• W3048405162 endingPage "645" @default.
• W3048405162 startingPage "635" @default.
• W3048405162 abstract "Abstract Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (Cf/C) composite for spark plasma sintering, two kinds of commercially pure α-Al2O3 powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (Tsg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al2O3 powder and 1400 °C for the 3 μm Al2O3 powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al2O3 compact can reach ∼80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth." @default.
• W3048405162 created "2020-08-18" @default.
• W3048405162 creator A5009953160 @default.
• W3048405162 creator A5011070722 @default.
• W3048405162 creator A5019325306 @default.
• W3048405162 creator A5029800638 @default.
• W3048405162 creator A5043824238 @default.
• W3048405162 creator A5056383338 @default.
• W3048405162 date "2021-01-01" @default.
• W3048405162 modified "2023-10-17" @default.
• W3048405162 title "Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering" @default.
• W3048405162 cites W1534918490 @default.
• W3048405162 cites W1585533436 @default.
• W3048405162 cites W1935395674 @default.
• W3048405162 cites W1972955039 @default.
• W3048405162 cites W1982352321 @default.
• W3048405162 cites W1998135674 @default.
• W3048405162 cites W2004396810 @default.
• W3048405162 cites W2010231320 @default.
• W3048405162 cites W2017653664 @default.
• W3048405162 cites W2017774268 @default.
• W3048405162 cites W2019851086 @default.
• W3048405162 cites W2022479570 @default.
• W3048405162 cites W2023061298 @default.
• W3048405162 cites W2025283853 @default.
• W3048405162 cites W2026173372 @default.
• W3048405162 cites W2029844066 @default.
• W3048405162 cites W2030006079 @default.
• W3048405162 cites W2043418691 @default.
• W3048405162 cites W2044273652 @default.
• W3048405162 cites W2052373444 @default.
• W3048405162 cites W2054964845 @default.
• W3048405162 cites W2057217243 @default.
• W3048405162 cites W2058572326 @default.
• W3048405162 cites W2062090463 @default.
• W3048405162 cites W2065795904 @default.
• W3048405162 cites W2067086824 @default.
• W3048405162 cites W2086696175 @default.
• W3048405162 cites W2099063760 @default.
• W3048405162 cites W2108451820 @default.
• W3048405162 cites W2144304300 @default.
• W3048405162 cites W2167773267 @default.
• W3048405162 cites W2412628612 @default.
• W3048405162 cites W2543124941 @default.
• W3048405162 cites W2587055415 @default.
• W3048405162 cites W2804404721 @default.
• W3048405162 cites W2914103316 @default.
• W3048405162 cites W4211191043 @default.
• W3048405162 doi "https://doi.org/10.1016/j.jeurceramsoc.2020.08.018" @default.
• W3048405162 hasPublicationYear "2021" @default.
• W3048405162 type Work @default.
• W3048405162 sameAs 3048405162 @default.
• W3048405162 citedByCount "28" @default.
• W3048405162 countsByYear W30484051622021 @default.
• W3048405162 countsByYear W30484051622022 @default.
• W3048405162 countsByYear W30484051622023 @default.
• W3048405162 crossrefType "journal-article" @default.
• W3048405162 hasAuthorship W3048405162A5009953160 @default.
• W3048405162 hasAuthorship W3048405162A5011070722 @default.
• W3048405162 hasAuthorship W3048405162A5019325306 @default.
• W3048405162 hasAuthorship W3048405162A5029800638 @default.
• W3048405162 hasAuthorship W3048405162A5043824238 @default.
• W3048405162 hasAuthorship W3048405162A5056383338 @default.
• W3048405162 hasConcept C127413603 @default.
• W3048405162 hasConcept C159985019 @default.
• W3048405162 hasConcept C191897082 @default.
• W3048405162 hasConcept C192562407 @default.
• W3048405162 hasConcept C2777581544 @default.
• W3048405162 hasConcept C2780357685 @default.
• W3048405162 hasConcept C2984729377 @default.
• W3048405162 hasConcept C42360764 @default.
• W3048405162 hasConcept C61696701 @default.
• W3048405162 hasConcept C87976508 @default.
• W3048405162 hasConceptScore W3048405162C127413603 @default.
• W3048405162 hasConceptScore W3048405162C159985019 @default.
• W3048405162 hasConceptScore W3048405162C191897082 @default.
• W3048405162 hasConceptScore W3048405162C192562407 @default.
• W3048405162 hasConceptScore W3048405162C2777581544 @default.
• W3048405162 hasConceptScore W3048405162C2780357685 @default.
• W3048405162 hasConceptScore W3048405162C2984729377 @default.
• W3048405162 hasConceptScore W3048405162C42360764 @default.
• W3048405162 hasConceptScore W3048405162C61696701 @default.
• W3048405162 hasConceptScore W3048405162C87976508 @default.
• W3048405162 hasFunder F4320321001 @default.
• W3048405162 hasFunder F4320324638 @default.
• W3048405162 hasFunder F4320335777 @default.
• W3048405162 hasIssue "1" @default.
• W3048405162 hasLocation W30484051621 @default.
• W3048405162 hasOpenAccess W3048405162 @default.
• W3048405162 hasPrimaryLocation W30484051621 @default.
• W3048405162 hasRelatedWork W1968916218 @default.
• W3048405162 hasRelatedWork W2033451903 @default.
• W3048405162 hasRelatedWork W2055093469 @default.
• W3048405162 hasRelatedWork W2219169289 @default.
• W3048405162 hasRelatedWork W2324637725 @default.
• W3048405162 hasRelatedWork W2331992200 @default.
• W3048405162 hasRelatedWork W2370800422 @default.
• W3048405162 hasRelatedWork W2377457182 @default.

• next