- W3036648754 abstract "High-pressure crystallization and resulting polymorphic composition of long-chain branched polypropylene (LCB-PP) were studied and compared with common linear isotactic polypropylene (PP). Commercially available LCB-PP and PP with similar melt flow indexes were crystallized under several high pressures (20, 40, 80, 120 and 160 MPa) at constant cooling rate 5 °C min−1. Structure of crystallized samples was evaluated via wide-angle X-ray scattering, differential scanning calorimetry and scanning electron microscopy. It was shown that under low pressure LCB-PP crystallizes at higher crystallization temperature than PP due to its higher nucleating density. The opposite situation is observed at high pressures (120 and 160 MPa): crystallization temperature of PP exceeds that of LCB-PP as a negative effect of branching is pronounced. Polymorphic analysis proved that LCB-PP tends to crystallize into orthorhombic γ-form. This crystalline form becomes to be dominant at 40 MPa, and LCB-PP samples crystallized at 120 and 160 MPa contain solely γ-form. On the other hand, no pure γ-form sample was prepared from PP in this study, although positive effect of pressure on its formation is observed. Thermodynamic stability of LCB-PP crystalline structure is systematically lower compared to PP. With pronounced crystallization pressure, the melting peak broadens and finally splits, indicating the presence of dominant amount of γ-form in LCB-PP. In comparison with PP, crystallites in LCB-PP structure are considerably smaller due to lower crystal growth rate and higher nucleating density." @default.
- W3036648754 created "2020-06-25" @default.
- W3036648754 creator A5015937454 @default.
- W3036648754 creator A5040588585 @default.
- W3036648754 creator A5054287166 @default.
- W3036648754 creator A5081898455 @default.
- W3036648754 date "2020-06-19" @default.
- W3036648754 modified "2023-10-01" @default.
- W3036648754 title "Long-chain branched polypropylene: crystallization under high pressure and polymorphic composition" @default.
- W3036648754 cites W1963779110 @default.
- W3036648754 cites W1974565309 @default.
- W3036648754 cites W1983217876 @default.
- W3036648754 cites W1985880703 @default.
- W3036648754 cites W2007122518 @default.
- W3036648754 cites W2007771134 @default.
- W3036648754 cites W2017305590 @default.
- W3036648754 cites W2021717272 @default.
- W3036648754 cites W2023336781 @default.
- W3036648754 cites W2024649245 @default.
- W3036648754 cites W2027696416 @default.
- W3036648754 cites W2028733721 @default.
- W3036648754 cites W2031796751 @default.
- W3036648754 cites W2032475661 @default.
- W3036648754 cites W2050840882 @default.
- W3036648754 cites W2051475198 @default.
- W3036648754 cites W2056147388 @default.
- W3036648754 cites W2062075999 @default.
- W3036648754 cites W2063036309 @default.
- W3036648754 cites W2071461318 @default.
- W3036648754 cites W2077762490 @default.
- W3036648754 cites W2079861346 @default.
- W3036648754 cites W2085414224 @default.
- W3036648754 cites W2120915678 @default.
- W3036648754 cites W2157030675 @default.
- W3036648754 cites W2171294566 @default.
- W3036648754 cites W2331820380 @default.
- W3036648754 cites W2548493560 @default.
- W3036648754 cites W2606187296 @default.
- W3036648754 cites W2609823701 @default.
- W3036648754 cites W2804499709 @default.
- W3036648754 cites W2883857675 @default.
- W3036648754 cites W2900223217 @default.
- W3036648754 cites W2902384012 @default.
- W3036648754 cites W4248142851 @default.
- W3036648754 doi "https://doi.org/10.1007/s10973-020-09931-1" @default.
- W3036648754 hasPublicationYear "2020" @default.
- W3036648754 type Work @default.
- W3036648754 sameAs 3036648754 @default.
- W3036648754 citedByCount "0" @default.
- W3036648754 crossrefType "journal-article" @default.
- W3036648754 hasAuthorship W3036648754A5015937454 @default.
- W3036648754 hasAuthorship W3036648754A5040588585 @default.
- W3036648754 hasAuthorship W3036648754A5054287166 @default.
- W3036648754 hasAuthorship W3036648754A5081898455 @default.
- W3036648754 hasBestOaLocation W30366487542 @default.
- W3036648754 hasConcept C113196181 @default.
- W3036648754 hasConcept C115624301 @default.
- W3036648754 hasConcept C120665830 @default.
- W3036648754 hasConcept C121332964 @default.
- W3036648754 hasConcept C131888329 @default.
- W3036648754 hasConcept C137637335 @default.
- W3036648754 hasConcept C159985019 @default.
- W3036648754 hasConcept C178790620 @default.
- W3036648754 hasConcept C185592680 @default.
- W3036648754 hasConcept C191486275 @default.
- W3036648754 hasConcept C192562407 @default.
- W3036648754 hasConcept C203036418 @default.
- W3036648754 hasConcept C2777973245 @default.
- W3036648754 hasConcept C37243968 @default.
- W3036648754 hasConcept C39519442 @default.
- W3036648754 hasConcept C43617362 @default.
- W3036648754 hasConcept C44228677 @default.
- W3036648754 hasConcept C521977710 @default.
- W3036648754 hasConcept C58018886 @default.
- W3036648754 hasConcept C61048295 @default.
- W3036648754 hasConcept C8010536 @default.
- W3036648754 hasConcept C97355855 @default.
- W3036648754 hasConceptScore W3036648754C113196181 @default.
- W3036648754 hasConceptScore W3036648754C115624301 @default.
- W3036648754 hasConceptScore W3036648754C120665830 @default.
- W3036648754 hasConceptScore W3036648754C121332964 @default.
- W3036648754 hasConceptScore W3036648754C131888329 @default.
- W3036648754 hasConceptScore W3036648754C137637335 @default.
- W3036648754 hasConceptScore W3036648754C159985019 @default.
- W3036648754 hasConceptScore W3036648754C178790620 @default.
- W3036648754 hasConceptScore W3036648754C185592680 @default.
- W3036648754 hasConceptScore W3036648754C191486275 @default.
- W3036648754 hasConceptScore W3036648754C192562407 @default.
- W3036648754 hasConceptScore W3036648754C203036418 @default.
- W3036648754 hasConceptScore W3036648754C2777973245 @default.
- W3036648754 hasConceptScore W3036648754C37243968 @default.
- W3036648754 hasConceptScore W3036648754C39519442 @default.
- W3036648754 hasConceptScore W3036648754C43617362 @default.
- W3036648754 hasConceptScore W3036648754C44228677 @default.
- W3036648754 hasConceptScore W3036648754C521977710 @default.
- W3036648754 hasConceptScore W3036648754C58018886 @default.
- W3036648754 hasConceptScore W3036648754C61048295 @default.
- W3036648754 hasConceptScore W3036648754C8010536 @default.
- W3036648754 hasConceptScore W3036648754C97355855 @default.
- W3036648754 hasLocation W30366487541 @default.