- W3014560752 abstract "Flame spray technique with nitrogen pressure was used to deposit FeCrAlTiY-30 mass% CoNiCrAlY coating on the surface of low carbon steel. The resistance of the sample against oxidation and corrosion at high temperature was studied cyclically at 700°C for 8 times. The sample was rapidly heated in a furnace at 700°C for 20 hours and then cooled for 4 hours at room temperature. XRD and SEM-EDX were used to investigate the phase composition and morphologies of the coating before and after high temperature oxidation and corrosion test. For corrosion evaluation, the test samples was sprayed using 20 mass% NaCl solution. After the test, it was found that the flame sprayed FeCrAlTiY-30 mass% CoNiCrAlY coating with N2 pressure effectively enhances the resistance of carbon steel toward oxidation and corrosion at high temperature due to the formation of FeCr, Fe2O3, Al2O3, (Ni,Co)Cr2O4 and Al2O3, Fe2O3, Fe(Cr, Al)2O4, respectively. On the contrary, the coating was degraded more easily in 20 mass% NaCl containing atmosphere than in air atmosphere, suggesting that the corrosion attack is more severe than oxidation." @default.
- W3014560752 created "2020-04-10" @default.
- W3014560752 creator A5017728774 @default.
- W3014560752 creator A5029475503 @default.
- W3014560752 creator A5048167546 @default.
- W3014560752 creator A5048668123 @default.
- W3014560752 creator A5061360860 @default.
- W3014560752 creator A5088449924 @default.
- W3014560752 date "2020-01-01" @default.
- W3014560752 modified "2023-10-11" @default.
- W3014560752 title "Improvement of carbon steel resistance against high temperature oxidation and corrosion by flame sprayed FeCrAlTiY-30 mass% CoNiCrAlY coating using N2 pressure" @default.
- W3014560752 cites W1972296813 @default.
- W3014560752 cites W1973849205 @default.
- W3014560752 cites W2007733444 @default.
- W3014560752 cites W2018470554 @default.
- W3014560752 cites W2026197334 @default.
- W3014560752 cites W2031483629 @default.
- W3014560752 cites W2508905825 @default.
- W3014560752 cites W2590515324 @default.
- W3014560752 cites W2742263220 @default.
- W3014560752 cites W2766215951 @default.
- W3014560752 cites W2880218763 @default.
- W3014560752 cites W2936845439 @default.
- W3014560752 doi "https://doi.org/10.1063/5.0003155" @default.
- W3014560752 hasPublicationYear "2020" @default.
- W3014560752 type Work @default.
- W3014560752 sameAs 3014560752 @default.
- W3014560752 citedByCount "0" @default.
- W3014560752 crossrefType "proceedings-article" @default.
- W3014560752 hasAuthorship W3014560752A5017728774 @default.
- W3014560752 hasAuthorship W3014560752A5029475503 @default.
- W3014560752 hasAuthorship W3014560752A5048167546 @default.
- W3014560752 hasAuthorship W3014560752A5048668123 @default.
- W3014560752 hasAuthorship W3014560752A5061360860 @default.
- W3014560752 hasAuthorship W3014560752A5088449924 @default.
- W3014560752 hasBestOaLocation W30145607521 @default.
- W3014560752 hasConcept C104779481 @default.
- W3014560752 hasConcept C140205800 @default.
- W3014560752 hasConcept C149669645 @default.
- W3014560752 hasConcept C159985019 @default.
- W3014560752 hasConcept C178790620 @default.
- W3014560752 hasConcept C185592680 @default.
- W3014560752 hasConcept C191897082 @default.
- W3014560752 hasConcept C192562407 @default.
- W3014560752 hasConcept C20625102 @default.
- W3014560752 hasConcept C2778560533 @default.
- W3014560752 hasConcept C2781099003 @default.
- W3014560752 hasConcept C2781448156 @default.
- W3014560752 hasConcept C44280652 @default.
- W3014560752 hasConcept C537208039 @default.
- W3014560752 hasConceptScore W3014560752C104779481 @default.
- W3014560752 hasConceptScore W3014560752C140205800 @default.
- W3014560752 hasConceptScore W3014560752C149669645 @default.
- W3014560752 hasConceptScore W3014560752C159985019 @default.
- W3014560752 hasConceptScore W3014560752C178790620 @default.
- W3014560752 hasConceptScore W3014560752C185592680 @default.
- W3014560752 hasConceptScore W3014560752C191897082 @default.
- W3014560752 hasConceptScore W3014560752C192562407 @default.
- W3014560752 hasConceptScore W3014560752C20625102 @default.
- W3014560752 hasConceptScore W3014560752C2778560533 @default.
- W3014560752 hasConceptScore W3014560752C2781099003 @default.
- W3014560752 hasConceptScore W3014560752C2781448156 @default.
- W3014560752 hasConceptScore W3014560752C44280652 @default.
- W3014560752 hasConceptScore W3014560752C537208039 @default.
- W3014560752 hasLocation W30145607521 @default.
- W3014560752 hasOpenAccess W3014560752 @default.
- W3014560752 hasPrimaryLocation W30145607521 @default.
- W3014560752 hasRelatedWork W2018137502 @default.
- W3014560752 hasRelatedWork W2060001200 @default.
- W3014560752 hasRelatedWork W2089232389 @default.
- W3014560752 hasRelatedWork W2265002562 @default.
- W3014560752 hasRelatedWork W2340469378 @default.
- W3014560752 hasRelatedWork W2350528383 @default.
- W3014560752 hasRelatedWork W2359132707 @default.
- W3014560752 hasRelatedWork W2372146901 @default.
- W3014560752 hasRelatedWork W3097783663 @default.
- W3014560752 hasRelatedWork W4225390762 @default.
- W3014560752 isParatext "false" @default.
- W3014560752 isRetracted "false" @default.
- W3014560752 magId "3014560752" @default.
- W3014560752 workType "article" @default.