- W3044013809 abstract "Abstract High Zn content Al-7.9Zn-2.7Mg-2.0Cu (wt. %) aluminum alloy strip with 5.5 mm thickness was successfully fabricated by twin roll casting (TRC). Fine grain size, second phase and second dendrite arm spacing (SDAS) were obtained in the cast strip due to the high cooling rate during TRC process. Short-time annealing treatment of 480 oC-1 h could effectively reduce the second phases, and the elongation of the strip was improved. The TRC alloy sheet with 2.0 mm thickness was fabricated by the annealing treatment (480 oC-1 h) and hot rolling. The yield strength, tensile strength and elongation along the rolling direction of the TRC sheet after solution treatment, pre-aging and natural aging were 398 MPa, 590 MPa and 15.74%, respectively. After bake-hardening, the yield strength, tensile strength and elongation along the rolling direction were 550 MPa, 605 MPa and 10.07%, respectively." @default.
- W3044013809 created "2020-07-29" @default.
- W3044013809 creator A5010443325 @default.
- W3044013809 creator A5011097136 @default.
- W3044013809 creator A5025420693 @default.
- W3044013809 creator A5025435781 @default.
- W3044013809 creator A5075839171 @default.
- W3044013809 creator A5083042997 @default.
- W3044013809 date "2020-12-01" @default.
- W3044013809 modified "2023-10-01" @default.
- W3044013809 title "Microstructure and mechanical properties of Al-7.9Zn-2.7Mg-2.0Cu (wt%) alloy strip fabricated by twin roll casting and hot rolling" @default.
- W3044013809 cites W1022794651 @default.
- W3044013809 cites W1976003154 @default.
- W3044013809 cites W1982483028 @default.
- W3044013809 cites W1990256953 @default.
- W3044013809 cites W2003710304 @default.
- W3044013809 cites W2008795219 @default.
- W3044013809 cites W2009970510 @default.
- W3044013809 cites W2011436057 @default.
- W3044013809 cites W2014580163 @default.
- W3044013809 cites W2017579516 @default.
- W3044013809 cites W2025813777 @default.
- W3044013809 cites W2026066555 @default.
- W3044013809 cites W2032064539 @default.
- W3044013809 cites W2037647696 @default.
- W3044013809 cites W2042855080 @default.
- W3044013809 cites W2049034085 @default.
- W3044013809 cites W2054448122 @default.
- W3044013809 cites W2059091088 @default.
- W3044013809 cites W2062463055 @default.
- W3044013809 cites W2063839491 @default.
- W3044013809 cites W2070360712 @default.
- W3044013809 cites W2070595269 @default.
- W3044013809 cites W2074668740 @default.
- W3044013809 cites W2090316916 @default.
- W3044013809 cites W2093050750 @default.
- W3044013809 cites W2093873538 @default.
- W3044013809 cites W2106802544 @default.
- W3044013809 cites W2110733247 @default.
- W3044013809 cites W2144094673 @default.
- W3044013809 cites W2172880157 @default.
- W3044013809 cites W2195769143 @default.
- W3044013809 cites W2282730498 @default.
- W3044013809 cites W2468914818 @default.
- W3044013809 cites W2508749988 @default.
- W3044013809 cites W2565144793 @default.
- W3044013809 cites W2571532210 @default.
- W3044013809 cites W2596573639 @default.
- W3044013809 cites W2737630260 @default.
- W3044013809 cites W2767600636 @default.
- W3044013809 cites W2781710095 @default.
- W3044013809 cites W2789948121 @default.
- W3044013809 cites W2800709142 @default.
- W3044013809 cites W2948006690 @default.
- W3044013809 cites W2951366446 @default.
- W3044013809 cites W3006540222 @default.
- W3044013809 cites W607442476 @default.
- W3044013809 doi "https://doi.org/10.1016/j.jallcom.2020.156481" @default.
- W3044013809 hasPublicationYear "2020" @default.
- W3044013809 type Work @default.
- W3044013809 sameAs 3044013809 @default.
- W3044013809 citedByCount "15" @default.
- W3044013809 countsByYear W30440138092021 @default.
- W3044013809 countsByYear W30440138092022 @default.
- W3044013809 countsByYear W30440138092023 @default.
- W3044013809 crossrefType "journal-article" @default.
- W3044013809 hasAuthorship W3044013809A5010443325 @default.
- W3044013809 hasAuthorship W3044013809A5011097136 @default.
- W3044013809 hasAuthorship W3044013809A5025420693 @default.
- W3044013809 hasAuthorship W3044013809A5025435781 @default.
- W3044013809 hasAuthorship W3044013809A5075839171 @default.
- W3044013809 hasAuthorship W3044013809A5083042997 @default.
- W3044013809 hasConcept C159985019 @default.
- W3044013809 hasConcept C16635281 @default.
- W3044013809 hasConcept C191897082 @default.
- W3044013809 hasConcept C192562407 @default.
- W3044013809 hasConcept C2780026712 @default.
- W3044013809 hasConcept C87976508 @default.
- W3044013809 hasConceptScore W3044013809C159985019 @default.
- W3044013809 hasConceptScore W3044013809C16635281 @default.
- W3044013809 hasConceptScore W3044013809C191897082 @default.
- W3044013809 hasConceptScore W3044013809C192562407 @default.
- W3044013809 hasConceptScore W3044013809C2780026712 @default.
- W3044013809 hasConceptScore W3044013809C87976508 @default.
- W3044013809 hasFunder F4320334885 @default.
- W3044013809 hasLocation W30440138091 @default.
- W3044013809 hasOpenAccess W3044013809 @default.
- W3044013809 hasPrimaryLocation W30440138091 @default.
- W3044013809 hasRelatedWork W2010733322 @default.
- W3044013809 hasRelatedWork W2046292958 @default.
- W3044013809 hasRelatedWork W2089251307 @default.
- W3044013809 hasRelatedWork W2123155170 @default.
- W3044013809 hasRelatedWork W2351679394 @default.
- W3044013809 hasRelatedWork W2359655419 @default.
- W3044013809 hasRelatedWork W2377876279 @default.
- W3044013809 hasRelatedWork W2379855728 @default.
- W3044013809 hasRelatedWork W4292623501 @default.
- W3044013809 hasRelatedWork W4303926928 @default.