- W3011323209 cites W2223161771 @default.
- W3011323209 cites W2321460008 @default.
- W3011323209 cites W2344431215 @default.
- W3011323209 cites W2533482753 @default.
- W3011323209 cites W2734406264 @default.
- W3011323209 cites W2763956865 @default.
- W3011323209 cites W2787946967 @default.
- W3011323209 cites W2791480408 @default.
- W3011323209 cites W2794777979 @default.
- W3011323209 cites W2795548981 @default.
- W3011323209 cites W2799442935 @default.
- W3011323209 cites W2807029607 @default.
- W3011323209 cites W2809658428 @default.
- W3011323209 cites W2887957914 @default.
- W3011323209 cites W2888692443 @default.
- W3011323209 cites W2888982575 @default.
- W3011323209 cites W2901546241 @default.
- W3011323209 cites W2905011582 @default.
- W3011323209 cites W2954539755 @default.
- W3011323209 cites W2965295081 @default.
- W3011323209 doi "https://doi.org/10.1016/j.surfcoat.2020.125651" @default.
- W3011323209 hasPublicationYear "2020" @default.
- W3011323209 type Work @default.
- W3011323209 sameAs 3011323209 @default.
- W3011323209 citedByCount "29" @default.
- W3011323209 countsByYear W30113232092020 @default.
- W3011323209 countsByYear W30113232092021 @default.
- W3011323209 countsByYear W30113232092022 @default.
- W3011323209 countsByYear W30113232092023 @default.
- W3011323209 crossrefType "journal-article" @default.
- W3011323209 hasAuthorship W3011323209A5020723421 @default.
- W3011323209 hasAuthorship W3011323209A5035823261 @default.
- W3011323209 hasAuthorship W3011323209A5036498106 @default.
- W3011323209 hasAuthorship W3011323209A5044791400 @default.
- W3011323209 hasAuthorship W3011323209A5048978284 @default.
- W3011323209 hasAuthorship W3011323209A5058652933 @default.
- W3011323209 hasAuthorship W3011323209A5065384023 @default.
- W3011323209 hasAuthorship W3011323209A5070827561 @default.
- W3011323209 hasAuthorship W3011323209A5072094182 @default.
- W3011323209 hasBestOaLocation W30113232091 @default.
- W3011323209 hasConcept C113196181 @default.
- W3011323209 hasConcept C127413603 @default.
- W3011323209 hasConcept C159985019 @default.
- W3011323209 hasConcept C171250308 @default.
- W3011323209 hasConcept C175708663 @default.
- W3011323209 hasConcept C185592680 @default.
- W3011323209 hasConcept C19067145 @default.
- W3011323209 hasConcept C191897082 @default.
- W3011323209 hasConcept C192562407 @default.
- W3011323209 hasConcept C20625102 @default.
- W3011323209 hasConcept C22423302 @default.
- W3011323209 hasConcept C26771246 @default.
- W3011323209 hasConcept C2781448156 @default.
- W3011323209 hasConcept C42360764 @default.
- W3011323209 hasConcept C43617362 @default.