- W3020643412 abstract "The response of a range of T650-35/Avimid® laminates to various environmental conditioning regimes incorporating thermal spikes has been investigated. Materials based on non-woven and woven reinforcements of different thicknesses were studied; the (minor) differences between the materials seemed to be a consequence of slight differences in resin chemistry as a result of different processing routes, rather than any effect of the reinforcement type. The base-line (standard) conditioning regime used was an isothermal hot-wet condition. One variant on this incorporated a low temperature spike at 220°C, while another incorporated a high temperature spike at 275°C. The final regime, which was intended to be representative of service condition comprised isothermal ageing (hot-wet), a low temperature spike and a period of prolonged drying. The sets of samples exposed to low temperature or high temperature spiking conditions showed enhanced moisture absorption compared to the standard regime. Blistering was seen in some samples after exposure to a significant number of spikes. The effect of varying the spike frequency was investigated and the blistering behaviour was not apparently influenced significantly by the spike frequency. On the other hand, by subjecting wet samples to a single spike at different temperatures, a link between moisture content and spike temperature required to cause blistering was established. The enhanced moisture absorption observed in spiked samples was permanent in that when (undamaged) samples were dried and then reconditioned using the standard regime, the enhanced moisture absorption was still apparent. Enhanced moisture absorption was also shown by the samples subjected to the service cycle, subsequently dried and reconditioned. The moisture distribution across the thickness of samples has been modelled using a commercially available finite difference model. This model enables the moisture uptake during the first few spikes to be simulated reasonably well, but the enhanced moisture saturation level can only be incorporated in an empirical manner. Potential chemical changes in the polymer matrix during conditioning have been investigated using mechanical testing, dynamic mechanical thermal analysis and diamond ATR infra-red spectroscopy of unidirectional material. Not surprisingly there were some changes in the matrix-dominated mechanical properties of wet samples. Interestingly there were changes in the glass transition of samples which had been exposed and then dried out. However, there was no significant chemical change or degradation apparent, even in blistered material." @default.
- W3020643412 created "2020-05-01" @default.
- W3020643412 creator A5006955979 @default.
- W3020643412 date "2003-01-01" @default.
- W3020643412 modified "2023-09-23" @default.
- W3020643412 title "The effects of thermal spiking on a high temperature carbon fibre reinforced polyimide" @default.
- W3020643412 hasPublicationYear "2003" @default.
- W3020643412 type Work @default.
- W3020643412 sameAs 3020643412 @default.
- W3020643412 citedByCount "0" @default.
- W3020643412 crossrefType "dissertation" @default.
- W3020643412 hasAuthorship W3020643412A5006955979 @default.
- W3020643412 hasConcept C121332964 @default.
- W3020643412 hasConcept C125287762 @default.
- W3020643412 hasConcept C127413603 @default.
- W3020643412 hasConcept C133347239 @default.
- W3020643412 hasConcept C159985019 @default.
- W3020643412 hasConcept C162324750 @default.
- W3020643412 hasConcept C176864760 @default.
- W3020643412 hasConcept C187320778 @default.
- W3020643412 hasConcept C187736073 @default.
- W3020643412 hasConcept C192562407 @default.
- W3020643412 hasConcept C24939127 @default.
- W3020643412 hasConcept C2779227376 @default.
- W3020643412 hasConcept C2780965675 @default.
- W3020643412 hasConcept C2781390188 @default.
- W3020643412 hasConcept C97355855 @default.
- W3020643412 hasConceptScore W3020643412C121332964 @default.
- W3020643412 hasConceptScore W3020643412C125287762 @default.
- W3020643412 hasConceptScore W3020643412C127413603 @default.
- W3020643412 hasConceptScore W3020643412C133347239 @default.
- W3020643412 hasConceptScore W3020643412C159985019 @default.
- W3020643412 hasConceptScore W3020643412C162324750 @default.
- W3020643412 hasConceptScore W3020643412C176864760 @default.
- W3020643412 hasConceptScore W3020643412C187320778 @default.
- W3020643412 hasConceptScore W3020643412C187736073 @default.
- W3020643412 hasConceptScore W3020643412C192562407 @default.
- W3020643412 hasConceptScore W3020643412C24939127 @default.
- W3020643412 hasConceptScore W3020643412C2779227376 @default.
- W3020643412 hasConceptScore W3020643412C2780965675 @default.
- W3020643412 hasConceptScore W3020643412C2781390188 @default.
- W3020643412 hasConceptScore W3020643412C97355855 @default.
- W3020643412 hasLocation W30206434121 @default.
- W3020643412 hasOpenAccess W3020643412 @default.
- W3020643412 hasPrimaryLocation W30206434121 @default.
- W3020643412 hasRelatedWork W1562852963 @default.
- W3020643412 hasRelatedWork W1976473191 @default.
- W3020643412 hasRelatedWork W1995656535 @default.
- W3020643412 hasRelatedWork W1998286089 @default.
- W3020643412 hasRelatedWork W2015641726 @default.
- W3020643412 hasRelatedWork W2045087530 @default.
- W3020643412 hasRelatedWork W2077759002 @default.
- W3020643412 hasRelatedWork W2086732809 @default.
- W3020643412 hasRelatedWork W2114580813 @default.
- W3020643412 hasRelatedWork W2158145041 @default.
- W3020643412 hasRelatedWork W2276863218 @default.
- W3020643412 hasRelatedWork W2316294870 @default.
- W3020643412 hasRelatedWork W2329103321 @default.
- W3020643412 hasRelatedWork W2329669559 @default.
- W3020643412 hasRelatedWork W2378798248 @default.
- W3020643412 hasRelatedWork W2385379649 @default.
- W3020643412 hasRelatedWork W2573980751 @default.
- W3020643412 hasRelatedWork W2968597517 @default.
- W3020643412 hasRelatedWork W3186807145 @default.
- W3020643412 hasRelatedWork W3142961957 @default.
- W3020643412 isParatext "false" @default.
- W3020643412 isRetracted "false" @default.
- W3020643412 magId "3020643412" @default.
- W3020643412 workType "dissertation" @default.