- W3048157064 abstract "The densification behavior and mechanical properties of spark plasma sintered titanium-molybdenum alloys were investigated in this paper. All Ti-(4, 8, 12, 16, and 20 wt%) Mo samples were sintered at 1200 °C for 5 min under 50 MPa. A significant relative density of 99.9% was secured for the Ti-based alloy with 16 wt.% Mo. The overall trend of hardness was similar to that of the relative density as Ti-16 wt.% Mo alloy showed the highest hardness values of 372 HV30 and 592 HV0.3 in macro (30 kg) and micro scales (300 g), respectively. Maximum ultimate tensile strength values (852 MPa at room temperature and 600 MPa at 600 ℃) belonged to the Ti-8 wt.% Mo sample. Such an observation was related to the formation of β-Ti phase and the strain-induced transformation phenomenon. The highest flexural strength of ∼2 GPa belonged to the Ti-12 wt.% Mo alloy, which may be a result of solid solution formation between Ti and Mo. Finally, average values of nano hardness, elastic modulus, and stiffness of various phases available in the samples with 12 and 20 wt% Mo were calculated through nano-indentation technique and the former specimen presented higher values in all the mentioned qualities." @default.
- W3048157064 created "2020-08-13" @default.
- W3048157064 creator A5007962924 @default.
- W3048157064 creator A5015545828 @default.
- W3048157064 creator A5016885524 @default.
- W3048157064 creator A5024102253 @default.
- W3048157064 creator A5025390015 @default.
- W3048157064 creator A5028900482 @default.
- W3048157064 creator A5053517075 @default.
- W3048157064 creator A5059961022 @default.
- W3048157064 creator A5073986724 @default.
- W3048157064 date "2020-09-01" @default.
- W3048157064 modified "2023-10-14" @default.
- W3048157064 title "Nanoindentational and conventional mechanical properties of spark plasma sintered Ti–Mo alloys" @default.
- W3048157064 cites W1970253002 @default.
- W3048157064 cites W1975618779 @default.
- W3048157064 cites W1975630211 @default.
- W3048157064 cites W1978616686 @default.
- W3048157064 cites W1981808447 @default.
- W3048157064 cites W1983132644 @default.
- W3048157064 cites W1990393678 @default.
- W3048157064 cites W2025671379 @default.
- W3048157064 cites W2033345420 @default.
- W3048157064 cites W2035161040 @default.
- W3048157064 cites W2035492728 @default.
- W3048157064 cites W2047211260 @default.
- W3048157064 cites W2051166244 @default.
- W3048157064 cites W2051317670 @default.
- W3048157064 cites W2064430730 @default.
- W3048157064 cites W2067621481 @default.
- W3048157064 cites W2073213963 @default.
- W3048157064 cites W2077027165 @default.
- W3048157064 cites W2077891939 @default.
- W3048157064 cites W2083555207 @default.
- W3048157064 cites W2124781074 @default.
- W3048157064 cites W2129679877 @default.
- W3048157064 cites W2138162649 @default.
- W3048157064 cites W2240316177 @default.
- W3048157064 cites W2398182315 @default.
- W3048157064 cites W2554288293 @default.
- W3048157064 cites W2587095627 @default.
- W3048157064 cites W2607099584 @default.
- W3048157064 cites W2746816997 @default.
- W3048157064 cites W2764242812 @default.
- W3048157064 cites W2898088199 @default.
- W3048157064 cites W2902070406 @default.
- W3048157064 cites W2915289757 @default.
- W3048157064 cites W2938490024 @default.
- W3048157064 cites W2944255782 @default.
- W3048157064 cites W2954211914 @default.
- W3048157064 cites W2969244129 @default.
- W3048157064 cites W2972001051 @default.
- W3048157064 cites W2990504824 @default.
- W3048157064 cites W2994751369 @default.
- W3048157064 cites W3010795974 @default.
- W3048157064 cites W3021652779 @default.
- W3048157064 cites W3026647859 @default.
- W3048157064 cites W3038211935 @default.
- W3048157064 cites W3038229375 @default.
- W3048157064 cites W3041200957 @default.
- W3048157064 cites W620536879 @default.
- W3048157064 doi "https://doi.org/10.1016/j.jmrt.2020.07.066" @default.
- W3048157064 hasPublicationYear "2020" @default.
- W3048157064 type Work @default.
- W3048157064 sameAs 3048157064 @default.
- W3048157064 citedByCount "30" @default.
- W3048157064 countsByYear W30481570642020 @default.
- W3048157064 countsByYear W30481570642021 @default.
- W3048157064 countsByYear W30481570642022 @default.
- W3048157064 countsByYear W30481570642023 @default.
- W3048157064 crossrefType "journal-article" @default.
- W3048157064 hasAuthorship W3048157064A5007962924 @default.
- W3048157064 hasAuthorship W3048157064A5015545828 @default.
- W3048157064 hasAuthorship W3048157064A5016885524 @default.
- W3048157064 hasAuthorship W3048157064A5024102253 @default.
- W3048157064 hasAuthorship W3048157064A5025390015 @default.
- W3048157064 hasAuthorship W3048157064A5028900482 @default.
- W3048157064 hasAuthorship W3048157064A5053517075 @default.
- W3048157064 hasAuthorship W3048157064A5059961022 @default.
- W3048157064 hasAuthorship W3048157064A5073986724 @default.
- W3048157064 hasBestOaLocation W30481570641 @default.
- W3048157064 hasConcept C112950240 @default.
- W3048157064 hasConcept C159985019 @default.
- W3048157064 hasConcept C178405089 @default.
- W3048157064 hasConcept C191897082 @default.
- W3048157064 hasConcept C192562407 @default.
- W3048157064 hasConcept C2776014600 @default.
- W3048157064 hasConcept C2780026712 @default.
- W3048157064 hasConcept C506065880 @default.
- W3048157064 hasConcept C549387045 @default.
- W3048157064 hasConcept C82455628 @default.
- W3048157064 hasConcept C87976508 @default.
- W3048157064 hasConcept C8953137 @default.
- W3048157064 hasConceptScore W3048157064C112950240 @default.
- W3048157064 hasConceptScore W3048157064C159985019 @default.
- W3048157064 hasConceptScore W3048157064C178405089 @default.
- W3048157064 hasConceptScore W3048157064C191897082 @default.
- W3048157064 hasConceptScore W3048157064C192562407 @default.