• W3021995485 abstract "Composite Ti–Y–N films with various Y contents (0–7.8 at.%) were deposited by reactive magnetron sputtering to investigate the crystal structure, oxidation resistance, mechanical and tribological properties. A combination of X-ray diffraction (XRD), Raman spectroscopy and high resolution transmission electron microscopy (HRTEM) analyses showed that substitutional solid solution of Ti–Y–N is formed by substitution of Ti in TiN lattice by Y and all films exhibit a single-phase face-centered cubic (fcc) structure. The oxidation resistance temperature of Ti–Y–N films increased gradually from 560 °C at 0 at.% Y to 680 °C at 7.8 at.% Y. As Y was incorporated into TiN film, the hardness and elastic modulus of the films increased gradually from 21.7 GPa and 302 GPa at 2.9 at.% Y to 23.8 GPa and 316 GP at 7.8 at.% Y. The improvement of hardness was attributed to solid solution strengthening and fine-grain strengthening. Tribological properties of Ti–Y–N films performed using dry sliding friction and wear tests against Al2O3 depended on Y content to a large extent. The average friction coefficient and wear rate of Ti–Y–N films decreased from about 0.32 and 7.7 × 10− 7 m3/N·m at 2.9 at.% Y to about 0.20 and 6.8 × 10− 7 m3/N·m at 7.8 at.% Y. Optical microscope and Raman spectroscopy measurements revealed that the decreasing amount of tribo-film TiO2 and Y2O3 detected on the surface of the wear tracks could lead to the friction coefficient curve stay constant and decrease the friction coefficients. Moreover, the incorporation of Y into TiN matrix induced the films to undergo a transition from serve wear to mild wear." @default.
• W3021995485 created "2020-05-13" @default.
• W3021995485 creator A5004768135 @default.
• W3021995485 creator A5011792514 @default.
• W3021995485 date "2015-12-01" @default.
• W3021995485 modified "2023-10-12" @default.
• W3021995485 title "Microstructure, oxidation resistance, mechanical and tribological properties of Ti–Y–N films by reactive magnetron sputtering" @default.
• W3021995485 cites W1204641280 @default.
• W3021995485 cites W1256599800 @default.
• W3021995485 cites W1498774038 @default.
• W3021995485 cites W1566024440 @default.
• W3021995485 cites W1967134446 @default.
• W3021995485 cites W1968584854 @default.
• W3021995485 cites W1970227084 @default.
• W3021995485 cites W1978452446 @default.
• W3021995485 cites W1982412278 @default.
• W3021995485 cites W1991042287 @default.
• W3021995485 cites W1997848678 @default.
• W3021995485 cites W1998063114 @default.
• W3021995485 cites W2018285139 @default.
• W3021995485 cites W2041679871 @default.
• W3021995485 cites W2044640365 @default.
• W3021995485 cites W2052943778 @default.
• W3021995485 cites W2053415211 @default.
• W3021995485 cites W2060604096 @default.
• W3021995485 cites W2071393560 @default.
• W3021995485 cites W2072969536 @default.
• W3021995485 cites W2077195222 @default.
• W3021995485 cites W2078746029 @default.
• W3021995485 cites W2088003718 @default.
• W3021995485 cites W2088149984 @default.
• W3021995485 cites W2089433332 @default.
• W3021995485 cites W2095450976 @default.
• W3021995485 cites W2158984913 @default.
• W3021995485 cites W2525282957 @default.
• W3021995485 cites W275132423 @default.
• W3021995485 cites W390972249 @default.
• W3021995485 doi "https://doi.org/10.1016/j.surfcoat.2015.10.068" @default.
• W3021995485 hasPublicationYear "2015" @default.
• W3021995485 type Work @default.
• W3021995485 sameAs 3021995485 @default.
• W3021995485 citedByCount "31" @default.
• W3021995485 countsByYear W30219954852016 @default.
• W3021995485 countsByYear W30219954852017 @default.
• W3021995485 countsByYear W30219954852018 @default.
• W3021995485 countsByYear W30219954852019 @default.
• W3021995485 countsByYear W30219954852020 @default.
• W3021995485 countsByYear W30219954852022 @default.
• W3021995485 countsByYear W30219954852023 @default.
• W3021995485 crossrefType "journal-article" @default.
• W3021995485 hasAuthorship W3021995485A5004768135 @default.
• W3021995485 hasAuthorship W3021995485A5011792514 @default.
• W3021995485 hasConcept C113196181 @default.
• W3021995485 hasConcept C120665830 @default.
• W3021995485 hasConcept C121332964 @default.
• W3021995485 hasConcept C146088050 @default.
• W3021995485 hasConcept C159985019 @default.
• W3021995485 hasConcept C161368742 @default.
• W3021995485 hasConcept C167310744 @default.
• W3021995485 hasConcept C171250308 @default.
• W3021995485 hasConcept C185592680 @default.
• W3021995485 hasConcept C19067145 @default.
• W3021995485 hasConcept C191897082 @default.
• W3021995485 hasConcept C192562407 @default.
• W3021995485 hasConcept C22423302 @default.
• W3021995485 hasConcept C26771246 @default.
• W3021995485 hasConcept C40003534 @default.
• W3021995485 hasConcept C43486711 @default.
• W3021995485 hasConcept C43617362 @default.
• W3021995485 hasConcept C525849907 @default.
• W3021995485 hasConcept C61427134 @default.
• W3021995485 hasConcept C87976508 @default.
• W3021995485 hasConceptScore W3021995485C113196181 @default.
• W3021995485 hasConceptScore W3021995485C120665830 @default.
• W3021995485 hasConceptScore W3021995485C121332964 @default.
• W3021995485 hasConceptScore W3021995485C146088050 @default.
• W3021995485 hasConceptScore W3021995485C159985019 @default.
• W3021995485 hasConceptScore W3021995485C161368742 @default.
• W3021995485 hasConceptScore W3021995485C167310744 @default.
• W3021995485 hasConceptScore W3021995485C171250308 @default.
• W3021995485 hasConceptScore W3021995485C185592680 @default.
• W3021995485 hasConceptScore W3021995485C19067145 @default.
• W3021995485 hasConceptScore W3021995485C191897082 @default.
• W3021995485 hasConceptScore W3021995485C192562407 @default.
• W3021995485 hasConceptScore W3021995485C22423302 @default.
• W3021995485 hasConceptScore W3021995485C26771246 @default.
• W3021995485 hasConceptScore W3021995485C40003534 @default.
• W3021995485 hasConceptScore W3021995485C43486711 @default.
• W3021995485 hasConceptScore W3021995485C43617362 @default.
• W3021995485 hasConceptScore W3021995485C525849907 @default.
• W3021995485 hasConceptScore W3021995485C61427134 @default.
• W3021995485 hasConceptScore W3021995485C87976508 @default.
• W3021995485 hasFunder F4320321001 @default.
• W3021995485 hasLocation W30219954851 @default.
• W3021995485 hasOpenAccess W3021995485 @default.
• W3021995485 hasPrimaryLocation W30219954851 @default.
• W3021995485 hasRelatedWork W1991793670 @default.
• W3021995485 hasRelatedWork W2020349643 @default.

• next