- W3011330341 abstract "Abstract This work reports a quantitative evaluation of the aging behavior of adhesively bonded joints manufactured using a toughened epoxy adhesive applied on CFRP substrates. Low-pressure plasma (LPP) treatment was employed, adopting air and pure oxygen as process gases and varying working parameters such as power and exposure time. A preliminary testing campaign was performed under standard laboratory conditions to evaluate shear strength of single-lap joints (SLJ), comparing effectiveness of LPP treatments to a traditional mechanical abrasion of the adherends. Even at this early stage, experimental findings highlighted how this physical method provides for competitive performance over abrasion, resulting in a remarkable enhancement of the shear resistance. Four sets of LPP-treatment conditions were selected and then subjected to accelerated aging (consisting of 56 cycles of 5 h at T = 70 °C, RH>90% and 5 h at T = −40 °C each). Their behavior was compared to that of abraded joints, employed as a reference. To assess the durability of the CFRP-epoxy adhesive system under accelerated aging conditions, tensile shear strength (TSS) testing and wedge cleavage test (WT) were performed in parallel. The experimental results showed that low-pressure plasma treatment of the CFRP substrates results in increased short-term quality of the adhesive joint as well as in enhancement of its durability even under severe aging conditions." @default.
- W3011330341 created "2020-03-23" @default.
- W3011330341 creator A5010537915 @default.
- W3011330341 creator A5050180501 @default.
- W3011330341 creator A5059220903 @default.
- W3011330341 date "2020-06-01" @default.
- W3011330341 modified "2023-10-03" @default.
- W3011330341 title "Low pressure plasma treatment of CFRP substrates for adhesive bonding: an investigation of joint durability under severe temperature-moisture conditioning" @default.
- W3011330341 cites W1144291066 @default.
- W3011330341 cites W1964981678 @default.
- W3011330341 cites W1970536145 @default.
- W3011330341 cites W2000999524 @default.
- W3011330341 cites W2005727049 @default.
- W3011330341 cites W2029348344 @default.
- W3011330341 cites W2074394538 @default.
- W3011330341 cites W2083641402 @default.
- W3011330341 cites W2109908310 @default.
- W3011330341 cites W2283849513 @default.
- W3011330341 cites W2533679207 @default.
- W3011330341 cites W2588814705 @default.
- W3011330341 cites W2592605268 @default.
- W3011330341 cites W2604158947 @default.
- W3011330341 cites W2886781678 @default.
- W3011330341 cites W2913864376 @default.
- W3011330341 doi "https://doi.org/10.1016/j.ijadhadh.2020.102592" @default.
- W3011330341 hasPublicationYear "2020" @default.
- W3011330341 type Work @default.
- W3011330341 sameAs 3011330341 @default.
- W3011330341 citedByCount "15" @default.
- W3011330341 countsByYear W30113303412021 @default.
- W3011330341 countsByYear W30113303412022 @default.
- W3011330341 countsByYear W30113303412023 @default.
- W3011330341 crossrefType "journal-article" @default.
- W3011330341 hasAuthorship W3011330341A5010537915 @default.
- W3011330341 hasAuthorship W3011330341A5050180501 @default.
- W3011330341 hasAuthorship W3011330341A5059220903 @default.
- W3011330341 hasConcept C104304963 @default.
- W3011330341 hasConcept C105795698 @default.
- W3011330341 hasConcept C127413603 @default.
- W3011330341 hasConcept C159985019 @default.
- W3011330341 hasConcept C176864760 @default.
- W3011330341 hasConcept C18555067 @default.
- W3011330341 hasConcept C192562407 @default.
- W3011330341 hasConcept C2779227376 @default.
- W3011330341 hasConcept C2779278059 @default.
- W3011330341 hasConcept C33923547 @default.
- W3011330341 hasConcept C45262634 @default.
- W3011330341 hasConcept C66938386 @default.
- W3011330341 hasConcept C68928338 @default.
- W3011330341 hasConceptScore W3011330341C104304963 @default.
- W3011330341 hasConceptScore W3011330341C105795698 @default.
- W3011330341 hasConceptScore W3011330341C127413603 @default.
- W3011330341 hasConceptScore W3011330341C159985019 @default.
- W3011330341 hasConceptScore W3011330341C176864760 @default.
- W3011330341 hasConceptScore W3011330341C18555067 @default.
- W3011330341 hasConceptScore W3011330341C192562407 @default.
- W3011330341 hasConceptScore W3011330341C2779227376 @default.
- W3011330341 hasConceptScore W3011330341C2779278059 @default.
- W3011330341 hasConceptScore W3011330341C33923547 @default.
- W3011330341 hasConceptScore W3011330341C45262634 @default.
- W3011330341 hasConceptScore W3011330341C66938386 @default.
- W3011330341 hasConceptScore W3011330341C68928338 @default.
- W3011330341 hasLocation W30113303411 @default.
- W3011330341 hasOpenAccess W3011330341 @default.
- W3011330341 hasPrimaryLocation W30113303411 @default.
- W3011330341 hasRelatedWork W139341264 @default.
- W3011330341 hasRelatedWork W1967613293 @default.
- W3011330341 hasRelatedWork W2042445919 @default.
- W3011330341 hasRelatedWork W2061712488 @default.
- W3011330341 hasRelatedWork W2062276134 @default.
- W3011330341 hasRelatedWork W2076361664 @default.
- W3011330341 hasRelatedWork W2366970374 @default.
- W3011330341 hasRelatedWork W3011330341 @default.
- W3011330341 hasRelatedWork W3089904018 @default.
- W3011330341 hasRelatedWork W4232026772 @default.
- W3011330341 hasVolume "99" @default.
- W3011330341 isParatext "false" @default.
- W3011330341 isRetracted "false" @default.
- W3011330341 magId "3011330341" @default.
- W3011330341 workType "article" @default.