• W3019780145 abstract "A glass fiber shell (GFS) and carbon fiber core (CFC) hybrid rod (HFRP) was produced through pultrusion technology for an alternative to traditional steel sucker rod for petroleum production. The mechanical properties of a really used HFRP rod closed to the ground (25 °C exposed temperature, 0.5 MPa hydraulic pressure and ~70 kN cyclic loading) and in the deep oil-well up to 2600 m (90 °C exposed temperature, 18 MPa hydraulic pressure and ~50 kN cyclic loading) were investigated as a function of service time as long as 553 days. The mechanical, thermal properties and microanalysis tests of HFRP rods were conducted to obtain the long-term evolution of HFRP rods under the above service environments. Exposure closed to the ground caused a maximum degradation rate of short beam shear strength (SBSS) up to 18.92%. Meanwhile, the maximum degradation rates of interface shear strength (ISS) were 28.24% for carbon fiber/resin, 16.88% for glass fiber/resin and 36.07% for CFC/GFS interface. In comparison, exposure in the deep oil-well brought in an extra degradation rate from 4.34% to 11.11% for ISS, and the higher cyclic loading (~70 kN) played an insignificant effect on the degradation. The degradation mechanism of mechanical properties for HFRP rods was attributed to plenty of bound water combined with the resin through the hydrogen bond and brought about the hydrolysis of resin and the increase of pore volume content (~5%), leading to the debonding of fiber/resin. The long-term prediction of interface shear strength shows the degradations of CFC and CFC/GFS were more sensitive to the cyclic load (70 kN) compared to no cyclic load (0 kN), and an extra degradation rate up to 31.3% was observed compared to the no load condition, and the accelerated degradation was weakened with the increase of service temperature and hydraulic pressure. In addition, the exposure at the increased service temperature and hydraulic pressure in the deep oil-well led to an additional degradation rate of ISS in comparison to the ground exposure: 10.70% (CFC), 13.25% (CFC/GFS) and 4.81% (GFS)." @default.
• W3019780145 created "2020-05-01" @default.
• W3019780145 creator A5014640164 @default.
• W3019780145 creator A5018788326 @default.
• W3019780145 creator A5029858919 @default.
• W3019780145 creator A5061063389 @default.
• W3019780145 creator A5064488288 @default.
• W3019780145 creator A5068304283 @default.
• W3019780145 creator A5072576273 @default.
• W3019780145 date "2020-08-01" @default.
• W3019780145 modified "2023-10-10" @default.
• W3019780145 title "Mechanical property evolution and service life prediction of pultruded carbon/glass hybrid rod exposed in harsh oil-well condition" @default.
• W3019780145 cites W1965407828 @default.
• W3019780145 cites W1968627412 @default.
• W3019780145 cites W1968680641 @default.
• W3019780145 cites W1989993298 @default.
• W3019780145 cites W2000338009 @default.
• W3019780145 cites W2006845154 @default.
• W3019780145 cites W2014464892 @default.
• W3019780145 cites W2039457149 @default.
• W3019780145 cites W2042593450 @default.
• W3019780145 cites W2044361017 @default.
• W3019780145 cites W2052278650 @default.
• W3019780145 cites W2053543884 @default.
• W3019780145 cites W2053599618 @default.
• W3019780145 cites W2060425346 @default.
• W3019780145 cites W2082220565 @default.
• W3019780145 cites W2085620498 @default.
• W3019780145 cites W2098365012 @default.
• W3019780145 cites W2298482010 @default.
• W3019780145 cites W2298817825 @default.
• W3019780145 cites W2360467235 @default.
• W3019780145 cites W2409971318 @default.
• W3019780145 cites W2556400716 @default.
• W3019780145 cites W2587760503 @default.
• W3019780145 cites W2773931539 @default.
• W3019780145 cites W2782657082 @default.
• W3019780145 cites W2789559745 @default.
• W3019780145 cites W2795307192 @default.
• W3019780145 cites W2798019035 @default.
• W3019780145 cites W2894811284 @default.
• W3019780145 cites W2899681800 @default.
• W3019780145 cites W2903509724 @default.
• W3019780145 cites W2911607709 @default.
• W3019780145 cites W2919532052 @default.
• W3019780145 cites W2921521459 @default.
• W3019780145 cites W2943772345 @default.
• W3019780145 cites W2968345575 @default.
• W3019780145 cites W2971779587 @default.
• W3019780145 doi "https://doi.org/10.1016/j.compstruct.2020.112418" @default.
• W3019780145 hasPublicationYear "2020" @default.
• W3019780145 type Work @default.
• W3019780145 sameAs 3019780145 @default.
• W3019780145 citedByCount "54" @default.
• W3019780145 countsByYear W30197801452020 @default.
• W3019780145 countsByYear W30197801452021 @default.
• W3019780145 countsByYear W30197801452022 @default.
• W3019780145 countsByYear W30197801452023 @default.
• W3019780145 crossrefType "journal-article" @default.
• W3019780145 hasAuthorship W3019780145A5014640164 @default.
• W3019780145 hasAuthorship W3019780145A5018788326 @default.
• W3019780145 hasAuthorship W3019780145A5029858919 @default.
• W3019780145 hasAuthorship W3019780145A5061063389 @default.
• W3019780145 hasAuthorship W3019780145A5064488288 @default.
• W3019780145 hasAuthorship W3019780145A5068304283 @default.
• W3019780145 hasAuthorship W3019780145A5072576273 @default.
• W3019780145 hasConcept C104779481 @default.
• W3019780145 hasConcept C140205800 @default.
• W3019780145 hasConcept C142724271 @default.
• W3019780145 hasConcept C159985019 @default.
• W3019780145 hasConcept C162184086 @default.
• W3019780145 hasConcept C177229083 @default.
• W3019780145 hasConcept C192562407 @default.
• W3019780145 hasConcept C204787440 @default.
• W3019780145 hasConcept C2779679103 @default.
• W3019780145 hasConcept C41008148 @default.
• W3019780145 hasConcept C519885992 @default.
• W3019780145 hasConcept C52359486 @default.
• W3019780145 hasConcept C71924100 @default.
• W3019780145 hasConcept C76155785 @default.
• W3019780145 hasConcept C76344452 @default.
• W3019780145 hasConceptScore W3019780145C104779481 @default.
• W3019780145 hasConceptScore W3019780145C140205800 @default.
• W3019780145 hasConceptScore W3019780145C142724271 @default.
• W3019780145 hasConceptScore W3019780145C159985019 @default.
• W3019780145 hasConceptScore W3019780145C162184086 @default.
• W3019780145 hasConceptScore W3019780145C177229083 @default.
• W3019780145 hasConceptScore W3019780145C192562407 @default.
• W3019780145 hasConceptScore W3019780145C204787440 @default.
• W3019780145 hasConceptScore W3019780145C2779679103 @default.
• W3019780145 hasConceptScore W3019780145C41008148 @default.
• W3019780145 hasConceptScore W3019780145C519885992 @default.
• W3019780145 hasConceptScore W3019780145C52359486 @default.
• W3019780145 hasConceptScore W3019780145C71924100 @default.
• W3019780145 hasConceptScore W3019780145C76155785 @default.
• W3019780145 hasConceptScore W3019780145C76344452 @default.
• W3019780145 hasFunder F4320313614 @default.
• W3019780145 hasFunder F4320321543 @default.

• next