- W3037797306 abstract "In recent years, significant efforts have been devoted to the research and development of spin-coated Al2O3 thin films, due to their large band gaps, high breakdown voltage and stability at high annealing temperature. However, as the alumina precursor has a large surface energy, substrates need to be treated by plasma before spin coating. Therefore, to avoid the expensive and process-complicated plasma treatment, we incorporated zirconium nitrate into the aluminum nitrate solution to decrease the surface energy of the precursor which improve the spreadability. Then, the electrical performances and the surface morphologies of the films were measured. For comparison, the pure Al2O3 films with plasma treatments were also prepared. As a result, after low temperature annealing (200 °C), the relative dielectric constant of Zr–AlOx spin-coated thin-film MIM (Metal-Insulator-Metal) devices can reach 12 and the leakage current density is not higher than 7.78 × 10−8 A/cm2 @ 1 MV/cm when the concentration of zirconium nitrate is 0.05 mol/L. The Aluminum oxide film prepared by zirconium doping has higher stability and better electrical properties than the pure films with plasma treatments and high performance can be attained under low-temperature annealing, which shows its potential application in printing and flexible electronic devices." @default.
- W3037797306 created "2020-07-02" @default.
- W3037797306 creator A5000245536 @default.
- W3037797306 creator A5004928994 @default.
- W3037797306 creator A5025827852 @default.
- W3037797306 creator A5025943547 @default.
- W3037797306 creator A5036326490 @default.
- W3037797306 creator A5066090520 @default.
- W3037797306 creator A5069887457 @default.
- W3037797306 creator A5070010908 @default.
- W3037797306 creator A5079053274 @default.
- W3037797306 creator A5085472611 @default.
- W3037797306 date "2020-06-29" @default.
- W3037797306 modified "2023-09-25" @default.
- W3037797306 title "Effect of Zirconium Doping on Electrical Properties of Aluminum Oxide Dielectric Layer by Spin Coating Method with Low Temperature Preparation" @default.
- W3037797306 cites W1512740549 @default.
- W3037797306 cites W1572253984 @default.
- W3037797306 cites W1969141180 @default.
- W3037797306 cites W1977608084 @default.
- W3037797306 cites W1982876375 @default.
- W3037797306 cites W1992721896 @default.
- W3037797306 cites W1994042190 @default.
- W3037797306 cites W2001380373 @default.
- W3037797306 cites W2006850332 @default.
- W3037797306 cites W2010432008 @default.
- W3037797306 cites W2021141322 @default.
- W3037797306 cites W2025064062 @default.
- W3037797306 cites W2031065678 @default.
- W3037797306 cites W2039859873 @default.
- W3037797306 cites W2059602277 @default.
- W3037797306 cites W2064748814 @default.
- W3037797306 cites W2065038191 @default.
- W3037797306 cites W2082075720 @default.
- W3037797306 cites W2082353118 @default.
- W3037797306 cites W2083392454 @default.
- W3037797306 cites W2084165843 @default.
- W3037797306 cites W2087569796 @default.
- W3037797306 cites W2088273074 @default.
- W3037797306 cites W2120022242 @default.
- W3037797306 cites W2162957680 @default.
- W3037797306 cites W2175007413 @default.
- W3037797306 cites W2303719102 @default.
- W3037797306 cites W2312445932 @default.
- W3037797306 cites W2325135517 @default.
- W3037797306 cites W2333678145 @default.
- W3037797306 cites W2337465360 @default.
- W3037797306 cites W2339881707 @default.
- W3037797306 cites W2378333990 @default.
- W3037797306 cites W2413471669 @default.
- W3037797306 cites W2614075610 @default.
- W3037797306 cites W2746550681 @default.
- W3037797306 cites W2772572309 @default.
- W3037797306 cites W2775073379 @default.
- W3037797306 cites W2788946185 @default.
- W3037797306 cites W2790154976 @default.
- W3037797306 cites W2793018310 @default.
- W3037797306 cites W2884925804 @default.
- W3037797306 cites W2892290337 @default.
- W3037797306 cites W2914003230 @default.
- W3037797306 cites W2926955578 @default.
- W3037797306 cites W2936377868 @default.
- W3037797306 cites W2981577465 @default.
- W3037797306 cites W2996294329 @default.
- W3037797306 cites W3010518616 @default.
- W3037797306 cites W3010642926 @default.
- W3037797306 cites W1965792219 @default.
- W3037797306 doi "https://doi.org/10.3390/coatings10070620" @default.
- W3037797306 hasPublicationYear "2020" @default.
- W3037797306 type Work @default.
- W3037797306 sameAs 3037797306 @default.
- W3037797306 citedByCount "4" @default.
- W3037797306 countsByYear W30377973062020 @default.
- W3037797306 countsByYear W30377973062022 @default.
- W3037797306 crossrefType "journal-article" @default.
- W3037797306 hasAuthorship W3037797306A5000245536 @default.
- W3037797306 hasAuthorship W3037797306A5004928994 @default.
- W3037797306 hasAuthorship W3037797306A5025827852 @default.
- W3037797306 hasAuthorship W3037797306A5025943547 @default.
- W3037797306 hasAuthorship W3037797306A5036326490 @default.
- W3037797306 hasAuthorship W3037797306A5066090520 @default.
- W3037797306 hasAuthorship W3037797306A5069887457 @default.
- W3037797306 hasAuthorship W3037797306A5070010908 @default.
- W3037797306 hasAuthorship W3037797306A5079053274 @default.
- W3037797306 hasAuthorship W3037797306A5085472611 @default.
- W3037797306 hasBestOaLocation W30377973061 @default.
- W3037797306 hasConcept C113196181 @default.
- W3037797306 hasConcept C115196108 @default.
- W3037797306 hasConcept C127413603 @default.
- W3037797306 hasConcept C133386390 @default.
- W3037797306 hasConcept C159985019 @default.
- W3037797306 hasConcept C171250308 @default.
- W3037797306 hasConcept C185592680 @default.
- W3037797306 hasConcept C19067145 @default.
- W3037797306 hasConcept C191897082 @default.
- W3037797306 hasConcept C192562407 @default.
- W3037797306 hasConcept C2777855556 @default.
- W3037797306 hasConcept C2779851234 @default.
- W3037797306 hasConcept C2781448156 @default.