- W3037610029 abstract "For high strength aluminium alloys, such as AA6008T61 and AA6111 PFHT, when they are joined as the bottom material by self-piercing riveting (SPR), they tend to crack at the joint buttons. These cracks, especially those penetrated to the rivets, may cause galvanic corrosion problem with the steel rivet. In this paper, the mechanical strength of four stack/die combinations with different joint button cracking severity was studied before and after salt-spray corrosion test. The results showed that corrosion on the severely cracked joints was worse than that on the joints with small cracks and the corrosion on the stack with the same top and bottom material was less than that on the stack with different top and bottom materials. For all joints the static lap shear strength after corrosion was improved, but the static T peel strength after corrosion was slightly reduced or did not have obvious change. The results also showed that after corrosion the lap shear fatigue strength of the specimens with severe cracks did not have obvious change, but the lap shear fatigue strength of the specimens with small cracks slightly reduced." @default.
- W3037610029 created "2020-07-02" @default.
- W3037610029 creator A5023930365 @default.
- W3037610029 creator A5028800902 @default.
- W3037610029 creator A5034366434 @default.
- W3037610029 creator A5080113768 @default.
- W3037610029 date "2018-01-01" @default.
- W3037610029 modified "2023-09-23" @default.
- W3037610029 title "Influence of corrosion of self-piercing riveted high strengthaluminium alloy joints with button cracks on the mechanical strength" @default.
- W3037610029 doi "https://doi.org/10.15377/2410-4701.2018.05.4" @default.
- W3037610029 hasPublicationYear "2018" @default.
- W3037610029 type Work @default.
- W3037610029 sameAs 3037610029 @default.
- W3037610029 citedByCount "0" @default.
- W3037610029 crossrefType "journal-article" @default.
- W3037610029 hasAuthorship W3037610029A5023930365 @default.
- W3037610029 hasAuthorship W3037610029A5028800902 @default.
- W3037610029 hasAuthorship W3037610029A5034366434 @default.
- W3037610029 hasAuthorship W3037610029A5080113768 @default.
- W3037610029 hasConcept C127413603 @default.
- W3037610029 hasConcept C127893833 @default.
- W3037610029 hasConcept C131850400 @default.
- W3037610029 hasConcept C159390177 @default.
- W3037610029 hasConcept C159750122 @default.
- W3037610029 hasConcept C159985019 @default.
- W3037610029 hasConcept C185324459 @default.
- W3037610029 hasConcept C18555067 @default.
- W3037610029 hasConcept C191897082 @default.
- W3037610029 hasConcept C192562407 @default.
- W3037610029 hasConcept C20625102 @default.
- W3037610029 hasConcept C2780026712 @default.
- W3037610029 hasConcept C2781371449 @default.
- W3037610029 hasConcept C29633239 @default.
- W3037610029 hasConcept C39432304 @default.
- W3037610029 hasConcept C513153333 @default.
- W3037610029 hasConcept C57769158 @default.
- W3037610029 hasConcept C58396970 @default.
- W3037610029 hasConcept C66938386 @default.
- W3037610029 hasConcept C96035792 @default.
- W3037610029 hasConceptScore W3037610029C127413603 @default.
- W3037610029 hasConceptScore W3037610029C127893833 @default.
- W3037610029 hasConceptScore W3037610029C131850400 @default.
- W3037610029 hasConceptScore W3037610029C159390177 @default.
- W3037610029 hasConceptScore W3037610029C159750122 @default.
- W3037610029 hasConceptScore W3037610029C159985019 @default.
- W3037610029 hasConceptScore W3037610029C185324459 @default.
- W3037610029 hasConceptScore W3037610029C18555067 @default.
- W3037610029 hasConceptScore W3037610029C191897082 @default.
- W3037610029 hasConceptScore W3037610029C192562407 @default.
- W3037610029 hasConceptScore W3037610029C20625102 @default.
- W3037610029 hasConceptScore W3037610029C2780026712 @default.
- W3037610029 hasConceptScore W3037610029C2781371449 @default.
- W3037610029 hasConceptScore W3037610029C29633239 @default.
- W3037610029 hasConceptScore W3037610029C39432304 @default.
- W3037610029 hasConceptScore W3037610029C513153333 @default.
- W3037610029 hasConceptScore W3037610029C57769158 @default.
- W3037610029 hasConceptScore W3037610029C58396970 @default.
- W3037610029 hasConceptScore W3037610029C66938386 @default.
- W3037610029 hasConceptScore W3037610029C96035792 @default.
- W3037610029 hasLocation W30376100291 @default.
- W3037610029 hasOpenAccess W3037610029 @default.
- W3037610029 hasPrimaryLocation W30376100291 @default.
- W3037610029 hasRelatedWork W1158085660 @default.
- W3037610029 hasRelatedWork W1982177547 @default.
- W3037610029 hasRelatedWork W2020085399 @default.
- W3037610029 hasRelatedWork W2028846235 @default.
- W3037610029 hasRelatedWork W2064835925 @default.
- W3037610029 hasRelatedWork W2145554699 @default.
- W3037610029 hasRelatedWork W2176529211 @default.
- W3037610029 hasRelatedWork W2314274811 @default.
- W3037610029 hasRelatedWork W2315884465 @default.
- W3037610029 hasRelatedWork W2319537516 @default.
- W3037610029 hasRelatedWork W2323004390 @default.
- W3037610029 hasRelatedWork W2323976037 @default.
- W3037610029 hasRelatedWork W2327925350 @default.
- W3037610029 hasRelatedWork W2412045422 @default.
- W3037610029 hasRelatedWork W2590574113 @default.
- W3037610029 hasRelatedWork W2901325470 @default.
- W3037610029 hasRelatedWork W3017214924 @default.
- W3037610029 hasRelatedWork W3176848618 @default.
- W3037610029 hasRelatedWork W3205342953 @default.
- W3037610029 hasRelatedWork W81394413 @default.
- W3037610029 isParatext "false" @default.
- W3037610029 isRetracted "false" @default.
- W3037610029 magId "3037610029" @default.
- W3037610029 workType "article" @default.