- W3046245035 abstract "Abstract The hydrogen behavior in electrochemically charged electron beam melting (EBM) and wrought Ti–6Al–4V alloys with a similar β-phase content of ~6 wt% was compared. Hydrogenation resulted in the formation of microvoids, either adjacent to the surface or along interphases, their coalescence, and emanation of microcracks around them. The microstructure of the EBM alloy displayed a discontinuous arrangement of β-phase particles in the short-transverse direction, a smaller lattice constant of the β-phase, and more α/β interphase boundaries, making the EBM alloy more susceptible to hydrogen embrittlement. The hydrogenated alloys were composed of αH (hcp) and βH (bcc) solid solutions as well as δa (fcc) and δb (fcc) hydrides with lattice parameters that have not been reported before. These hydrides were transformed from the primary α-phase. No major microstrain difference was observed between the EBM and wrought alloys, either before or after hydrogenation. Microstrains in the α and β phases increased following hydrogenation; they were larger in the βH and δa phases compared to the αH and δb phases. A post-treatment that would increase the size of the β particles is suggested to improve the resistance of EBM Ti–6Al–4V to hydrogen-induced damage." @default.
- W3046245035 created "2020-08-07" @default.
- W3046245035 creator A5002764732 @default.
- W3046245035 creator A5006154934 @default.
- W3046245035 creator A5012497894 @default.
- W3046245035 creator A5014156494 @default.
- W3046245035 creator A5026033228 @default.
- W3046245035 creator A5040742886 @default.
- W3046245035 creator A5041145489 @default.
- W3046245035 creator A5041884797 @default.
- W3046245035 creator A5043953386 @default.
- W3046245035 creator A5073453674 @default.
- W3046245035 creator A5084050529 @default.
- W3046245035 date "2020-09-01" @default.
- W3046245035 modified "2023-09-30" @default.
- W3046245035 title "Hydrogen effects on electrochemically charged additive manufactured by electron beam melting (EBM) and wrought Ti–6Al–4V alloys" @default.
- W3046245035 cites W1855490885 @default.
- W3046245035 cites W1956988534 @default.
- W3046245035 cites W1967109990 @default.
- W3046245035 cites W1968272638 @default.
- W3046245035 cites W1971901608 @default.
- W3046245035 cites W1972384764 @default.
- W3046245035 cites W1973387178 @default.
- W3046245035 cites W1977292408 @default.
- W3046245035 cites W1980423774 @default.
- W3046245035 cites W1988871411 @default.
- W3046245035 cites W1993458539 @default.
- W3046245035 cites W1995662513 @default.
- W3046245035 cites W1998016055 @default.
- W3046245035 cites W2002210549 @default.
- W3046245035 cites W2004285892 @default.
- W3046245035 cites W2007134507 @default.
- W3046245035 cites W2007784031 @default.
- W3046245035 cites W2019718382 @default.
- W3046245035 cites W2023381719 @default.
- W3046245035 cites W2028032736 @default.
- W3046245035 cites W2031467495 @default.
- W3046245035 cites W2040697905 @default.
- W3046245035 cites W2042310099 @default.
- W3046245035 cites W2042947602 @default.
- W3046245035 cites W2050582925 @default.
- W3046245035 cites W2050869396 @default.
- W3046245035 cites W2055148452 @default.
- W3046245035 cites W2065867116 @default.
- W3046245035 cites W2068309205 @default.
- W3046245035 cites W2072812566 @default.
- W3046245035 cites W2074402847 @default.
- W3046245035 cites W2079276987 @default.
- W3046245035 cites W2079719887 @default.
- W3046245035 cites W2080348296 @default.
- W3046245035 cites W2080892086 @default.
- W3046245035 cites W2081469533 @default.
- W3046245035 cites W2082888867 @default.
- W3046245035 cites W2086058904 @default.
- W3046245035 cites W2088101001 @default.
- W3046245035 cites W2089193199 @default.
- W3046245035 cites W2090832912 @default.
- W3046245035 cites W2091397211 @default.
- W3046245035 cites W2092655420 @default.
- W3046245035 cites W2093321371 @default.
- W3046245035 cites W2095432611 @default.
- W3046245035 cites W2130947934 @default.
- W3046245035 cites W2156364813 @default.
- W3046245035 cites W2157480703 @default.
- W3046245035 cites W2161181293 @default.
- W3046245035 cites W2204647836 @default.
- W3046245035 cites W2406944394 @default.
- W3046245035 cites W2415989392 @default.
- W3046245035 cites W2503161491 @default.
- W3046245035 cites W2584257649 @default.
- W3046245035 cites W2602810215 @default.
- W3046245035 cites W2616801167 @default.
- W3046245035 cites W2621283698 @default.
- W3046245035 cites W2728023690 @default.
- W3046245035 cites W2766916166 @default.
- W3046245035 cites W2767214661 @default.
- W3046245035 cites W2789847045 @default.
- W3046245035 cites W2794199564 @default.
- W3046245035 cites W2800610975 @default.
- W3046245035 cites W2802992442 @default.
- W3046245035 cites W2884618583 @default.
- W3046245035 cites W2912094871 @default.
- W3046245035 cites W2912689729 @default.
- W3046245035 cites W2913840193 @default.
- W3046245035 cites W2937618590 @default.
- W3046245035 cites W2938015769 @default.
- W3046245035 cites W2942512393 @default.
- W3046245035 cites W2944536200 @default.
- W3046245035 cites W2965624382 @default.
- W3046245035 cites W2973298041 @default.
- W3046245035 cites W3015111427 @default.
- W3046245035 cites W3022592244 @default.
- W3046245035 cites W590665704 @default.
- W3046245035 doi "https://doi.org/10.1016/j.ijhydene.2020.06.277" @default.
- W3046245035 hasPublicationYear "2020" @default.
- W3046245035 type Work @default.
- W3046245035 sameAs 3046245035 @default.
- W3046245035 citedByCount "30" @default.